A kind of nanosheet layered carbon black emulsion and its preparation method and application

A technology of nanosheets and carbon black, applied in chemical instruments and methods, fibrous fillers, textiles and papermaking, etc., can solve the problems of uneven coating, complicated process, high cost, etc., solve the problem of agglomeration and improve antistatic Sexuality, the effect of excellent application performance

Active Publication Date: 2022-04-15
SUZHOU UNIV
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The surface coating of carbon black, although the modification conditions are mild, but the process is complicated, and problems such as uneven coating or homopolymers are prone to occur; methods such as grafting and oxidation of carbon black are chemical changes, which can effectively solve the problem of dispersants The problem of desorption, the dispersion system is durable and stable, but there are also some problems, such as the reaction is too complicated, the pollution is large, the cost is high, and it is difficult to carry out industrial production, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of nanosheet layered carbon black emulsion and its preparation method and application
  • A kind of nanosheet layered carbon black emulsion and its preparation method and application
  • A kind of nanosheet layered carbon black emulsion and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] 2000 kg of carbon 15F, 168 g of dispersant MF, 200 grams of sodium plain sulfate-N, 55 grams of octadamine polyoxyethylene ether (EO = 15), 117 grams of flat plus O15 (EO = 15), 78 The polyether polyol HSH, 32 g of dispersant RQT-Fs and 7350 g of water were premixed, and the carbon black solution was obtained, and the abrasive was 650 grams. Carbon black solution was continuously ground in a zirconia abrasive apparatus for 3 hours to prepare a carbon black emulsion. The above-mentioned carbon black emulsion was placed in a container, and solid bulk carbon black A was dried.

Embodiment 2

[0035] 3000 g of charging F15, 300 g of dispersant MF, 314 grams of wood sulfate-N, 100 grams of octadamine polyoxyethylene ether (EO = 20), 100 grams of flat plus O15 (EO = 30), 156 The polyether polyol HSH, 30 grams of dispersant RQT-FS and 6000 g of water were premixed, produced carbon black solution, and the abrasive was 1000 grams. Carbon black solution was continuously ground in a zirconia abrasive apparatus for 3 hours to prepare a carbon black emulsion. The above-mentioned carbon black emulsion was placed in a container, and the solid bulk carbon black B was dried.

[0036] Embodiment 4 of another inventive application (a speed-soluble ultra-fine solid bulk carbon black and preparation method and application thereof) is respectively submitted in the same day, respectively, and Example 5; The materials composition of 3 to Example 6 are as follows:

[0037]

[0038] In the table, the fourth column 4 to 9 is the detailed composition of the dispersant.

Embodiment 3

[0040] 500 grams of solid bulk carbon black A (Example 1), 10 grams of dispersant MF, 21 grams of sodium sulfonate N, 4 g of octade amine polyoxyethylene ether (EO = 15), 4 grams flat plus O15 (EO = 15), 8 grams of polyether polyol HSH, 3 g of dispersant RQT-Fs and 9450 g of water were premixed, and the carbon black solution was obtained. The carbon black solution was continuously ground in the zirconia abrasive apparatus for 2 hours, and the carbon black particle diameter was not higher than 100 nm of nanoculate black emulsion.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a nanosheet layered carbon black emulsion and its preparation method and application. The powdery carbon black is ground in the presence of abrasives and water, and then dried to obtain block carbon black, block carbon black and dispersant , mixed with water and then ground to obtain a nano-sheet carbon black emulsion, so as to obtain a nano-carbon black emulsion with a carbon black particle size not higher than 100nm; It has better application performance, and avoids dust pollution in the preparation process; the processing equipment of the present invention is conventional equipment, which is a green manufacturing technology.

Description

Technical field [0001] The present invention relates to a preparation technique of a carbon-based material, and more particularly to a nano sheet-like carbon black emulsion prepared to solve the dust pollution of existing powdered carbon black and significantly improve the performance of carbon black materials. Background technique [0002] Carbon black particles are a statistical binding of the carbon-level, which is arranged in concentric graphite. Carbon black In the production process, the incomplete cleavage of hydrocarbon substances will still contain a small amount of hydrocarbons in the product, especially polycyclic aromatic substances. These materials are wrapped in the surface of the carbon black particles such that the surface of the carbon black particles exhibits non-polar, and the specific surface area is large, resulting in the presence of carbon black particles, usually in the context, under the action of shear external force, aggregate It can be reissued and can...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09C1/48C09C1/56C09C3/10D06M11/74D06M101/32D06M101/38
CPCC09C1/56C09C1/48C09C3/041C09C3/006C09C3/10D06M11/74D06M2101/32D06M2101/38
Inventor 候礼文艾丽朱亚伟
Owner SUZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap