Gel capable of stabilizing fragrant substances
A fragrance substance and gel technology, applied in the field of supramolecular gel, can solve the problems of incongruity, inconsistent release behavior, volatilization loss of fragrance components, etc., and achieve the effects of prolonging release time, lasting physiological sensation, and reducing release loss.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0077] A method of preparing a gel that stabilizes the flavor substance, including the following steps:
[0078] Step 1, the preparation of the gelling agent: Press the racemic malic acid and nicotine to 2: 1 molar ratio, soluble in ethanol, respectively, racemic malic acid and dissolved ethanol mass ratio of 1 g: 28ml, nicotine and dissolution The ethanol mass ratio is 1 g: 210 mL, stirred at room temperature to completely dissolve, each obtained racemic malic acid solution and nicotine solution, and then thoroughly mixed the above two solutions to obtain a mixed liquid to warming the mixture To reflux, the reaction was 30 min, 190 mbar, and evaporated, then the evaporated product was dried at 36 ° C for 1.5 h, resulting in a racemic maline glycodehydrogen gelling agent;
[0079] Step 2, the preparation of the gel:
[0080] The fragrant substance was dissolved in 1,2-propanediol to obtain a flavor solvent, and the volume ratio of fragrance and 1,2-propylene glycol mass was 1 g: 2...
Embodiment 2
[0084] This example provides the application of a carrier super molecular gel prepared in the first embodiment of the present invention in a heating cigarette
[0085] The Ni Dated Salt Syrotic Molecular Gel can separately apply a single gel or different types of mixed gels in the manufacturing process of reacting cigarette and exciting pulp to heat the cigarette.
[0086] Papermaking method heating the cigarette use to make tobacco:
[0087]Method 1: A quantitative cosmetic (1,2-propanediol, glycerol or two proportible mixtures) is added to the preparation of the carrier super molecular gel, and the quality of the super molecular gel and the quality of the smoke. The ratio is 5: 1, warmed to 85 ° C, gel melting into a sol, uniformly mixed, forming a mixed coating liquid containing a molten gel and a smoke agent, spraying a mixed coating liquid to paper The preparative tobacco tablet is made. Reproduction tobacco the above mixed coating liquid is applied to room temperature, which...
Embodiment 3
[0099] This example provides the application of the carried abstentive ultra molecular gel prepared in Example 1 in the electronic smoke.
[0100] The Niurota salt hypermor gel can be applied to the electronic cigarette in two ways and can be used in accordance with the actual use of a single gel or different types of mixed gels.
[0101] Method 1: After 24-36 h, a hemolecular gel prepared in an oven at a 40 ° C oven 24-36 h, after the drying gel is ground into a uniform microparticle, and a certain amount of electronic smoke is added to a certain proportion. The mixture is thoroughly stirred in the changering agent, and the hybrid agent is a mixed solvent of glycerol and 1,2-propylene glycol 1.5: 1 (volume ratio), and the proportion of incense ultrasonic gel and the hairy agent mass is 1: 120, and after mixing is uniform. Fragrant gel-containing cosmetic or as an excipients were added to the finished tofonic mixed uniform mixed uniform as a metallogenic gel.
[0102] Smoky in the...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com