Warm-keeping moisture-conducting multifunctional nylon 6 fiber and preparation method thereof

A multi-functional, nylon technology, applied in fiber processing, fiber chemical characteristics, conductive/antistatic filament manufacturing, etc., can solve the problems of warmth retention, moisture permeability, lightness and lightness, etc., to improve gloss effect and Hand feeling, simple production process and simple processing effect

Inactive Publication Date: 2020-12-04
SUZHOU UNIV
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of the above disadvantages, the present invention provides a heat-retaining and moisture-conducting multifunctional nylon 6 fiber and its preparation method. Disadvantages that gas and lightness cannot be combined

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Warm-keeping moisture-conducting multifunctional nylon 6 fiber and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A method for preparing warm and moisture-conducting multifunctional nylon 6 fibers, the steps are as follows:

[0041] (1) Raw material allocation;

[0042] At a temperature of 80°C, caprolactam, terephthalic acid and deionized water were mixed, wherein relative to the caprolactam, the amount of deionized water added was 1 wt%, and the amount of terephthalic acid added was 0.1 wt%;

[0043] (2) Ring-opening reaction;

[0044] Transfer the mixture obtained in step (1) to a ring-opening kettle for ring-opening reaction. The temperature of the ring-opening reaction is 230°C, the pressure is 0.1MPa, and the time is 3h;

[0045] (3) polycondensation reaction;

[0046] The ring-opening reaction product obtained in step (2) was subjected to polycondensation reaction to obtain nylon 6. The temperature of the polycondensation reaction was 230°C, the pressure was -0.1MPa, and the time was 3h;

[0047] (4) Nylon 6 is mixed with functional components, the content of functional c...

Embodiment 2

[0070] A method for preparing warm and moisture-conducting multifunctional nylon 6 fibers, the steps are as follows:

[0071] (1) Raw material allocation;

[0072] At a temperature of 95°C, caprolactam, terephthalic acid and deionized water were mixed, wherein relative to the caprolactam, the amount of deionized water added was 2 wt%, and the amount of terephthalic acid added was 0.2 wt%;

[0073] (2) Ring-opening reaction;

[0074] Transfer the mixture obtained in step (1) to a ring-opening kettle for ring-opening reaction. The temperature of the ring-opening reaction is 238°C, the pressure is 0.2MPa, and the time is 5h;

[0075] (3) polycondensation reaction;

[0076] The ring-opening reaction product obtained in step (2) was subjected to polycondensation reaction to obtain nylon 6. The temperature of the polycondensation reaction was 240° C., the pressure was 0 MPa, and the time was 5 hours;

[0077] (4) Nylon 6 is mixed with functional components, the content of functio...

Embodiment 3

[0084] A method for preparing warm and moisture-conducting multifunctional nylon 6 fibers, the steps are as follows:

[0085] (1) Raw material allocation;

[0086] At a temperature of 108°C, mix caprolactam, terephthalic acid and deionized water, wherein relative to caprolactam, the amount of deionized water added is 2.5wt%, and the amount of terephthalic acid added is 0.25wt% ;

[0087] (2) Ring-opening reaction;

[0088] Transfer the mixture obtained in step (1) to a ring-opening kettle for ring-opening reaction. The temperature of the ring-opening reaction is 245°C, the pressure is 0.5MPa, and the time is 6h;

[0089] (3) polycondensation reaction;

[0090] The ring-opening reaction product obtained in step (2) was subjected to a polycondensation reaction to obtain nylon 6. The temperature of the polycondensation reaction was 255° C., the pressure was 0.01 MPa, and the time was 9 hours;

[0091] (4) Nylon 6 is mixed with the functional component, the content of the func...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
heightaaaaaaaaaa
heightaaaaaaaaaa
Login to view more

Abstract

The invention relates to a warm-keeping and moisture-conducting multifunctional nylon 6 fiber and a preparation method thereof. The preparation method comprises the steps that nylon 6 serves as a rawmaterial, a spinneret plate with a similar H-shaped spinneret hole cross section is adopted for spinning, and the warm-keeping and moisture-conducting multifunctional nylon 6 fiber is prepared. The similar H shape is composed of a curve m, a curve n and a curve t, m and n are symmetrical, t is connected with m and n at the same time, the I ends of m and n are located on the same side, and the II ends of m and n are located on the same side; and the distance between the end I of m and the end I of n is 0.20-0.30 mm, and the distance between the end II of m and the end II of n is 0.35-0.50 mm. The cross section of the monofilament of the finally prepared warm-keeping moisture-conducting multifunctional nylon 6 fiber is similar to A shape, and the similar A shape is composed of a single bending curve and a curve located in the single bending curve. The process is simple, production can be achieved on the basis of an original device, the fibers can be endowed with excellent warm-keeping and moisture-conducting functions, and the method can be applied to the fields of clothing fibers, household textiles and the like.

Description

technical field [0001] The invention belongs to the technical field of textile fiber material preparation, and relates to a heat-retaining and moisture-conducting multifunctional nylon 6 fiber and a preparation method thereof. Background technique [0002] With the advancement of science and technology, the development of the world economy, and the improvement of people's living standards, a yearning for leisure, the pursuit of a comfortable and relaxed living environment is being set off, making the world's clothing is gradually evolving unconsciously, in order to adapt to people's "new, strange According to the consumption habits of ", special and comfortable", the weaving industry is also doing everything possible to design various fabrics that meet people's needs, so the development of new fiber materials has become an urgent need. In order to enhance the thermal insulation effect of clothing fabrics, the conventional practice in the market is to add layers and thicken t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D01D5/253D01F6/60D01F1/09D01F1/10
CPCD01D5/253D01F1/09D01F1/103D01F1/106D01F6/60
Inventor 于金超潘志娟
Owner SUZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap