Dlp type 3d printing photocuring material for clinical dental temporary crown

A light-curing material and 3D printing technology, applied in dentistry, dental preparations, dental prostheses, etc., can solve the problems of poor performance stability, poor dimensional stability, poor mechanical properties, etc., to improve detail resolution and reduce workpieces Effects of lamination and viscosity reduction

Inactive Publication Date: 2021-02-12
WUXI CITY CASHEW NEW MATERIALS CO LTD
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Aiming at the problems in the prior art, the present invention provides a dlp-type 3D printing light-curing material that can be used for clinical dental temporary crowns to solve the defects of foreign restoration materials. It uses nano-organic-inorganic hybrid UV resin as the scaffold structure, and cooperates with inorganic The silver-based antibacterial agent forms a free radical system, which effectively improves the problems of poor material performance stability, poor dimensional stability, poor toughness, poor mechanical properties, and medical risks.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Dlp type 3d printing photocuring material for clinical dental temporary crown
  • Dlp type 3d printing photocuring material for clinical dental temporary crown
  • Dlp type 3d printing photocuring material for clinical dental temporary crown

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A dlp-type 3D printing light-curing material that can be used for clinical dental temporary crowns, its quality ratio is as follows:

[0028] Nano-organic-inorganic hybrid UV resin 30g; high-strength aliphatic urethane acrylate 30g; high-toughness aliphatic urethane acrylate 30g; monofunctional free radical acrylate monomer 30g; difunctional free radical acrylate monomer 10g; Free radical acrylate monomer 10g; inorganic silver-based antibacterial agent 10g; pigment 5g; 2,4,6-trimethylbenzoyl-diphenylphosphine oxide 10g.

[0029] The nano-organic-inorganic hybrid UV resin adopts POSS-PCL hybrid UV resin, and the resin highly reactive primary hydroxyl polycaprolactone oligomer and polyamino POSS monomer react to synthesize POSS-PCL hybrid material, and then The POSS-PCL hybrid material was grafted to the (meth)acrylic group capable of radical polymerization to synthesize nano-organic-inorganic hybrid UV resin.

[0030] Allnex EBECRYL 4666 is used for the high-strength al...

Embodiment 2

[0040] A dlp-type 3D printing light-curing material that can be used for clinical dental temporary crowns, its quality ratio is as follows:

[0041] Nano-organic-inorganic hybrid UV resin 10g; high-strength aliphatic urethane acrylate 10g; high-toughness aliphatic urethane acrylate 10g; monofunctional free radical acrylate monomer 3g; difunctional free radical acrylate monomer 3g; Free radical acrylate monomer 3g; inorganic silver-based antibacterial agent 1g; pigment 1g; 2,4,6-trimethylbenzoyl-diphenylphosphine oxide 1g.

[0042] The nano-organic-inorganic hybrid UV resin adopts POSS-PCL hybrid UV resin, and the resin highly reactive primary hydroxyl polycaprolactone oligomer and polyamino POSS monomer react to synthesize POSS-PCL hybrid material, and then The POSS-PCL hybrid material was grafted to the (meth)acrylic group capable of radical polymerization to synthesize nano-organic-inorganic hybrid UV resin.

[0043] Allnex EBECRYL 4666 is used for the high-strength aliphat...

Embodiment 3

[0053] A dlp-type 3D printing light-curing material that can be used for clinical dental temporary crowns, its quality ratio is as follows:

[0054] Nano-organic-inorganic hybrid UV resin 20g; high-strength aliphatic urethane acrylate 20g; high-toughness aliphatic urethane acrylate 20g; monofunctional free radical acrylate monomer 8g; difunctional free radical acrylate monomer 8g; Free radical acrylate monomer 8g; inorganic silver-based antibacterial agent 6g; pigment 3g; 2,4,6-trimethylbenzoyl-diphenylphosphine oxide 5g.

[0055] The nano-organic-inorganic hybrid UV resin adopts POSS-PCL hybrid UV resin, and the resin highly reactive primary hydroxyl polycaprolactone oligomer and polyamino POSS monomer react to synthesize POSS-PCL hybrid material, and then The POSS-PCL hybrid material was grafted to the (meth)acrylic group capable of radical polymerization to synthesize nano-organic-inorganic hybrid UV resin.

[0056] Allnex EBECRYL 4666 is used for the high-strength aliphat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of dentistry, and particularly relates to a dlp type 3d printing photocuring material for a clinical dental temporary crown, which takes nano organic-inorganic hybrid UV resin, high-strength aliphatic urethane acrylate, high-toughness aliphatic urethane acrylate and a free radical acrylate monomer diluent as main bodies and is matched with an inorganic silver antibacterial agent and a pigment, the dLp type 3D printing photocuring material for the clinical dental temporary crown is prepared from a 385nm wavelength free radical system composed of a photoinitiator, and the problems of poor material performance stability, poor size stability, poor toughness, poor mechanical property, medical risk and the like are effectively solved by using a special printingprocess and a post-treatment process.

Description

technical field [0001] The invention belongs to the field of dentistry, and in particular relates to a dlp type 3D printing light-curing material for clinical dental temporary crowns. Background technique [0002] A temporary crown, also known as a temporary crown, is a temporary full crown that is temporarily bonded in the patient's mouth after the preparation of the tooth for crown restoration and before the completion of the final crown restoration, and the patient cannot freely wear it. Currently, the temporary crown (bridge) technology used in the clinical dental market mainly uses plastic resin crowns, gun-mixed temporary crown and bridge resins, hand-mixed temporary crown and bridge resins, and self-curing temporary crown and bridge resins. Commonly used materials for crown restoration include zirconia, stainless steel, and polycarbonate. However, the traditional process has the disadvantages of high initial investment cost, long production cycle, high labor cost, lo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61K6/893A61K6/891A61K6/831A61K6/844B33Y70/10C08F283/00C08F220/20C08F222/14C08F222/22C08F222/20
CPCA61K6/831A61K6/844A61K6/891A61K6/893B33Y70/10C08F283/008C08F220/20C08F222/102C08F222/103C08L75/14C08L67/04
Inventor 覃章友雷晓航
Owner WUXI CITY CASHEW NEW MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products