Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

E2 vertical roller forging forming technology

A technology of forging forming and craftsmanship, which is applied in the field of forging forming technology of E2 vertical rolls, which can solve the problems that the quality of E2 vertical rolls is difficult to meet the standard.

Active Publication Date: 2020-08-07
PANGANG GROUP JIANGYOU CHANGCHENG SPECIAL STEEL
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of this, the object of the present invention is to provide a forging forming process of the E2 vertical roll, which can effectively solve the problem that the quality of the E2 vertical roll is difficult to reach the standard

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • E2 vertical roller forging forming technology

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] The E2 vertical roller is produced by the above process, and its specification is: φ1360×720×2875mm. The specific forging process is as follows:

[0049] S11: Steel ingot heating, the heating temperature range is 1210-1230°C.

[0050] S12: out of the furnace, the whole ingot upsetting H≤1200mm, FM method drawing length to 1200mm 2 , return to the furnace for homogenization, the homogenization temperature is 1220°C, the time is 10h, and a billet with one upsetting and one pulling out is obtained;

[0051] S12: Out of the furnace, upsetting H≤1100mm, FM method to lengthen to 1400mm 2 , and then pull out the flat anvil to grow to 1200mm 2 , return to the furnace for homogenization, the homogenization temperature is 1200°C, and the time is 2 to 4 hours to obtain a two-upsetting and two-drawing billet;

[0052] S13: out of the furnace, upsetting H≤1100mm, FM method drawing length to 1400mm 2 , and then pull out the flat anvil to grow to 1200mm 2 , return to the furnace f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an E2 vertical roller forging forming technology. The E2 vertical roller forging forming technology comprises the steps that steel ingot heating is conducted, and the heating temperature range is 1,210 DEG C-1,230 DEG C; integral steel ingot upsetting is conducted, a steel ingot is subjected to upsetting to 1 / 3-1 / 2 of the height of the steel ingot, and after upsetting, first-time drawing is conducted, and then, the steel ingot returns to a furnace for homogenizing; after furnace discharging, upsetting is conducted again, upsetting is conducted to 1 / 3-1 / 2 of the heightof a first-upsetting and first-drawing blank, and after upsetting, drawing is conducted again, and then, the steel ingot returns to the furnace for homogenizing; after furnace discharging, third-timeupsetting is conducted, upsetting is conducted to 1 / 3-1 / 2 of the height of a second-upsetting and second-drawing blank, and after upsetting, third-time drawing is conducted, a blank with the height-diameter ratio being 2.2-2.4 is obtained, and then the blank returns to the furnace for homogenizing; rounding embossing blank manufacturing is conducted; die forging forming is conducted; and heat treatment after forging is conducted. By adoption of the forging forming technology, the three-upsetting and three-drawing production manner is adopted, crushing of a steel ingot cast-state structure canbe sufficiently guaranteed, and in combination with deformation and reversion and recrystallization effects, grains are sufficiently refined; and through forging production, the quality of a preparedE2 vertical roller is good, and volume production and quality requirements can be met.

Description

technical field [0001] The invention relates to the technical field of forging, and more specifically, relates to a forging forming process of an E2 vertical roll. Background technique [0002] The E2 vertical roll mill can roll the two vertical sides of the slab in the hot strip rolling mill to reduce and ensure the width and precision of the strip steel; it can align the slab to the rolling center line and lift the guide plate Billet function; when rolling a slab with a thickness greater than 100mm, the 300mm-wide oxide scale at the edge of the slab can be loosened, and then the high-pressure water descaling effect is good. [0003] E2 vertical rolls usually have complex shapes and require high product quality. There must be no defects such as cracks, pores, slag inclusions, sand holes, porosity, etc. that affect the use. The flaw detection requirements meet the requirements of level 3 of the GB / T6402-2008 flaw detection method, and the rolling volume per millimeter is ≥ ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B21J5/00B21J5/02B21J5/06B21J5/08B21K1/02
CPCB21J5/002B21J5/02B21J5/06B21J5/08B21K1/02
Inventor 师宇韩涛陈炜陈孝平余多贤代永斌王川东文泽龙于瑞芝
Owner PANGANG GROUP JIANGYOU CHANGCHENG SPECIAL STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com