Preparation method and processing equipment of rosin resin

A technology of rosin resin and processing equipment, applied in the field of rosin processing, which can solve the problems of unfavorable rosin resin widely used, deep color, poor thermal stability, etc., and achieve the effect of reducing heat emission, improving thermal stability, and preventing oxidation

Active Publication Date: 2021-06-11
广西上林县林发松香有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing rosin resins are generally difficult to meet the needs of use. Existing rosin resins have a darker color and poor thermal stability, which is not conducive to the widespread use of rosin resins.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method and processing equipment of rosin resin
  • Preparation method and processing equipment of rosin resin
  • Preparation method and processing equipment of rosin resin

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A kind of processing equipment used in the preparation method of rosin resin, comprises reactor shell 1, agitator 2, feed pipe 3 and discharge pipe 5, and described agitator 2 is above described reactor shell 1 , and the stirring shaft 14 of the agitator 2 is inserted in the reactor shell 1, and the left and right sides of the stirring shaft 14 in the reactor shell 1 are provided with a number of stirring blades 15, the The left and right sides of the bottom end of the stirring shaft 14 are respectively fixed with two stirring blades 16, the feed pipe 3 is positioned on the upper side of the reactor shell 1, and the upper side of the reactor shell 1 is also provided with Auxiliary material pipe one 4, the middle part of the bottom end of the reactor shell 1 is provided with a discharge pipe 5, and the bottom end of the reactor shell 1 is also provided with an auxiliary material pipe two 6, the bottom end of the reactor shell 1 is A support rod 7 is provided, a pressure ...

Embodiment 2

[0027] A preparation method for rosin resin, specifically comprising the following steps:

[0028] 1) Modified catalyst carrier: first make the concentration of 2mol / L NH 4 HCO 3 solution and 2mol / L Al(OH) 3 Solution reaction, adjustment makes the pH value of reaction be between 9, reacts and filters and obtains precipitate, and the precipitate obtained is cleaned, makes the precipitate after cleaning and mass concentration be 8% TiO 2 Reaction, adding ethanol and sodium pyrophosphate at the same time, under the condition of heating in a water bath, the reaction temperature is 75°C, after the reaction, perform suction filtration, washing, impregnation, drying, and calcination to obtain modified nano-alumina;

[0029] 2) prepare catalyst: first make 30 parts of nano silicon dioxide and 0.2 part of emulsifier add 60 parts of deionized water, described emulsifier comprises polyoxyethylene 20 sorbitan monooleate and glyceryl monostearate, and The mass ratio between the polyoxye...

Embodiment 3

[0032] A preparation method for rosin resin, specifically comprising the following steps:

[0033] 1) Modified catalyst carrier: first make the concentration of 2mol / L NH 4 HCO 3 solution and 2mol / L Al(OH) 3 Solution reaction, adjustment makes the pH value of reaction between 10, reacts and filters and obtains precipitate, the precipitate obtained is cleaned, makes the precipitate after cleaning and mass concentration be 8% TiO 2 Reaction, adding ethanol and sodium pyrophosphate at the same time, under the condition of heating in a water bath, the reaction temperature is 85°C, after the reaction, perform suction filtration, washing, impregnation, drying, and calcination to obtain modified nano-alumina;

[0034] 2) prepare catalyst: first make 50 parts of nano silicon dioxide and 0.4 part of emulsifier add 80 parts of deionized water, described emulsifier comprises polyoxyethylene 20 sorbitan monooleate and glyceryl monostearate, and The mass ratio between the polyoxyethylen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention is applicable to the technical field of rosin processing, and provides a preparation method and processing equipment of rosin resin, in the preparation method of the rosin resin, nano aluminum oxide is modified to serve as a carrier, so that the nano aluminum oxide has good carrying capacity and is beneficial to carrying silicon dioxide; silicon dioxide is used as a carrier, so that the reaction can be well catalyzed, impurities in the rosin resin can be adsorbed, and the color of the rosin resin can be lightened; an antioxidant is added in the preparation process of the rosin resin, so that the rosin resin can be effectively prevented from being oxidized, the color of the rosin resin is further lightened, and meanwhile, the thermal stability of the rosin resin can be effectively improved; and the rosin resin processing equipment disclosed by the invention has a good heat preservation and heat insulation effect, and is beneficial to the proceeding of a reaction.

Description

technical field [0001] The invention belongs to the technical field of rosin processing, and in particular relates to a method for preparing rosin resin and processing equipment thereof. Background technique [0002] Rosin, also known as turpentine, is the substance distilled from the resin contained in pine trees. It is solid and transparent in appearance, light yellow or brown in color, hard and brittle, insoluble in water and soluble in alcohol. It can be used in industry, Flux, Chinese medicinal materials, stringed musical instruments, etc. According to its source, rosin is divided into three types: gum rosin, wood rosin and tall oil rosin. Gum rosin is also called relaxing incense, with light color, large acid value and high softening point; wood rosin is also called leaching rosin, its quality is not as good as gum rosin, dark in color, small in acid value, and easy to crystallize from certain solvents; tall oil rosin Also known as tall oil rosin. Rosin is a transpa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09F1/02B01J21/12B01J19/18B01J19/00B01J20/10B01J20/30
CPCB01J19/0053B01J19/0066B01J19/18B01J20/103B01J21/12C09F1/02
Inventor 陈秉煌
Owner 广西上林县林发松香有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com