Combined transmutation glaze, combined transmutation glaze porcelain and preparation method of combined transmutation glaze porcelain

A technology of kiln changing glaze and glaze, applied in the field of ceramics, can solve the problems of lack of color and diverse textures, and achieve the effects of diverse surface textures, enhanced plasticity, and increased viscosity

Active Publication Date: 2021-08-06
武汉遇知音文化发展有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In view of the problems existing in the above-mentioned prior art, the purpose of the present invention is to provide a combined kiln-changing glaze, combined kiln-changing glaze porcelain and a preparation method thereof, to solve the existing In the process of one-time or two-time glazing in the technology, ceramic products with richer colors, various textures, and uneven surface can not be obtained, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Combined transmutation glaze, combined transmutation glaze porcelain and preparation method of combined transmutation glaze porcelain
  • Combined transmutation glaze, combined transmutation glaze porcelain and preparation method of combined transmutation glaze porcelain

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A combined kiln-changing glaze, comprising a base glaze, a first intermediate glaze, a second intermediate glaze and a top glaze, in parts by weight:

[0041] The bottom glaze glaze material comprises the following components: 65 parts of nepheline orthoclase, 5 parts of dolomite, 4 parts of limestone, 10 parts of china clay, and 5 parts of bentonite;

[0042] The first intermediate glaze comprises the following components: 65 parts of nepheline orthoclase, 5 parts of dolomite, 4 parts of limestone, 10 parts of zinc oxide, 5 parts of bentonite, 10 parts of quartz, and 10 parts of colorant;

[0043] The second intermediate glaze comprises the following components: 60 parts of nepheline orthoclase, 10 parts of dolomite, 2 parts of zinc oxide, 5 parts of bentonite, 10 parts of rutile, and 10 parts of ilmenite;

[0044] The surface glaze includes the following components: 70 parts of nepheline orthoclase, 10 parts of dolomite, 3 parts of zinc oxide, 5 parts of bentonite and 5...

Embodiment 2

[0056] A combined kiln-changing glaze, comprising a base glaze, a first intermediate glaze, a second intermediate glaze and a top glaze, in parts by weight:

[0057] The bottom glaze glaze material comprises the following components: 70 parts of nepheline orthoclase, 4 parts of dolomite, 3 parts of limestone, 8 parts of china clay, and 4 parts of bentonite;

[0058] The first intermediate glaze comprises the following components: 70 parts of nepheline orthoclase, 4 parts of dolomite, 3 parts of limestone, 8 parts of zinc oxide, 4 parts of bentonite, 8 parts of quartz, and 8 parts of colorant;

[0059] The second intermediate glaze comprises the following components: 65 parts of nepheline orthoclase, 8 parts of dolomite, 1.5 parts of zinc oxide, 4 parts of bentonite, 8 parts of rutile, and 8 parts of ilmenite;

[0060] The surface glaze includes the following components: 75 parts of nepheline orthoclase, 8 parts of dolomite, 2.5 parts of zinc oxide, 4 parts of bentonite and 4 p...

Embodiment 3

[0072] A combined kiln-changing glaze, comprising a base glaze, a first intermediate glaze, a second intermediate glaze and a top glaze, in parts by weight:

[0073] The underglaze glaze comprises the following components: 75 parts of nepheline orthoclase, 3 parts of dolomite, 2 parts of limestone, 5 parts of china clay, and 3 parts of bentonite;

[0074] The first intermediate glaze comprises the following components: 75 parts of nepheline orthoclase, 3 parts of dolomite, 2 parts of limestone, 5 parts of zinc oxide, 3 parts of bentonite, 5 parts of quartz, and 5 parts of colorant;

[0075] The second intermediate glaze comprises the following components: 70 parts of nepheline orthoclase, 5 parts of dolomite, 1 part of zinc oxide, 3 parts of bentonite, 5 parts of rutile, and 5 parts of ilmenite;

[0076] The surface glaze includes the following components: 80 parts of nepheline orthoclase, 5 parts of dolomite, 2 parts of zinc oxide, 3 parts of bentonite and 3 parts of quartz. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a combined transmutation glaze, combined transmutation glaze porcelain and a preparation method of the combined transmutation glaze porcelain. The combined transmutation glaze comprises a ground glaze material, a first intermediate glaze material, a second intermediate glaze material and a cover glaze material. The ground glaze material has a covering effect, nepheline, syenite, dolomite and limestone cooperate with one another to achieve a dissolution assisting effect, the porcelain clay can improve the viscosity, and the bentonite can enhance the plasticity of the glaze material; the first intermediate glaze contains zinc oxide, so that the firing temperature can be reduced, and a colorant provides different colors for the glaze; the components in the second intermediate glaze have a synergistic effect, so that the whole glaze has high viscosity at a high temperature, and a concave-convex feeling is generated on the surface of a green body; and the overglaze material is sprayed on the outermost layer of the green body. Therefore, the surface texture of the green body is diversified, the effect that the glaze surface is uneven is formed, and meanwhile, the artificial decoration pattern is supplemented, so that the surface texture of the whole porcelain is diversified and uneven, people think, and the porcelain has extremely high artistic value.

Description

technical field [0001] The invention belongs to the technical field of ceramics, and in particular relates to a combined kiln-changing glaze, combined kiln-changing glaze porcelain and a preparation method thereof. Background technique [0002] Kiln-changing glaze means that when the utensils are fired in the kiln, due to the oxidation or reduction of various color-forming elements, the utensils will show unexpected glaze color effects after leaving the kiln. Because it appeared by accident, its shape is special, and people don't know its principle, but only know that it is obtained due to the change of the roasting process in the kiln, so it is called "kiln change". At first, the appearance of kiln changes in the kiln was regarded as unknown, but after a long time, it was found that its shape was extremely beautiful, or like brilliant clouds, or like spring flowers and autumn clouds, or like a raging sea, or like a galloping horse, so it was regarded as a masterpiece of art...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/04C04B33/13C04B41/89C03C8/00
CPCC04B33/04C04B33/13C04B41/009C04B41/52C04B41/89C03C8/00C04B2235/3472C04B2235/3481C04B2235/3418C04B2235/602C04B2235/606C04B2235/612C04B2235/656C04B2235/6567C04B2235/658C04B41/5022C04B41/4543C04B41/0072Y02P40/60
Inventor 温华徐在源施占杰
Owner 武汉遇知音文化发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com