Solid cartridge suitable for heat-not-burn smoking set and preparation method

A heat-not-burn and solid-smoke technology, which is applied in the fields of application, tobacco, and tobacco treatment, can solve the problems of high waste pollution, insufficient smoke quality and quantity, and high cost, and achieve low-consumption and high-efficiency production processes, simple preparation processes, and multiple The effect of suction

Active Publication Date: 2021-08-10
CHINA TOBACCO HENAN IND
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a solid pod suitable for heat-not-burn smoking appliances and its preparation method, so as to solve the problem of complex processing technology, high cost, high waste pollution, poor heating uniformity, and smoke pods prepared from tobacco sheets. Insufficient temperament and quantity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Solid cartridge suitable for heat-not-burn smoking set and preparation method
  • Solid cartridge suitable for heat-not-burn smoking set and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] 1) Prepare the main material of the heat not burn solid cartridge:

[0035] The 20-mesh tobacco particles and the 60-mesh tobacco particles are uniformly mixed in a ratio of 6:4 by mass to obtain the first material.

[0036] 2) Preparation of heat-not-burn solid cartridge accessories:

[0037] Use glycerin and water to make a fuming agent in a ratio of 8:2 by mass, and use high acyl gellan gum and low acyl gellan gum to make a pectin adhesive in a ratio of 6:4 by mass, and mix the fuming agent Mix it with the binder according to the mass ratio of 94:6, fully stir it and let it stand for 5 minutes to obtain the second material.

[0038] 3) Preparation of heat-not-burn solid pod material:

[0039] The first material and the second material are mixed evenly in a ratio of 6:4 by mass to obtain the third material.

[0040] 4) Preparation of heat-not-burn solid cartridges:

[0041] The third material is placed in a vacuum drying box and preheated at 40°C for 2 minutes, th...

Embodiment 2

[0043] 1) Prepare the main material of the heat not burn solid cartridge:

[0044] The 20-mesh tobacco powder and the 20-mesh microwave-expanded stem powder are uniformly mixed in a ratio of 6:4 by mass to obtain the first material.

[0045] 2) Preparation of heat-not-burn solid cartridge accessories:

[0046] Use glycerin and water to make a fuming agent in a ratio of 8:2 by mass, and use high acyl gellan gum and low acyl gellan gum to make a pectin adhesive in a ratio of 6:4 by mass, and mix the fuming agent Mix it with the binder according to the mass ratio of 94:6, fully stir it and let it stand for 5 minutes to obtain the second material.

[0047] 3) Preparation of heat-not-burn solid pod material:

[0048] The first material and the second material are mixed evenly in a ratio of 6:4 by mass to obtain the third material.

[0049] 4) Preparation of heat-not-burn solid cartridges:

[0050] The third material is placed in a vacuum drying box and preheated at 40°C for 2 m...

Embodiment 3

[0052] 1) Prepare the main material of the heat not burn solid cartridge:

[0053] Mix the 20-mesh tobacco powder and the 60-mesh tobacco powder in a ratio of 6:4 by mass, and use high-acyl gellan gum and low-acyl gellan gum in a mass ratio of 6:4 to make pectin adhesive. The first material is obtained by mixing the tobacco leaf raw material and the binder dry powder in a mass ratio of 94:6.

[0054] 2) Preparation of heat-not-burn solid cartridge accessories:

[0055] Using glycerin and water according to the mass ratio of 8:2 to prepare a smoke agent, fully stirring and then allowing to stand for 5 minutes to obtain the second material.

[0056] 3) Preparation of heat-not-burn solid pod material:

[0057] The first material and the second material are mixed evenly in a ratio of 6:4 by mass to obtain the third material.

[0058] 4) Preparation of heat-not-burn solid cartridges:

[0059] The third material is placed in a vacuum drying box and preheated at 40°C for 2 minutes,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention relates to a solid cartridge suitable for a heat-not-burn smoking set and a preparation method. The solid cartridge is composed of a cartridge main material and a cartridge auxiliary material. The cartridge main material and the cartridge auxiliary material are fully mixed, so that the tobacco particles in the cartridge main material absorb sufficient smoke agent, the finally prepared solid cartridge product has higher smoke amount, and a smoker can obtain more smoking times during smoking. According to the technical scheme, mixed glue prepared from low-acyl gellan gum and high-acyl gellan gum according to a certain proportion is selected as a binder, and two kinds of tobacco particles with different particle sizes and corresponding mesh numbers are selected, so that the air permeability of the smoke cartridge is determined, the suction resistance value during smoking is influenced, and meanwhile, the physical characteristics such as elasticity, hardness, toughness and density of the smoke cartridge are influenced. Compared with common sheet type cartridges, the solid cartridge is prepared through extrusion forming equipment, the preparation technology is simple, the production process is low in consumption and efficient, and the requirements of enterprises for cost reduction and efficiency improvement are met.

Description

technical field [0001] The invention belongs to the technical field of novel tobacco, and in particular relates to a solid smoke bomb suitable for heat-not-burn smoking articles and a preparation method thereof. Background technique [0002] In recent years, as the sales growth of traditional cigarettes has slowed down, new tobacco products have gradually become the future development trend, and have received extensive attention and research at home and abroad. Among them, heat-not-burn tobacco has become a research hotspot in the industry because its usage and flavor characteristics are the closest to cigarette products. Compared with traditional cigarettes, heat-not-burn tobacco products have the advantages of low heating temperature, less tar content, and less harm to health. At the same time, they have fashionable appearance and excellent consumption experience. They have performed well in foreign markets and are especially popular among young consumers. . [0003] Exi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A24B15/18A24F40/70A24F40/20A24F40/42
CPCA24B15/167A24F40/70A24F40/20A24F40/42
Inventor 文秋成杨琦李金学段鹍王鹏飞王浩宇张婷婷赵阔李龙飞刘欢
Owner CHINA TOBACCO HENAN IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com