An anti-fingerprint and anti-glare coating, a protective film comprising the same and a preparation method thereof

An anti-glare and anti-fingerprint technology, applied in coatings, fireproof coatings, paints containing biocides, etc., can solve problems such as easy scratches, poor anti-fouling performance, glare and glare, etc., and achieve high light transmittance and clarity High, high transmittance effect

Active Publication Date: 2021-02-19
NINGBO FUNA NEW MATERIALS TECH CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The anti-fingerprint and anti-glare coating provided by the present invention is cured by UV. It is a coating with good hydrophobicity and oil repellency, high hardness and wear resistance, and excellent anti-fouling and anti-glare performance. Easy to scratch, poor stain resistance and glare problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • An anti-fingerprint and anti-glare coating, a protective film comprising the same and a preparation method thereof
  • An anti-fingerprint and anti-glare coating, a protective film comprising the same and a preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] a protective film such as figure 1 As shown, it includes an anti-fingerprint and anti-glare coating 1 and a substrate layer 2 stacked sequentially from top to bottom.

[0038] The material of the base material layer 2 is PC.

[0039]The specific raw material composition of the anti-fingerprint and anti-glare coating 1 is calculated by weight percentage, including the following components: 10% of 9-official aromatic urethane acrylate, 5% of 15-official aliphatic urethane acrylate, acrylic acid (N-methyl all 5% fluorohexylsulfonamido)ethyl ester, 4% dipentaerythritol hexaacrylate, a 6-official monomer, 3% low-official monomer (2-official, three-official mass ratio is 2:1), fluorinated acrylic acid monomer 1.5% , nanodiamond 0.5%, acrylic-cage polysilsesquioxane monomer 0.8%, leveling agent 0.3%, light stabilizer 0.2%, hydrophobic and oleophobic additive 1.5%, photoinitiator 0.9% (cyclo Hexyl phenyl ketone (IRGACURE 184) and 2-hydroxy-2-methyl-1-phenyl-1-propanone (DAROC...

Embodiment 2

[0055] What is different from Example 1 is 8% of 9 official aromatic urethane acrylates in the composition of the raw material formula, 4% of 15 official aliphatic urethane acrylates, 8% of ethyl acrylate (N-methyl perfluorohexylsulfonamido), The nano-diamond is 0.8%, the acrylic-cage polysilsesquioxane monomer is 1.25%, the composite solvent is 66.55%, and the others are the same as in Example 1.

Embodiment 3

[0057] What is different from Example 1 is that 9-official aromatic polyurethane acrylic acid 12%, 15-official aliphatic polyurethane acrylate 3% in raw material formula composition, acrylate (N-methyl perfluorohexylsulfonamido) ethyl ester 8%, acrylic acid The base-cage polysilsesquioxane monomer is 1.5%, the fluorinated acrylic acid monomer is 2%, the composite solvent is 66.1%, and others are the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
water contact angleaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an anti-fingerprint and anti-glare coating, a protective film containing the same and a preparation method thereof. The protective film includes an anti-fingerprint and anti-glare coating and a substrate layer sequentially stacked from top to bottom; the anti-fingerprint The fingerprint anti-glare coating is calculated by weight percentage, including the following components: 10-15% polyurethane acrylate, 5-8% fluorine-containing acrylate, 3-5% hexafunctional monomer, 2-3% low-functionality monomer , fluorine-containing functional monomer 1~2%, inorganic filler 0.5~0.8%, POSS monomer 0.5~2%, additive 2~3%, photoinitiator 0.5~1%, composite solvent 65~75%, each group The sum of the percentages by weight is 100%. The coating of the present invention has the characteristics of low haze, high light transmittance, high definition, good imaging quality and high visual visibility, and the coating can be used for a long time in relatively complex and severe environments.

Description

technical field [0001] The invention relates to the technical field of anti-glare coatings, in particular to an anti-fingerprint and anti-glare coating, a protective film containing it and a preparation method thereof. Background technique [0002] At present, substrates such as PC and PMMA are widely used in the fields of automotive central control panels and mobile phone screens due to their high transparency, light weight, impact resistance, and aging resistance. However, these materials have low surface hardness and are easy to scratch. It is easy to be stained with fingerprints and not resistant to dirt, so it is usually coated with a hard anti-fouling coating to solve this problem, but the effect is not satisfactory. [0003] The PC coating currently used in the market is not hard enough and not scratch-resistant, and its surface has a high gloss. When it is used in an environment with strong light, it is easy to cause glare, resulting in visual fatigue for users. It'...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D175/14C09D151/08C09D5/16C09D7/61C09D7/65C08J7/046C08F283/12C08F220/24C08L69/00C08L33/12C08L67/02
CPCC08F283/124C08J2333/12C08J2367/02C08J2369/00C08K2201/011C08L2201/08C08L2205/025C08L2205/03C09D5/1668C09D5/1681C09D5/1687C09D5/18C09D175/14C08J7/0427C08J7/046C08L75/14C08L51/08C08K3/04C08F220/24
Inventor 陈喆李友良张家祯朱小云
Owner NINGBO FUNA NEW MATERIALS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com