Partridge spot Jian cup manufacturing process

A production process and partridge technology, which is applied in the field of partridge-spotted lantern manufacturing technology, can solve the problems of no display of partridge-spotted crystal patterns, low yield, bubbles, etc., and achieve high artistic value and appreciation value, deformation and stability. The effect of less blistering defects and clear process flow

Pending Publication Date: 2020-12-08
福建省鼎吉建盏陶瓷有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the production process of Partridge Banjian is very difficult. It is often difficult to control the formula, firing atmosphere and temperature curve, and the following defects often occur: body cracks, glaze sticking to the bottom, air bubbles, and glaze jumping. Glaze, partridge spot crystal pattern does not show or is not clear, the pattern is dim, etc., the yield is very low, and partridge spots are mostly silver drops on black background

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Partridge spot Jian cup manufacturing process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] The manufacturing process of partridge spot Jianzhan includes the following steps:

[0038] (1) preparing green body and glaze slurry;

[0039] The green body is prepared by the following method: mix red clay and pear puree by equal weight, add water to wash, pass through an 80-mesh sieve, press filter, stale for 5 years, smelt, and pull the green body to form a green body, dry it, and then repair the green body Molded, dried again and bisque fired to obtain the green body;

[0040] Wherein, the laterite and pear mud are all taken from Dali Village, Shuiji Town, Jianyang District, Nanping City, Fujian Province; the Dali Mud is the mud on the mountain of Dali Village;

[0041] The biscuit firing is that the temperature of the kiln rises to 800° C. after 6 hours, and the furnace is stopped for cooling.

[0042] The glaze slurry is prepared by the following method: mix 75 parts by weight of glaze ore, 15 parts by weight of plant ash, 2 parts by weight of iron red, and 8 ...

Embodiment 2

[0057] The manufacturing process of partridge spot Jianzhan includes the following steps:

[0058] (1) preparing green body and glaze slurry;

[0059] The green body is prepared by the following method: mix red clay and pear puree by equal weight, add water to wash, pass through a 90-mesh sieve, press filter, age for 4.5 years, smelt, and pull the green body to form a green body, dry it, and then repair the green body Molded, dried again and bisque fired to obtain the green body;

[0060] Wherein, the laterite and pear mud are all taken from Dali Village, Shuiji Town, Jianyang District, Nanping City, Fujian Province; the Dali Mud is the mud on the mountain of Dali Village;

[0061] The biscuit firing is that the temperature of the kiln rises to 850° C. after 6 hours, and the furnace is stopped for cooling.

[0062] The glaze slurry is prepared by the following method: take 75 parts by weight of glaze ore, 14 parts by weight of plant ash, 1.5 parts by weight of iron red, and ...

Embodiment 3

[0075] The manufacturing process of partridge spot Jianzhan includes the following steps:

[0076] (1) preparing green body and glaze slurry;

[0077] The green body is prepared by the following method: mix red clay and pear puree by equal weight, add water to wash, pass through a 100-mesh sieve, press filter, stale for 5.5 years, smelt, and pull the green body to form a green body, dry it, and then repair the green body Molded, dried again and bisque fired to obtain the green body;

[0078] Wherein, the laterite and pear mud are all taken from Dali Village, Shuiji Town, Jianyang District, Nanping City, Fujian Province; the Dali Mud is the mud on the mountain of Dali Village;

[0079] The biscuit firing is that the temperature of the kiln rises to 820° C. after 6 hours, and the furnace is stopped for cooling.

[0080] The glaze slurry is prepared by the following method: take 75 parts by weight of glaze ore, 15 parts by weight of plant ash, 1.8 parts by weight of iron red, a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a partridge spot Jian cup manufacturing process. The process comprises the following steps: preparing a green body and glaze slip, glazing, putting the glazed and aired green body into an electric kiln for roasting, cooling and discharging. According to the partridge spot Jian cup fired by the method, silver drops, yellow spots and stripes are clear from bottom to top on ablack and transparent ground color glaze surface, are well-arranged, are similar to partridge feathers and stripes one by one and are vivid, and meanwhile, the mouth edge is golden and glossy, so thatthe partridge spot Jian cup has extremely high artistic value and appreciation value.

Description

technical field [0001] The invention relates to the technical field of porcelain, and in particular relates to a manufacturing process of a partridge-ban Jianzhan. Background technique [0002] Black-glazed porcelain is a strange flower in the history of Chinese ceramics, well-known at home and abroad. Jianzhan is a typical representative of black-glazed porcelain. The colorful light phenomenon of Jianzhan is natural, mysterious and refined, and the markings of Jianzhan have obvious three-dimensional and layered feelings. What Jianzhan pursues is the artistic effect formed naturally. Its glaze pattern is not artificially painted, but formed under strict formula technology, special firing atmosphere and firing temperature curve. The three are indispensable. The artistic effect formed by Jianzhan has no sense of artificial carving at all, and it is completely a display of the essential beauty of its products. [0003] Jianzhan fired by ancient dragon kiln is generally black ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/04C04B33/13C04B41/86C03C8/00
CPCC04B33/04C04B33/13C04B41/5022C04B41/86C04B41/009C03C8/00C04B2235/5427C04B2235/612C04B2235/656C04B2235/6562C04B2235/6567C04B2235/658C03C2209/02C04B41/4535C04B41/0072
Inventor 杨敏
Owner 福建省鼎吉建盏陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com