A Method of Quickly Obtaining Standard Forming Parameters of Selective Laser Melting Equipment

A technology of selective laser melting and parameters, which is applied in the direction of additive manufacturing and additive processing, can solve the problems of low efficiency, time-consuming and laborious, etc., and achieve the effect of comprehensive analysis accuracy, narrowing the test range, and increasing the printing speed

Active Publication Date: 2021-09-28
恒新增材制造研究中心(佛山)有限公司
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The process is time-consuming and laborious, and the efficiency is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A Method of Quickly Obtaining Standard Forming Parameters of Selective Laser Melting Equipment
  • A Method of Quickly Obtaining Standard Forming Parameters of Selective Laser Melting Equipment
  • A Method of Quickly Obtaining Standard Forming Parameters of Selective Laser Melting Equipment

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0049] In order to make the object, technical solution and advantages of the present invention clearer, the present invention will be further described in detail below in conjunction with the accompanying drawings. It is only stated here that the words for directions such as up, down, left, right, front, back, inside, and outside that appear or will appear in the text of the present invention are only based on the accompanying drawings of the present invention, and are not specific to the present invention. limited.

[0050] see figure 1 , figure 1 It is a step-by-step flowchart of a method for quickly obtaining standard forming parameters of selective laser melting equipment according to the present invention. The method for rapidly obtaining standard forming parameters of selective laser melting equipment provided by the present invention includes the following steps:

[0051]S1. Design the printing model of the test workpiece, wherein the test workpiece includes an inclin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for quickly obtaining standard forming parameters of a selective laser melting device, comprising: S1, designing a printing model of a test workpiece, wherein the test workpiece includes an inclined surface structure, a curved surface structure, a side through hole structure and a cantilever beam structure; S2. Print out n on the substrate according to the printing model 1 A test workpiece with the same shape, each test workpiece corresponds to a set of basic forming parameters; S3, detect each test workpiece, and obtain the corresponding inclined surface structural parameters, curved surface structural parameters, side through hole structural parameters and cantilever beam structure parameters; S4, according to the inclined surface structure parameters, curved surface structure parameters, side through hole structure parameters and cantilever beam structure parameters in step S3, obtain the standard forming parameters of the metal powder to be processed, the standard forming parameters include filling Forming parameters, upper surface standard forming parameters and lower surface standard forming parameters. The method of the invention has fast acquisition speed and strong directivity.

Description

technical field [0001] The invention relates to the technical field of selective laser melting, in particular to a method for quickly obtaining standard forming parameters of selective laser melting equipment. Background technique [0002] Selective Laser Melting (SLM) technology is a kind of additive manufacturing technology. It is based on the principle of discrete slicing and superposition forming. It uses metal powder as raw material and laser as energy source. It scans according to the layered model. One layer, the substrate is lowered to a certain height, repeated continuously, and the parts are formed. [0003] Process parameter matching refers to the process parameter sets that can be applied to different sequences within a certain range for certain materials to be formed on related equipment. Due to the interaction and mutual restriction among multiple process parameters, it is a multi-variable coupling system, and it is difficult to directly select a combination o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B22F10/80B22F10/28B33Y50/00
CPCB33Y50/00
Inventor 李伟强陈超
Owner 恒新增材制造研究中心(佛山)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap