Heat-not-burn solid smoke cartridge

A heat-not-burn, solid smoke technology, applied to tobacco and other directions, can solve the problems of insufficient smoke quality and quantity, large waste pollution, and high cost, and achieve the effects of improving the degree of blending, low consumption and high efficiency in the production process, and simple preparation process.

Pending Publication Date: 2021-10-08
CHINA TOBACCO HENAN IND
View PDF14 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a heat-not-burn solid pod to solve the problems of complex processing technology, high cost, large waste pollution, poor heating uniformity, and insufficient smoke quality and quantity of the pod prepared by tobacco sheet. question

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Heat-not-burn solid smoke cartridge
  • Heat-not-burn solid smoke cartridge

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0025] The preparation method of the heat-not-burn solid cartridge of the present application comprises the following steps:

[0026] 1) Preparation of heat-not-burn solid pod main material:

[0027] The tobacco particles of two meshes after pre-drying are uniformly mixed according to the mass ratio of tobacco particles with a large particle size to tobacco particles with a small particle size of 2:8-8:2 to obtain the first material;

[0028] 2) Preparation of heat-not-burn solid pod accessories:

[0029] Preparation of fuming agent: Mixture A prepared by preparing fuming agent and water at a mass ratio of 3:7-7:3;

[0030] Preparation of the binder: a mixed gum B made of low-acyl gellan gum and high-acyl gellan gum at a mass ratio of 0:10-10:0;

[0031] Mixing according to the mass ratio of A:B is 99:1-90:10, fully stirring and then standing still to obtain the second material;

[0032] 3) Preparation of heat-not-burn solid pod materials:

[0033] Mixing the first materia...

Embodiment 1

[0038] A method for preparing a heat-not-burn solid cartridge, as follows:

[0039] 1) Preparation of heat-not-burn solid pod main material:

[0040] The 20-mesh tobacco particles and the 60-mesh tobacco particles are uniformly mixed in a mass ratio of 6:4 to obtain the first material.

[0041] 2) Preparation of heat-not-burn solid pod accessories:

[0042] Glycerin and water are used to make a fuming agent according to the ratio of mass ratio of 7:3, and high acyl gellan gum and low acyl gellan gum are used to make pectin adhesive according to the ratio of mass ratio of 6:4, and the fuming agent Mix with the binder at a mass ratio of 94:6, stir well and let stand for 5 minutes to obtain the second material.

[0043] 3) Preparation of heat-not-burn solid pod materials:

[0044] Mix the first material and the second material uniformly at a mass ratio of 6:4 to obtain the third material.

[0045] 4) Preparation of heat-not-burn solid pods:

[0046] Put the third material in...

Embodiment 2

[0048] A method for preparing a heat-not-burn solid cartridge, as follows:

[0049] 1) Preparation of heat-not-burn solid pod main material:

[0050] 20-mesh tobacco powder and 20-mesh microwave expanded stalk powder were uniformly mixed at a mass ratio of 6:4 to obtain a mixture, and then tobacco straw biochar with a mass ratio of 5% of the mixture was added to obtain the first material.

[0051] 2) Preparation of heat-not-burn solid pod accessories:

[0052] Glycerin and water are used to make a fuming agent according to the ratio of mass ratio of 6:4, and high acyl gellan gum and low acyl gellan gum are used to make pectin adhesive according to the ratio of mass ratio of 6:4, and the fuming agent Mix with the binder at a mass ratio of 94:6, stir well and let stand for 5 minutes to obtain the second material.

[0053] 3) Preparation of heat-not-burn solid pod material:

[0054] Mix the first material and the second material uniformly at a mass ratio of 6:4 to obtain the t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a heat-not-burn solid smoke cartridge, which comprises a smoke cartridge body, the smoke cartridge body is provided with an axially-through insertion hole of a smoking set heating rod, and the hole diameter of the insertion hole is smaller than the outer diameter of the smoking set heating rod; the cigarette cartridge body is composed of a cigarette cartridge main material and a cigarette cartridge auxiliary material, wherein the cigarette cartridge main material is composed of tobacco particles with two mesh numbers; the smoke cartridge auxiliary material is prepared by blending a smoke agent and a binder; and the binder is prepared from low-acyl gellan gum and high-acyl gellan gum. According to the technical scheme, two kinds of tobacco particles with different particle sizes and corresponding mesh numbers are selected, so that the air permeability of the cigarette cartridge is determined, the smoking resistance value during smoking is influenced, and meanwhile, the physical characteristics such as elasticity, hardness, toughness and density of the cigarette cartridge are influenced. Compared with common sheet type smoke cartridges, the solid smoke cartridge is prepared through extrusion forming equipment, the preparation technology is simple, the production process is low in consumption and efficient, and the requirements of enterprises for cost reduction and efficiency improvement are met.

Description

technical field [0001] The invention belongs to the technical field of new tobacco, and in particular relates to a heat-not-burn solid cigarette bomb. Background technique [0002] In recent years, as the growth rate of traditional cigarette sales has slowed down, new tobacco products have gradually become the future development trend and have received extensive attention and research at home and abroad. Among them, heat-not-burn tobacco has become a research hotspot in the industry because of its use method and flavor characteristics closest to cigarette products. Compared with traditional cigarettes, heat-not-burn tobacco products have the advantages of low heating temperature, less tar, and less harmful to health. At the same time, they have fashionable appearance and excellent consumption experience. They perform well in foreign markets and are especially welcomed by young consumer groups. . [0003] Existing heat-not-burn products have great similarities in tobacco sh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A24F40/20A24F40/42A24F40/70
CPCA24F40/20A24F40/42A24F40/70
Inventor 段鹍文秋成李金学崔廷王浩宇赵阔张婷婷刘欢李龙飞杨琦
Owner CHINA TOBACCO HENAN IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More