A method of wet carbonization to activate waste concrete regenerated micropowder and the application of regenerated micropowder

A technology of waste concrete and recycled micropowder, applied in cement production and other directions, can solve problems such as low utilization rate

Active Publication Date: 2022-03-01
HENAN POLYTECHNIC UNIV
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to overcome the technical problems of the prior art that the regenerated micropowder is directly utilized without treatment, the utilization rate is low, and an activator needs to be added, and a method for wet carbonization to activate waste concrete regenerated micropowder is proposed. Regenerated micropowder undergoes carbonization reaction in aqueous solution, and the calcium carbonate and silicon dioxide produced by carbonization have higher activity, and the activity of pozzolan is better than that of commonly used auxiliary cementing materials such as fly ash and silica fume, and can be used as auxiliary cementing materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method of wet carbonization to activate waste concrete regenerated micropowder and the application of regenerated micropowder
  • A method of wet carbonization to activate waste concrete regenerated micropowder and the application of regenerated micropowder
  • A method of wet carbonization to activate waste concrete regenerated micropowder and the application of regenerated micropowder

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A method for wet carbonization to activate waste concrete regenerated micropowder, comprising the following steps:

[0041] (1) After the waste concrete is crushed and screened, the regenerated micropowder with a particle size of less than 150 microns is collected, and the regenerated micropowder is added to water to form a mixed slurry with a concentration of 90 g / L. The water temperature is 20° C., and the stirring speed is 500 r / min;

[0042] (2) then pass into the industrial waste gas containing carbon dioxide in the mixed slurry formed in step (1), this industrial waste gas is the industrial waste gas of chemical industry, wherein the carbon dioxide volume fraction is 95%, and the ventilation rate of this industrial waste gas It is 0.2L / min / g, and the ventilation time is 10 minutes. During this process, the carbonization reaction between the regenerated micropowder and carbon dioxide occurs;

[0043] (3) Filtrating and drying the mixed slurry after the carbonizatio...

Embodiment 2

[0046] A method for wet carbonization to activate waste concrete regenerated micropowder, comprising the following steps:

[0047] (1) After crushing and screening the waste concrete, regenerated micropowder with a particle size of less than 150 microns is obtained, and the regenerated micropowder is added to water to form a mixed slurry with a concentration of 90 g / L. The water temperature is 20° C., and the stirring speed is 500 r / min;

[0048] (2) then pass into the industrial waste gas containing carbon dioxide in the mixed slurry formed in step (1), this industrial waste gas is the industrial waste gas of _ chemical industry, wherein the carbon dioxide volume fraction is 95%, and the ventilating of this industrial waste gas The rate is 0.2L / min / g, and the aeration time is 20 minutes. During this process, the carbonization reaction between the regenerated micropowder and carbon dioxide occurs;

[0049] (3) After the carbonization reaction in step (2) is completed, the mixe...

Embodiment 3

[0052] A method for wet carbonization to activate waste concrete regenerated micropowder, comprising the following steps:

[0053] (1) After crushing and screening waste concrete, regenerated micropowder with a particle size of less than 150 microns is obtained, and the regenerated micropowder is added to water to form a mixed slurry with a concentration of 60 g / L. The water temperature is 20° C., and the stirring speed is 300 r / min;

[0054] (2) then pass into the industrial waste gas containing carbon dioxide in the mixed slurry formed in step (1), this industrial waste gas is lime kiln industrial flue gas, wherein the carbon dioxide volume fraction is 37%, and the ventilation rate of this industrial waste gas It is 0.3L / min / g, and the ventilation time is 30 minutes. During this process, the carbonization reaction between the regenerated micropowder and carbon dioxide occurs;

[0055] (3) After the carbonization reaction in step (2) is completed, the mixed slurry is filtered...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The present invention proposes a method for activating recycled micropowder of waste concrete by wet carbonization. The powder produced in the process of crushing waste concrete to produce recycled aggregate is used as regenerated micropowder, and the regenerated micropowder is dispersed in water to form a mixed slurry, which is mixed in the The industrial waste gas containing carbon dioxide is continuously fed into the slurry, and during this process, the carbon dioxide contained in the industrial waste gas and the regenerated micropowder undergo a carbonization reaction. In the present invention, the regenerated micropowder is subjected to carbonization reaction in an aqueous solution, and the calcium carbonate and silicon dioxide produced by carbonization have higher activity, and the pozzolanic ash activity is better than auxiliary gelling materials such as commonly used fly ash and silica fume, and can be used as auxiliary gelling materials material used.

Description

technical field [0001] The invention belongs to the field of recycled micropowder of waste and old concrete, and in particular relates to a method for activating recycled micropowder of waste concrete by wet carbonization and an application of the recycled micropowder. Background technique [0002] Due to the demolition or collapse of buildings, a large amount of construction waste will be generated. According to statistics, China is the country that produces the most construction waste in the world. The annual construction waste production is nearly 2 billion tons, of which waste concrete accounts for about 30%-40%. Deactivates large areas of soil. On the other hand, my country's infrastructure needs about 10 billion tons of sand and gravel aggregates every year. If such a large-scale demand is met only by mining, it will inevitably cause excessive consumption of limited natural resources and destroy the sustainable development of the ecological environment. If the waste...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B7/24
CPCC04B7/246Y02P40/10
Inventor 刘松辉管学茂朱建平赵松海张海波王雨利史才军勾密峰
Owner HENAN POLYTECHNIC UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com