A sintering method with low energy consumption and low emission by compound injection of multi-component gas medium

A technology of gas medium and sintering method, which is applied in the direction of reducing gas emissions, can solve the problems of limited ability to reduce fossil fuel consumption, limited degree of emission reduction, and inability to reduce emissions of multiple pollutants at the same time, achieving obvious economic advantages, Improved yield and low cost

Active Publication Date: 2022-05-17
CENT SOUTH UNIV
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the defects that the existing single-medium injection technology cannot achieve simultaneous emission reduction of multiple pollutants, and the degree of emission reduction is limited, and the ability to reduce fossil fuel consumption is limited. The purpose of the present invention is to provide a method that can Meet the heat demand at different heights of the material layer, synergistically improve fuel combustion efficiency, further reduce solid fossil fuel consumption, and make CO 2 Greenhouse gas and CO, NO X , SO X Low energy consumption and low emission sintering method of multi-component gas medium compound injection with effective emission reduction of various pollutants such as dioxin and dioxin

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A sintering method with low energy consumption and low emission by compound injection of multi-component gas medium

Examples

Experimental program
Comparison scheme
Effect test

Embodiment -1

[0035] According to the mass ratio of 59.77% mixed iron ore, 4.27% dolomite, 5.57% limestone, 3.46% quicklime, 13.85% sintered ore return, 9.23% blast furnace return ore, and 3.85% coke powder (the chemical composition of the obtained sintered ore is TFe56. 08%, R1.80, MgO1.80%, CaO10.76%), after the materials are mixed and granulated, they are placed on the sintering surface, ignited for 1min at a temperature of 1050±50°C, held for 1min, and then heated under negative pressure Sintering is carried out under the condition of 15kPa. The sintering process is divided into three gas medium injection areas from the end of ignition to the beginning of exhaust gas temperature rise (see Figure-1 for the schematic diagram): Area-1 accounts for 40% of the entire interval, and the total concentration of the injected medium is 0.8% (70 % coke oven gas, 20% water vapor (temperature 200°C, pressure 1.57MPa), 10% oxygen); area-2 accounts for 40% of the entire interval, and the total concentr...

Embodiment -2

[0037] According to the mass ratio of 59.77% mixed iron ore, 4.27% dolomite, 5.57% limestone, 3.46% quicklime, 13.85% sintered ore return, 9.23% blast furnace return ore, and 3.85% coke powder (the chemical composition of the obtained sintered ore is TFe56. 08%, R1.80, MgO1.80%, CaO10.76%), after the materials are mixed and granulated, they are placed on the sintering surface, ignited for 1min at a temperature of 1050±50°C, held for 1min, and then heated under negative pressure Sintering is carried out under the condition of 15kPa. The sintering process is divided into three gas medium injection areas from the end of ignition to the beginning of exhaust gas temperature rise (see Figure-1 for the schematic diagram): Area-1 accounts for 50% of the entire interval, and the total concentration of injected medium is 1.0% (75 % converter gas, 10% water vapor (temperature 200°C, pressure 1.57MPa), 15% oxygen); zone-2 accounts for 40% of the entire interval, and the total concentratio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
percent by volumeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a low-energy-consumption and low-emission sintering method of multi-component gas medium compound injection. The method divides the area between the sintering material surface in the sintering machine from the ignition end point to the exhaust gas temperature rising point into areas in sequence. -1, area-2 and area-3; during the sintering process, a high gas ratio multi-component gas medium is injected into area-1, a medium gas ratio multi-component gas medium is injected into area-2, and a multi-component gas medium is injected into area-3 Blowing low gas ratio and multi-component gas medium, this method can meet the limitations of different heat requirements at different heights of the material layer to a greater extent, synergistically improve fuel combustion efficiency, further reduce solid fossil fuel consumption, and reduce solid fuel consumption by 6~ 10kg, CO emission reduction 2 18-30%, CO 25-40%, dioxin 40-70%.

Description

technical field [0001] The present invention relates to a sintering method, in particular to a sintering method with low energy consumption and low emission by compound injection of multi-component gas medium, in particular to a method of injecting different components according to the characteristics of different sections of the sintering material layer and the heat demand. The invention relates to a method for synergistically improving fuel combustion efficiency, reducing consumption of solid fossil fuels, and reducing emissions by composing gaseous media, and belongs to the sintering industry in the field of iron and steel metallurgy. Background technique [0002] As a front-end process of the iron and steel industry, sintering has high energy consumption and heavy pollution load, which poses severe challenges to the clean production of the iron and steel industry. In the traditional sintering process, solid fossil fuels such as coke and anthracite are generally used as h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22B1/16
CPCC22B1/16Y02P10/143
Inventor 季志云范晓慧甘敏赵元杰陈许玲黄晓贤袁礼顺武钰丰李浩锐
Owner CENT SOUTH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com