A Production Method for Improving the Uniformity of Residual Stress in Full Section of F-rail

A technology of residual stress and production method, which is applied to the improvement of process efficiency, furnace type, furnace, etc., can solve the problems of large residual stress and poor uniformity of residual stress distribution in the whole section, and achieve simple production method, easy popularization and application, and highly operable effect

Active Publication Date: 2022-02-01
武汉钢铁有限公司
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to overcome the problems of poor distribution of residual stress and excessive residual stress in the current F-shaped rail, and provide a production method that can effectively improve the uniformity of residual stress in the entire cross-section of the F-shaped rail. Control the cooling intensity and temperature difference at each position of the F-rail section after rolling, so that the distribution of residual stress on the entire section of the F-rail is more uniform and the performance is improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A Production Method for Improving the Uniformity of Residual Stress in Full Section of F-rail
  • A Production Method for Improving the Uniformity of Residual Stress in Full Section of F-rail
  • A Production Method for Improving the Uniformity of Residual Stress in Full Section of F-rail

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] The chemical composition of F-rail is: C: 0.07%, Si: 0.26%, Mn: 0.90%, Cr: 0.10%, Nb: 0.05%, P: 0.016%, S: 0.008%, and the rest are Fe and impurities element. The production method is as follows: according to the conventional section steel smelting and casting methods, the process includes converter smelting, LF refining, vacuum treatment and continuous casting. Among them, molten iron desulfurization adopts magnesium powder desulfurization process, converter smelting adopts top-bottom combined blowing process, LF refining slag alkalinity is controlled at 1.8-2.3, RH vacuum treatment time is not less than 15 minutes, tundish temperature in continuous casting process It is controlled at 15-20°C above the liquidus line, and the casting speed is 0.6-1.0m / min. The continuous casting process should be carried out under full protection to prevent contact with air. At the same time, the cast billets should be naturally stacked and cooled to room temperature. A walking beam h...

Embodiment 2

[0041] The chemical composition of F-rail is: C: 0.09%, Si: 0.27%, Mn: 1.15%, Cr: 0.13%, Nb: 0.02%, P: 0.011%, S: 0.010%, and the rest are Fe and impurities element. The production method is carried out according to the method of Example 1, the difference is that the rolling process and post-rolling accelerated cooling process parameters are as shown in Table 1.

Embodiment 3

[0043] The chemical composition of F-rail is: C: 0.05%, Si: 0.22%, Mn: 0.85%, Cr: 0.09%, Nb: 0.03%, P: 0.013%, S: 0.009%, and the rest are Fe and impurities element. The production method is carried out according to the method of Example 1, the difference is that the rolling process and post-rolling accelerated cooling process parameters are as shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a production method for improving the uniformity of residual stress in the full section of an F-shaped rail, comprising: dividing the F-shaped rail into three cooling areas according to different positions of the section, and adopting Cooling at different cooling rates. Among them, the starting cooling temperature is controlled at 520-600°C, the cooling rate of the first cooling zone is 0.2-0.7°C / s; the cooling rate of the second cooling zone is 0.8-1.3°C / s; the cooling rate of the third cooling zone is 1.4-2.0°C / s, when the surface temperature of the first cooling zone drops to 60-100°C, stop the accelerated cooling, and carry out straightening and finishing. The method provided by the invention reduces the temperature difference across the entire section of the F-rail by reasonably controlling the cooling intensity at each position of the F-shaped rail section after rolling, and the absolute value of the residual stress fluctuation of the entire section is controlled within 100 MPa.

Description

technical field [0001] The invention relates to a treatment method in the production process of steel rails, in particular to a production method for improving the uniformity of residual stress on the full section of an F-shaped rail, and belongs to the field of metal material production and application. Background technique [0002] Medium and low-speed maglev trains are an important direction for the development of urban rail transit at present. They have many characteristics such as fast speed, safety, energy saving, and environmental protection. my country has built and operated two medium- and low-speed maglev lines. With the rapid development of urban transportation in my country, the development of maglev railways Showing a momentum of leaps and bounds. [0003] F-rails are used to manufacture tracks and magnetic poles of maglev railways, to support and guide trains, and their product performance has an important impact on the stability and safety of trains. The shape...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C21D9/04C22C38/02C22C38/04C22C38/26B21B37/74
CPCC21D9/04C22C38/02C22C38/04C22C38/26B21B37/74C21D2211/005C21D2211/009Y02P10/20
Inventor 费俊杰朱敏周剑华叶佳林王俊郑建国王瑞敏赵国知
Owner 武汉钢铁有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com