Preparation process of high-strength porous ceramic atomizing core

A porous ceramic and preparation technology, which is applied in the field of ceramic cores, can solve problems such as insufficient grinding, waste of resources, and uneven particle size, and achieve the effects of avoiding insufficient grinding, avoiding waste of resources, and reducing manufacturing costs

Inactive Publication Date: 2021-08-13
邝青
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Porous ceramic material is a new type of material that utilizes the physical surface. It is fired at high temperature and has a large number of three-dimensional interconnected channels inside. It is a ceramic body with a three-dimensional network skeleton mechanism. The existing porous ceramics Ceramic raw materials need to be ground before firing at high temperature, and the existing grinding device may not be sufficiently ground during use
[0003] When the existing grinding device grinds the ceramic raw material, due to the improper setting of the mechanical data by the staff, the grinding of the ceramic raw material will be insufficient, resulting in the phenomenon of uneven particle size after the ceramic raw material is ground, resulting in The hardness of the porous ceramic atomizing core does not meet the standard, resulting in a decrease in the qualified rate of the product, resulting in a waste of resources and increasing the manufacturing cost of the porous ceramic atomizing core

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation process of high-strength porous ceramic atomizing core
  • Preparation process of high-strength porous ceramic atomizing core
  • Preparation process of high-strength porous ceramic atomizing core

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] see Figure 1-4 A high-strength porous ceramic atomization core preparation process is completed using a grinding device prepared from a high-strength porous ceramic atomization core. The grinding device prepared from a high-strength porous ceramic atomization core includes a housing 1, a connecting mechanism 2, Filtering mechanism 3, rotating mechanism 4, triggering mechanism 5, sliding mechanism 6 and braking mechanism 7, the inner wall of casing 1 is movably connected with connecting mechanism 2, and connecting mechanism 2 comprises groove 21, fixed block 22 and spring one 23, and shell The inner wall of the body 1 is provided with a groove 21, the inner wall of the groove 21 is fixedly connected with a fixed block 22, the inner wall of the groove 21 is fixedly connected with a spring 23, the connecting mechanism 2 is used to connect the filter mechanism 3, and the inner side of the connecting mechanism 2 is fixed. Connected with a filter mechanism 3, the filter mech...

Embodiment 2

[0036] see Figure 1-4 , a process for preparing a high-strength porous ceramic atomizing core, comprising the following steps:

[0037] S1. Adjust the data of the grinding device and calibrate the machine several times to ensure the normal operation of the grinding device and the fineness of the grinding raw materials;

[0038] S2. Open the cover of the grinding device, evenly put the raw materials for preparing the ceramic atomizing core into the grinding device, and then close the grinding device;

[0039] S3, then connect the external power supply, adjust the data of the grinding device, and ensure the normal operation of the grinding device under manual inspection;

[0040] S4. Open the discharge port of the grinding device, place the collection container on the bottom of the discharge port, and fix the collection container;

[0041] S5. Start the grinding device, and then the ground raw materials will pass through the filtering action of the filtering mechanism 3 along...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of ceramic cores, and discloses a preparation process of a high-strength porous ceramic atomizing core, which is completed by using a grinding device for preparing the high-strength porous ceramic atomizing core. The grinding device for preparing the high-strength porous ceramic atomizing core comprises a shell, a connecting mechanism, a filtering mechanism, a rotating mechanism, a triggering mechanism, a sliding mechanism and a braking mechanism, the inner wall of the shell is movably connected with the connecting mechanism, and the inner side of the connecting mechanism is fixedly connected with the filtering mechanism. According to the preparation process of the high-strength porous ceramic atomization core, through separation of an electric contact and a conductor rail and stopping of a braking mechanism on a rotating mechanism, the phenomena that ceramic raw materials are not sufficiently ground, the particle size is not uniform after the ceramic raw materials are ground are avoided, and the situation that the hardness of the fired porous ceramic atomization core cannot reach the standard is avoided; and the qualified rate of products is increased, waste of resources is avoided, and the manufacturing cost of the porous ceramic atomizing core is reduced.

Description

technical field [0001] The invention relates to the technical field of ceramic cores, in particular to a preparation process of a high-strength porous ceramic atomizing core. Background technique [0002] Porous ceramic material is a new type of material that utilizes the physical surface. It is fired at high temperature and has a large number of three-dimensional interconnected channels inside. It is a ceramic body with a three-dimensional network skeleton mechanism. The existing porous ceramics Before the material is fired at high temperature, the ceramic raw material needs to be ground. During the use of the existing grinding device, there will be insufficient grinding. [0003] When the existing grinding device grinds the ceramic raw material, due to the improper setting of the mechanical data by the staff, the grinding of the ceramic raw material will be insufficient, resulting in the phenomenon of uneven particle size after the ceramic raw material is ground, resulting...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/626A24F40/70
CPCA24F40/70C04B35/6261
Inventor 邝青
Owner 邝青
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com