A kind of preparation method of granule for ternary cavity filter rod

A technology of particles and filter rods, which is applied in the field of preparation of particles for ternary cavity filter rods. It can solve the problems affecting the effect of filter rod adhesives, affecting the quality of cigarette smoking, and the cracking of finished filter rods, etc., to achieve particle flow Good performance, regular and beautiful appearance, good material absorption performance

Active Publication Date: 2022-05-20
CHINA TOBACCO YUNAN NEW MATERIAL
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the leakage of limonene components will affect the effect of the filter stick adhesive, causing the problem of cracking of the finished filter stick
Moreover, limonene components will also diffuse to the end of the shredded tobacco when escaping, so that the essence partly volatilizes to the end of the shredded tobacco, and participate in combustion when the cigarette is smoked, affecting the smoking quality of the cigarette

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0038] The preparation method of the particles for the ternary cavity filter rod of the present disclosure comprises the following steps:

[0039] Step (1): According to the mass ratio (10-60): 1, the denatured tapioca starch and the porous starch are uniformly mixed, and then a flavoring treatment is performed to obtain the first mixture. The material absorption performance of modified tapioca starch can reach 40%-50%, and the material absorption performance of porous starch can reach 50%-60%.

[0040] In order to more effectively reduce the bursting of the finished filter rod and reduce the dissipation of limonene components, step (1) is specifically as follows:

[0041] Step (1-1): According to the mass ratio (10-60): 1, the denatured tapioca starch and the porous starch are evenly mixed to obtain the first premix.

[0042] Step (1-2): After uniformly mixing the first premix and the primary flavoring spice, the first mixture is obtained, wherein the mass percentage of the ...

Embodiment 1

[0065] The denatured tapioca starch and the porous starch are mixed according to the mass ratio of 40:1, and the raw materials after mixing are flavored once (the flavored spices include 12.0% tangerine peel extract, 0.2% tree moss extract, 1.0% apple juice, Sydney extract 1.0%, citral 1.0%, limonene 10.0% and propylene glycol 74.8%), flavoring amount is 16%, obtains the first mixture;

[0066] Put the first mixture and tangerine peel powder in a conical mixer according to the mass ratio of 20:1 and mix for 2 hours to obtain the second mixture;

[0067] Add an adhesive to the second mixture, the adhesive is 2% sodium carboxymethyl cellulose aqueous solution, after mixing, add a granulator to granulate, and the granulator is a screw extrusion granulator;

[0068] Shot blasting is carried out on the prepared particles, and after shot blasting, they are screened according to 14-20 mesh to obtain pellets with a moisture content of 6%;

[0069] Carry out secondary flavoring to pel...

Embodiment 2

[0072] The denatured tapioca starch and the porous starch are mixed according to a mass ratio of 50:1, and the raw materials after mixing are flavored once (the flavored spices include 15.0% orange peel extract, 0.1% tree moss extract, 1.0% apple juice, Sydney extract 1.0%, 1% citral 1.0%, limonene 8.0% and propylene glycol 73.9%), the flavoring amount is 15%, obtains the first mixture;

[0073] Put the first mixture and tangerine peel powder in a conical mixer according to the mass ratio of 10:1 and mix for 2 hours to obtain the second mixture;

[0074] Add an adhesive to the second mixture, the adhesive is 2% methyl cellulose aqueous solution, after mixing, add a granulator to granulate, and the granulator is a screw extrusion granulator;

[0075] Shot blasting is carried out on the manufactured particles, and after shot blasting, they are screened according to 14-20 mesh to obtain pellets with a moisture content of 7%;

[0076] Carry out secondary perfuming to pellet (seco...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
degree of polymerizationaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of granules for ternary cavity filter rods, comprising: mixing denatured tapioca starch and porous starch uniformly according to the mass ratio (10-60): 1, and then performing a flavoring treatment to obtain the first mixed Material; According to mass ratio (20-1): 1, the first compound material and tangerine peel powder are mixed uniformly, obtain the second compound material; Carry out shot blasting after the second compound material is granulated, obtain pellets; Carry out secondary flavoring treatment to obtain flavoring granules, the mass percentage content of secondary flavoring spices is 3% - 8% of the flavoring granules; carry out coating treatment to the flavoring granules, obtain the three-way cavity filter Granules for sticks. The method of the present disclosure embeds the limonene-like essence in the modified starch to form a small fragrance group by adding fragrance twice, and after granulation, the escape of the limonene-like ingredients is blocked by coating, thereby solving the problem of bursting during the preparation of the filter stick. Mouth problems, and the problem of reduced smoking quality caused by the leakage of limonene components.

Description

technical field [0001] The invention relates to the field of composite filter rods, in particular to a method for preparing particles for ternary cavity filter rods. Background technique [0002] In recent years, the research on cigarette materials and the application of new materials have continuously promoted the reform and innovation of cigarette products. Granular composite filter sticks are currently the most widely used special filter sticks for cigarettes at home and abroad. Compared with single-structure filter sticks such as acetate fiber filter sticks, various functional particles are added to the inner section of the granular composite filter sticks, making the composite filter sticks not only have a choice It has the function of permanently adsorbing harmful components in the flue gas, and can also make up for the loss of aroma caused by harm reduction and coke reduction. [0003] The existing orange flavor applied to the filter stick is mainly composed of limon...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01D39/04B01J20/24B01J20/28B01J20/30C11B9/00A24D3/14
CPCB01D39/04B01J20/24B01J20/28016C11B9/00C11B9/0015C11B9/0007A24D3/14B01D2239/0407B01D2239/10B01J2220/4825B01J2220/4812
Inventor 刘鑫张强徐世涛刘强吴恒赵立恒肖永银杜超蒋卓芳陈婉王厚娴
Owner CHINA TOBACCO YUNAN NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com