Light bulletproof composite destroy-resistant plate for vehicle and preparation method of light bulletproof composite destroy-resistant plate

A lightweight and bulletproof technology, applied to the structure of armor plates, etc., can solve the problems of large thickness, incompatible with the lightweight development of armored vehicles, and heavy weight, so as to achieve the safety of protection, improve maneuverability and payload, and reduce weight Effect

Active Publication Date: 2020-12-29
JIANGSU LINRY NEW MSTAR TECH
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the existing anti-destruction boards made of PE composite materials can resist Type 53 7.62 steel core bullets with a thickness of 20-25mm and a weight of 19.6-24.5kg / ㎡. The thickness is large and the weight is heavy. Lightweight development of armored vehicles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Light bulletproof composite destroy-resistant plate for vehicle and preparation method of light bulletproof composite destroy-resistant plate
  • Light bulletproof composite destroy-resistant plate for vehicle and preparation method of light bulletproof composite destroy-resistant plate
  • Light bulletproof composite destroy-resistant plate for vehicle and preparation method of light bulletproof composite destroy-resistant plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] This embodiment provides a lightweight bulletproof composite anti-destruction board for vehicles, the process is as follows figure 1 As shown, the composite anti-destruction board is made of UHMWPE fiber material and adhesive.

[0038] In this embodiment, the UHNWPE fiber has a fineness of 1100-1200D and a strength of not less than 35cn / dten.

[0039] In this example, the modulus of the ultra-high molecular weight polyethylene fiber is 1470 cn / dtex.

[0040] In this example, the adhesive uses acrylic acid modified water-based polyurethane glue, and the specific preparation method is as follows:

[0041]By adding polytetramethylene ether glycol PTMEG, 2,2-dimethylolpropionic acid (DMPA), 1,4-dihydroxybutane, dicyclohexylmethane-4,4-diisocyanate (HMDI), Accurately weigh and add to the reaction kettle one by one, start stirring, slowly heat the mixture in the reaction kettle to 70.0°C, and then add 2 drops of catalyst;

[0042] The temperature of the reaction kettle is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a light bulletproof composite destroy-resistant plate for a vehicle. The composite destroy-resistant plate is prepared by compounding a UHMWPE fiber material and an adhesive. The invention further relates to a preparation method of the light bulletproof composite destroy-resistant plate for the vehicle. The preparation method is simple and easy to implement, and the prepared destroy-resistant plate is light in weight, high in environmental adaptability, high in protection performance and small in depth of concavity; and the maneuvering performance and the effective loadof the vehicle are improved, and the safety of the vehicle and personnel is protected to the maximum extent.

Description

technical field [0001] The invention relates to an important protective equipment for armored vehicles, in particular to a lightweight bulletproof composite anti-destruction board for vehicles and a preparation method thereof, belonging to the technical field of polymer material development. Background technique [0002] Armored vehicles such as the Dongfeng Mengshi high-mobility off-road vehicle, in order to meet the requirements of bulletproof performance, are equipped with combat maneuverability when the armored vehicle is refitted, which requires protective equipment to realize it; The transition from simple synthetic materials to the development process of composite systems such as composite materials, metal armor plates, and ceramic shields. At present, the existing anti-destruction boards made of PE composite materials can resist Type 53 7.62 steel core bullets with a thickness of 20-25mm and a weight of 19.6-24.5kg / ㎡. The thickness is large and the weight is heavy. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B29C70/34C08L75/08C08L23/06C08L33/04F41H5/04
CPCB29C70/34B29C70/345C08L75/08F41H5/04C08L2205/03C08L2205/16C08L2207/068C08L2201/08C08L23/06C08L33/04
Inventor 郭振勤张鑫谭健魏秋生
Owner JIANGSU LINRY NEW MSTAR TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap