Method for catalytic oxidation of cycloalkane by bimetallic porphyrin MOFs PCN-224 (Co&Cu)

A double metal porphyrin, mofspcn-224 technology, applied in the field of industrial catalysis and fine organic synthesis, can solve the problems of reducing the selectivity of cycloalkyl alcohols and cycloalkyl ketones, increasing the uncontrollability of the reaction system, and poor selectivity of target products , achieve high selectivity, inhibit disordered diffusion, and have little environmental impact

Pending Publication Date: 2020-12-18
ZHEJIANG UNIV OF TECH
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the industrial catalytic oxidation of naphthenes is mainly based on homogeneous Co 2+ or Mn 2+ As a catalyst, oxygen (O 2 ) is an oxidizing agent, which is carried out at 150°C to 170°C. The main problems are that the reaction temperature is high, the conversion rate of the substrate is low, and the selectivity of the target product is poor, especially the formation of aliphatic diacids is difficult to suppress (Applied Catalysis A, General 2019 ,575:120-131; Catalysis Communications 2019,132:105809)
The main root causes of the above problems are: (1) O 2 Oxidation of cycloalkanes mainly undergoes a disordered free radical diffusion process; (2) the oxidation intermediate product, cycloalkyl hydroperoxide, converts to the target oxidation products cycloalkanol and cycloalkanone through a free radical thermal decomposition path, which increases the inability of the reaction system. controllability, reducing the selectivity of cycloalkyl alcohols and cycloalkyl ketones

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for catalytic oxidation of cycloalkane by bimetallic porphyrin MOFs PCN-224 (Co&Cu)
  • Method for catalytic oxidation of cycloalkane by bimetallic porphyrin MOFs PCN-224 (Co&Cu)

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Synthesis of PCN-224(Co&Cu)-1: In a 35mL pressure-resistant reaction tube, T(4-COOH)PPCo(II)(0.0282g, 0.033mmol), T(4-COOH)PPCu(II)(0.0568 g, 0.067mmol), ZrCl 4 (0.2540g, 1.090mmol), benzoic acid (3.3888g, 27.50mmol) were dissolved in 17.0mL DMF, and ultrasonicated for 30min until all dissolved. The mixture was placed in an electric constant temperature blast drying oven at 120° C. for 48.0 hours of static reaction. After the reaction is complete, turn off the heating, cool to room temperature naturally, filter the crude product with suction and rinse with DMF and acetone successively, then transfer to a 10.0mL centrifuge tube, centrifuge for 5min in a low-speed centrifuge (3000rpm), pour out the upper layer, and dry the DMF Leach (3×8.0mL) until the upper layer is clear, dry acetone leaching (3×8.0mL) until the upper layer is clear, remove the lower solid, and dry at 90°C for 8.0h to obtain a brick red powder (0.08260g, 68.21% yield Rate).

Embodiment 2

[0029] Synthesis of PCN-224(Co&Cu)-2: In a 35mL pressure-resistant reaction tube, T(4-COOH)PPCo(II)(0.0424g, 0.050mmol), T(4-COOH)PPCu(II)(0.0425 g, 0.050mmol), ZrCl 4(0.2540g, 1.090mmol), benzoic acid (3.3888g, 27.50mmol) was dissolved in 17.0mL DMF, and ultrasonicated for 30min until all dissolved. The mixture was placed in an electric constant temperature blast drying oven at 120° C. for 48.0 hours of static reaction. After the reaction is complete, turn off the heating, cool to room temperature naturally, filter the crude product with suction and rinse with DMF and acetone successively, then transfer to a 10.0mL centrifuge tube, centrifuge for 5min in a low-speed centrifuge (3000rpm), pour out the upper layer, and dry the DMF Leach (3×8.0mL) until the upper layer is clear, dry acetone leaching (3×8.0mL) until the upper layer is clear, remove the solid in the lower layer, and dry at 90°C for 8.0h to obtain a brick red powder (0.0835g, 68.95% yield Rate).

Embodiment 3

[0031] Synthesis of PCN-224(Co&Cu)-3: In a 35mL pressure-resistant reaction tube, T(4-COOH)PPCo(II)(0.0565g, 0.067mmol), T(4-COOH)PPCu(II)(0.0284 g, 0.033mmol), ZrCl 4 (0.2540g, 1.090mmol), benzoic acid (3.3888g, 27.50mmol) was dissolved in 17.0mL DMF, and ultrasonicated for 30min until all dissolved. The mixture was placed in an electric constant temperature blast drying oven at 120° C. for 48.0 hours of static reaction. After the reaction is complete, turn off the heating, cool to room temperature naturally, filter the crude product with suction and rinse with DMF and acetone successively, then transfer to a 10.0mL centrifuge tube, centrifuge for 5min in a low-speed centrifuge (3000rpm), pour out the upper layer, and dry the DMF Leach (3×8.0mL) until the upper layer is clear, dry acetone leaching (3×8.0mL) until the upper layer is clear, remove the solid in the lower layer, and dry at 90°C for 8.0h to obtain a brick red powder (0.0846g, 69.86% yield Rate).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for catalytic oxidation of cycloalkane by bimetallic porphyrin MOFs PCN224 (Co&Cu), which comprises the following steps: dispersing bimetallic porphyrin MOFs PCN224 (Co&Cu) in cycloalkane, wherein the mass of the bimetallic porphyrin MOFs PCN224 (Co&Cu) is 1-10% of the molar mass of the cycloalkane, g / mol; and sealing the reaction system, heating to 90-150 DEG C while stirring, introducing an oxidant (0.10-2.0 MPa), keeping the set temperature and pressure, stirring to react for 2.0-24.0 hours, and carrying out after-treatment on the reaction solution to obtain the products naphthenic alcohol and naphthenic ketone. The method disclosed by the invention has the advantages of high naphthenic alcohol and naphthenic ketone selectivity, low reactiontemperature, few byproducts, small environmental influence and the like. In addition, the content of cycloalkyl hydroperoxide is low, and the safety coefficient is high. The invention provides an efficient, feasible and safe method for synthesizing naphthenic alcohol and naphthenic ketone through selective catalytic oxidation of cycloalkane.

Description

technical field [0001] The invention relates to a method for synthesizing cycloalkanol and cycloalkanone by catalytically oxidizing cycloalkane with double metal porphyrin MOFs PCN-224 (Co&Cu), which belongs to the field of industrial catalysis and fine organic synthesis. Background technique [0002] Catalytic oxidation of naphthenes is a very important conversion process in the chemical industry. The oxidation products cycloalkanol and cycloalkanone are not only important organic solvents, but also important fine chemical intermediates, widely used in pesticides, medicines, dyes, surface Synthesis of fine chemical products such as active agents and resins, especially the production of polyamide fibers nylon-6 and nylon-66. At present, the industrial catalytic oxidation of naphthenes is mainly based on homogeneous Co 2+ or Mn 2+ As a catalyst, oxygen (O 2 ) is an oxidizing agent, which is carried out at 150°C to 170°C. The main problems are that the reaction temperature ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C07C45/33C07C29/50C07C49/403C07C49/413C07C35/08C07C35/20C07C35/205C07C49/395C07C35/06B01J31/22
CPCC07C45/33C07C29/50B01J31/183B01J31/1691C07C2601/08C07C2601/14C07C2601/20C07C2601/18B01J2231/70B01J2531/025B01J2531/16B01J2531/845C07C49/403C07C49/413C07C49/395C07C35/08C07C35/20C07C35/205C07C35/06
Inventor 沈海民郭阿兵
Owner ZHEJIANG UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com