High-toughness resin optical filter and preparation method thereof

An optical filter, high toughness technology, applied in optical filters, nonlinear optics, optics, etc., can solve the problems of not meeting the requirements of use, easy to produce scratches, poor surface strength, etc., to achieve good strength and toughness, light transmission. Good quality and uniform particle distribution

Inactive Publication Date: 2020-08-07
苏州京浜光电科技股份有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the existing optical filters, blue glass is generally used as the optical element, which can filter out infrared rays, but its own toughness is poor, and the thickness will be between 2-5mm. For some high-demand products, this thickness is still insufficient. Larger, does not meet the requirements of use, and the surface strength is poor, prone to scratches, therefore, a high-toughness resin filter and its preparation method are needed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-toughness resin optical filter and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A high-toughness resin filter, comprising a substrate 2, a modified dispersion resin layer 3 is provided on the outside of the substrate 2, a repair coating 4 is coated on the outside of the modified dispersion resin layer 3, and a repair coating 4 is provided on the inside of the substrate 2. There is coating layer 1.

[0026] Wherein, the modified dispersion resin layer 3 includes 13 parts of methacrylate, 3 parts of methyl methacrylate, 4 parts of butyl methacrylate, 13 parts of benzyl methacrylate, 6 parts of phenethyl ester, propylene glycol methyl 5 parts of ether acetate, the modified dispersion resin layer 3 is mixed with an infrared adsorption layer, and the infrared adsorption layer is o-phthalimine nickel fuel, sulfide double tin nickel fuel and dichloromethane, and the mixing ratio 2.5:1.5:4, the repair coating 4 includes 5 parts of methyltriethoxysilane, 4 parts of ethyl orthosilicate, 4 parts of methanol, 5 parts of ethanol, 5 parts of 1,2-dipropanol and ...

Embodiment 2

[0036] A high-toughness resin filter, comprising a substrate 2, a modified dispersion resin layer 3 is provided on the outside of the substrate 2, a repair coating 4 is coated on the outside of the modified dispersion resin layer 3, and a repair coating 4 is provided on the inside of the substrate 2. There is coating layer 1.

[0037] Wherein, the modified dispersion resin layer 3 includes 12 parts of methacrylate, 1 part of methyl methacrylate, 2 parts of butyl methacrylate, 10 parts of benzyl methacrylate, 4 parts of phenethyl ester, propylene glycol methyl 3 parts of ether acetate, and the modified dispersion resin layer 3 is mixed with an infrared adsorption layer, and the infrared adsorption layer is phthalimine nickel fuel, sulfide double tin nickel fuel and dichloromethane, and the mixing ratio is 2:1:3, the repair coating 4 includes 3 parts of methyltriethoxysilane, 2 parts of ethyl orthosilicate, 2 parts of methanol, 3 parts of ethanol, 1 part of 1,2-dipropanol and 2...

Embodiment 3

[0047]A high-toughness resin filter, comprising a substrate 2, a modified dispersion resin layer 3 is provided on the outside of the substrate 2, a repair coating 4 is coated on the outside of the modified dispersion resin layer 3, and a repair coating 4 is provided on the inside of the substrate 2. There is coating layer 1.

[0048] Wherein, the modified dispersion resin layer 3 includes 16 parts of methacrylate, 4 parts of methyl methacrylate, 5 parts of butyl methacrylate, 15 parts of benzyl methacrylate, 8 parts of phenethyl ester, propylene glycol methyl 6 parts of ether acetate, the modified dispersion resin layer 3 is mixed with an infrared adsorption layer, and the infrared adsorption layer is phthalimine nickel fuel, disulfide-nickel fuel and dichloromethane, and the mixing ratio is 3:2:5, the repair coating 4 includes 6 parts of methyltriethoxysilane, 5 parts of ethyl orthosilicate, 5 parts of methanol, 6 parts of ethanol, 8 parts of 1,2-dipropanol and 9 parts of or...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-toughness resin optical filter and a preparation method thereof. The optical filter comprises a substrate, and a modified dispersion resin layer is arranged on the outerside of the base plate; a restoration coating is disposed outside the modified dispersion resin layer; and a coating layer is disposed inside the substrate. According to the present invention, the preparation method is simple, and the prepared optical filter has characteristics of good light transmittance, high infrared ray absorption degree, good strength, good toughness, uniform particle distribution, wear resistance, scratch resistance and corrosion resistance, and can be popularized.

Description

technical field [0001] The invention relates to the technical field of optical filter preparation, in particular to a high-toughness resin optical filter and a preparation method thereof. Background technique [0002] With the development of Thin Film Transistor Liquid Crystal Display (TFT-LCD) technology, its cost has been reduced and its manufacturing process has been further improved, making it a mainstream technology in the field of flat panel display. In the existing optical filters, blue glass is generally used as the optical element, which can filter out infrared rays, but its own toughness is poor, and the thickness will be between 2-5mm. For some high-demand products, this thickness is still insufficient. Larger, does not meet the use requirements, and the surface strength is poor, easy to produce scratches, therefore, a high toughness resin filter and its preparation method are needed. Contents of the invention [0003] The purpose of the present invention is to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G02B5/20G02B5/22G02F1/1335C03C17/42C03C17/38C03C17/28C09D133/10C09D5/32C09D183/04B05D1/36B05D7/24B05D5/06
CPCB05D5/061B05D7/24B05D7/58B05D2203/35C03C17/006C03C17/009C03C17/28C03C17/36C03C17/3605C03C17/3621C03C17/3649C03C17/3657C03C17/38C03C17/42C03C2217/40C03C2218/11C03C2218/151C03C2218/152C03C2218/365C09D4/00C09D5/32C09D133/10C09D183/04G02B5/208G02B5/223G02F1/133514G02F1/133516
Inventor 贺力伟
Owner 苏州京浜光电科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com