Toughening agent composition and application thereof, HIPS resin, ABS resin and preparation method thereof

A technology of a toughening agent and a composition is applied in the field of a method and the ABS resin prepared by the method, and can solve the problems of single particle size, difficulty in taking into account both impact resistance and gloss, and low impact resistance of the resin. Achieve high impact strength, broad industrial application prospects, and high surface gloss.

Active Publication Date: 2021-10-12
CHINA PETROLEUM & CHEM CORP +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to overcome the single particle size of the toughening agent in the prior art. When used for resin toughening, the resin has low impact resistance and impact resistance. Defects where performance and gloss are difficult to balance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Toughening agent composition and application thereof, HIPS resin, ABS resin and preparation method thereof
  • Toughening agent composition and application thereof, HIPS resin, ABS resin and preparation method thereof
  • Toughening agent composition and application thereof, HIPS resin, ABS resin and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example

[0088] This preparation example is used to illustrate the preparation of the low-cis polybutadiene rubber and styrene-butadiene rubber of the present invention.

[0089] (1) Preparation of low cis polybutadiene rubber

[0090] Use anionic batch polymerization process to carry out butadiene solution polymerization, then use silicon tetrachloride for coupling, use carbon dioxide aqueous solution (the molar ratio of carbon dioxide and n-butyllithium is 1:1) to terminate, and then add low-cis polybutylene The 1520 and 1076 composite antioxidants (1520:1076=1:1, weight ratio) of diene rubber weight 0.3% by weight are prepared respectively to obtain low-cis polybutadiene rubber LCBR 1 -LCBR 6 , respectively measured the structure and performance of the obtained low-cis polybutadiene rubber, and the specific results are shown in Table 1.

[0091] (2) Preparation of styrene-butadiene rubber

[0092] Using an anionic batch polymerization process, carry out solution polymerization of...

Embodiment 1

[0094] This embodiment is used to illustrate the preparation of toughening agent composition of the present invention

[0095] Low cis polybutadiene rubber LCBR 1 Solution and styrene butadiene rubber BS 1 The solution is mixed according to the dry rubber weight ratio of low-cis polybutadiene rubber and styrene-butadiene rubber at 1:1 to obtain a toughening agent composition solution R 1 , the R 1 Carry out steam condensation and desolvation treatment to obtain the toughening agent composition CR 1 , and determine the toughener composition CR 1 The structure and performance of the specific results are shown in Table 3.

Embodiment 2-5

[0097] This embodiment is used to illustrate the preparation of toughening agent composition of the present invention

[0098] Adopt the method similar to embodiment 1 to prepare toughening agent composition, difference is, the kind of low-cis polybutadiene rubber or styrene-butadiene rubber that adopts is different from embodiment 1, and all the other are all the same as embodiment 1, A toughening agent composition is prepared, specifically:

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
impact strengthaaaaaaaaaa
molecular weight distributionaaaaaaaaaa
molecular weight distributionaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of rubber toughening agents, and discloses a toughening agent composition and application thereof, HIPS resin, ABS resin and a preparation method thereof, the composition contains low cis-polybutadiene rubber and butadiene styrene rubber, and the content weight ratio of the low cis-polybutadiene rubber to the butadiene styrene rubber is (0.25-4): 1; the viscosity of the toughening agent composition in a 5 wt% rubber-styrene solution at 25 DEG C is 27-37 cp; the Mooney viscosity ML1 + 4 of the toughening agent composition at 100 DEG C is 40 to 50; the content of a butadiene structural unit in the toughening agent composition is 92-98wt%, and the content of styrene structural unit in the toughening agent composition is 2-8 wt%. When the toughening agent composition provided by the invention is used for an aromatic vinyl resin toughening agent, the aromatic vinyl resin with excellent surface gloss can be obtained while the impact strength is ensured, and the toughening agent composition has a wide industrial application prospect.

Description

technical field [0001] The invention relates to the technical field of rubber toughening agents, in particular to a toughening agent composition, the application of the toughening agent composition in the preparation of aromatic vinyl resins, a method for preparing HIPS resin and the method The prepared HIPS resin, a method for preparing ABS resin and the ABS resin prepared by the method. Background technique [0002] The selection of rubber species is a key technology in the toughening of continuous bulk aromatic vinyl resins. Low cis polybutadiene rubber has the advantages of uniform quality, moderate vinyl content, low gel content, low chroma, random distribution of molecular chain cis-trans 1,4 structure, and no transition metals. It is a continuous body Best toughening rubber for aromatic vinyl resins. [0003] According to the performance requirements of the resin, the microstructure, molecular weight and its distribution, Mooney viscosity and 5% by weight rubber-sty...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/06C08L9/00C08F279/02C08F279/04C08F212/08C08F220/44
CPCC08L9/06C08L9/00C08F279/02C08F279/04C08F212/08C08F220/44Y02T10/86
Inventor 李建成赫炜朱晓光刘天鹤王爱东王雪徐林
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com