Preparation process of cool quick-drying composite fibers and fabric

A preparation process and composite fiber technology, applied in fiber treatment, fiber chemical characteristics, rayon manufacturing, etc., can solve the problems of decreased contact coolness and no improvement in quick-drying performance, so as to reduce water absorption and keep cool Sensitive properties, the effect of increasing the coolness of contact

Active Publication Date: 2021-04-23
XIAMEN ANTA SPORTS GOODS CO LTD
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing nylon / polyester skin-core composite fiber generally maintains part of the characteristics of nylon, mainly to reduce costs, but the cool feeling of the composite fiber material decreases, and the quick-drying performance has not been greatly improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation process of cool quick-drying composite fibers and fabric
  • Preparation process of cool quick-drying composite fibers and fabric
  • Preparation process of cool quick-drying composite fibers and fabric

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0028] The embodiment of the present invention first carries out the preparation of fiber cortex material:

[0029] In parts by mass, mix 84-89 parts of PA6 slices, 10-13 parts of jade powder, and preferably 1-3 parts of coupling agent, and add them into a twin-screw machine to melt at a temperature of 230-250°C. The rotating speed can be 100-130r / min. The above-mentioned nylon material in the molten state is extruded through the head of the wire drawing machine, and the extrusion temperature is preferably controlled at 210-220° C., and the head pressure of the wire drawing machine is 0.2-0.3 MPa. After the nylon filament is cooled by the cold water tank, it enters the granulator and cuts into granules. The speed of the granulator can be 140r / min, and the particle size is generally 3-6mm. The mass parts and process parameters within the scope of this application can meet the production requirements, and have little influence on the final fiber performance.

[0030] Among the...

Embodiment 1

[0054] 1. Preparation of fiber cortex material:

[0055] In parts by mass, mix 84-89 parts of PA6 slices, 10-13 parts of jade powder, and 1-3 parts of coupling agent evenly and add them to a twin-screw machine, melt at a temperature of 230-250°C, and the screw speed is 100-130r / min. The nylon material in the molten state is extruded through the head of the wire drawing machine, the extrusion temperature is controlled at 210-220°C, and the pressure of the head of the wire drawing machine is 0.2-0.3MPa. After the nylon filament is cooled by the cold water tank, it enters the granulator and cuts into granules. The speed of the granulator is 140r / min, and the particle size is 3-6mm.

[0056] 2. Preparation of skin-core composite fiber:

[0057] 1) Add the fiber sheath material prepared above into the first screw extruder, melt and extrude it into a melt, then transport the melt to the spinning box, pass through the pre-filter, and evenly distribute it to the sheath core In com...

Embodiment 2

[0076] 1. Preparation of fiber cortex material:

[0077] In parts by mass, mix 84-89 parts of PA6 slices, 10-13 parts of jade powder, and 1-3 parts of coupling agent evenly and add them to a twin-screw machine, melt at a temperature of 230-250°C, and the screw speed is 100-130r / min. The nylon material in the molten state is extruded through the head of the wire drawing machine, the extrusion temperature is controlled at 210-220°C, and the pressure of the head of the wire drawing machine is 0.2-0.3MPa. After the nylon filament is cooled by the cold water tank, it enters the granulator and cuts into granules. The speed of the granulator is 140r / min, and the particle size is 3-6mm.

[0078] 2. Preparation of skin-core composite fiber:

[0079]1) Add the fiber sheath material prepared above into the first screw extruder, melt and extrude it into a melt, then transport the melt to the spinning box, pass through the pre-filter, and evenly distribute it to the sheath core In comp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention provides a reparation process of cool quick-drying composite fibers and fabric. The preparation process of the cool quick-drying composite fibers comprises the following steps: melting and extruding a fiber skin layer material into first melt according to a high-temperature melting and low-temperature extrusion mode; melting and extruding a fiber core layer material into second melt according to a low-temperature melting and high-temperature extruding mode; wherein the fiber skin layer material comprises 84-89 parts by weight of PA6 and 10-13 parts by weight of jade powder; and the fiber core layer material is polypropylene; and carrying out extrusion molding on the first melt and the second melt through a skin-core composite spinning assembly, and drafting is conducted to obtain the cool quick-drying composite fibers. The skin-core composite fibers prepared by the invention not only maintain the cool feeling characteristic of a nylon material, but also improves the quick-drying performance of the nylon material, and improves the wearing comfort. The contact cooling coefficient Q-max value of the fabric woven by the fibers is 0.20 or above, and the fabric has good quick-drying performance and is comfortable to wear.

Description

technical field [0001] The invention relates to the technical field of textile materials, in particular to a preparation process and fabric of a cool-feeling quick-drying composite fiber. Background technique [0002] Nylon is a term for polyamide fiber (nylon), which can be made into long fibers, short fibers, etc. Nylon is the trade name of polyamide (PA) fiber, also known as nylon (Nylon); there are many varieties of PA, such as PA6 and PA66. Nylon material is widely used in clothing. It has excellent wear resistance and heat resistance (the melting point of nylon 6 is 220°C, and the melting point of nylon 66 is 260°C). [0003] Especially in the summer clothing category, nylon T-shirts have an excellent cooling experience. Compared with polyester materials, nylon fabrics bring a cooler feeling. Part of the reason is that the amino groups contained in the molecular structure of polyamide fibers are a type of hydrophilic group, and water has a larger specific heat capaci...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01D5/34D01F8/12D01F8/06D01F1/10D01D1/04
CPCD01D5/34D01F8/12D01F8/06D01F1/10D01D1/04
Inventor 张伟强曾国坪胡凯
Owner XIAMEN ANTA SPORTS GOODS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com