High-strength die-casting alloy material for mobile phone middle plate and preparation method and application of high-strength die-casting alloy material

A technology of die-casting alloys and alloy materials, applied in the field of aluminum alloy high-pressure casting, which can solve the problems of increased wiring density, pad pitch, diameter reduction, size reduction, etc., to achieve high density, improve mechanical properties, and reduce pore content Effect

Active Publication Date: 2020-08-25
苏州慧金新材料科技有限公司
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The amount of devices on the main board of 5G mobile phones will increase significantly, and the integration level will be greatly improved in a limited space. Increased linear density

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength die-casting alloy material for mobile phone middle plate and preparation method and application of high-strength die-casting alloy material
  • High-strength die-casting alloy material for mobile phone middle plate and preparation method and application of high-strength die-casting alloy material
  • High-strength die-casting alloy material for mobile phone middle plate and preparation method and application of high-strength die-casting alloy material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-9

[0045] A high-strength die-casting alloy material for a mobile phone mid-plate, comprising the following components in mass percentage, and the balance being aluminum and unavoidable impurities.

[0046] Si: 4.0wt%-8.0wt%; Mg: 4.0wt%-8.0wt%; Mn: 0.4wt%-1.0wt%; Cu<4.0wt%; Zn<1.5wt%; Fe<0.5wt%; Ti< 0.25wt%; Sc<1.0wt%; Zr<0.5wt%, the sum of weight percentages of other impurities is controlled below 1.0wt%, and the balance is Al.

[0047] Table 1 is the content table of each element in the aluminum alloy of Examples 1-9 and the performance table of the middle plate of the mobile phone made therefrom

[0048]

[0049] The aluminum alloy materials described in the above embodiments are made into aluminum alloy ingots according to the following methods, and then made into the middle plate of the mobile phone. The process is as follows:

[0050] 1) Put the high-purity aluminum element into the heating furnace, heat it to 680°C, completely melt and keep it for 20 minutes;

[0051]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-strength die-casting alloy material for a mobile phone middle plate and a preparation method and application of the alloy material. The alloy material comprises, by weight, 4.0%-8.0% of Si, 4. %-8.0% of Mg, 0.4%-1.0% of Mn, 4.0% of Cu, 1.5% of Zn, 0.5% of Fe, 0.25% of Ti, 1.0% of Sc, 0.5% of Zr, and the balance of Al, wherein the sum of the weight percentages of other impurities is controlled to be less than 1.0 %. Compared with the prior art, the high-strength die-casting alloy material and the preparation method thereof have the advantages that the tensile strength of the obtained mobile phone middle plate can reach 350-400 MPa, the yield strength can reach 250-300 MPa, and the elongation is 2.0%-4.0%.

Description

technical field [0001] The invention belongs to the technical field of aluminum alloy high-pressure casting, and relates to a high-strength die-casting alloy material, in particular to a preparation method and application of a high-strength die-casting alloy material for a mobile phone middle plate. Background technique [0002] At present, it is the period of rapid development of the 5G industry. With the development of 5G technology and the improvement of the supporting industrial chain, 5G mobile phones will become the mainstream of the future mobile phone market. The entire industry is optimistic about the wave of phone replacements brought about by 5G. The appearance of mobile phones has also changed from plastic casings to metal mobile phone casings 10 years ago, and then to non-metallic mobile phone casings. As a key component of the mobile phone, the middle board of the mobile phone must also keep pace with the times, and the materials used are the most important. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/00C22C1/03B22D17/00
CPCC22C21/00C22C1/03C22C1/026B22D17/00
Inventor 周银鹏汪时宜陈曦胡安罗云斌赵华屈雪莲陈煜
Owner 苏州慧金新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com