Hydrocolloid antibacterial dressing and preparation method thereof

A hydrocolloid and liquid technology, applied in medical science, bandages, etc., to achieve the effect of protecting skin safety, protecting and repairing damaged skin, and enriching the use properties

Active Publication Date: 2020-06-26
WENZHOU MEDICAL UNIV
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are many types of hydrocolloid dressings available, and each type of hydrocolloid dressing has its own advantages and disadvantages, but no one product has obvious advantages in preventing facial pressure ulcers caused by medical personnel wearing masks and goggles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydrocolloid antibacterial dressing and preparation method thereof
  • Hydrocolloid antibacterial dressing and preparation method thereof
  • Hydrocolloid antibacterial dressing and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A hydrocolloid antibacterial dressing, comprising the following components in terms of mass percentages: 0.5% small molecule silk peptide, 0.8% fish scale collagen, 3% chitosan, 2% propylene glycol, 3% glycerin, 30% polyethylene glycol, The balance is purified water.

[0030] The preparation method of described hydrocolloid antibacterial dressing, comprises the steps:

[0031] (1) Weigh each raw material component by weight, mix polyethylene glycol and purified water, heat to 90°C, stir to dissolve and cool to 40°C, then add small molecule silk peptide, fish scale collagen, chitosan in sequence , propylene glycol and glycerin, after stirring and dissolving, hydrocolloid liquid is obtained;

[0032] (2) Vacuumize and defoam the hydrocolloid liquid in step (1), then pour it into a forming mold, and immediately place it at -10°C for 10 hours to freeze to obtain a freeze-formed hydrocolloid film;

[0033] (3) Vacuum-seal the hydrocolloid film freeze-formed in step (2), th...

Embodiment 2

[0035] A hydrocolloid antibacterial dressing, comprising the following components in terms of mass percentages: 1.0% small molecule silk peptide, 0.2% fish scale collagen, 6% chitosan, 5% sodium hyaluronate, 20% polyvinyl alcohol, and the balance for purified water.

[0036]The preparation method of described hydrocolloid antibacterial dressing, comprises the steps:

[0037] (1) Weigh each raw material component by weight, mix polyvinyl alcohol and purified water, heat to 95°C, stir to dissolve and cool to 42°C, then add small molecule silk peptide, fish scale collagen, chitosan and Sodium hyaluronate, after stirring and dissolving, hydrocolloid liquid is obtained;

[0038] (2) Vacuumize and defoam the hydrocolloid liquid in step (1), then pour it into a forming mold, and immediately place it at -15°C for 6 hours to freeze to obtain a freeze-formed hydrocolloid film;

[0039] (3) Vacuum-seal the hydrocolloid film freeze-formed in step (2), thaw it at room temperature and ste...

Embodiment 3

[0041] A hydrocolloid antibacterial dressing, comprising the following components in terms of mass percentages: 0.8% small molecule silk peptide, 0.5% fish scale collagen, 4% chitosan, 3% allantoin, 10% polyvinylpyrrolidone, carboxymethyl Sodium cellulose 15%, the balance is purified water.

[0042] The preparation method of described hydrocolloid antibacterial dressing, comprises the steps:

[0043] (1) Weigh each raw material component by weight ratio, mix polyvinylpyrrolidone, sodium carboxymethylcellulose and purified water, heat to 92°C, stir to dissolve and cool to 45°C, then add small molecule silk peptide, Fish scale collagen, chitosan and allantoin, stirred and dissolved to obtain hydrocolloid liquid;

[0044] (2) Vacuumize and defoam the hydrocolloid liquid in step (1), then pour it into a forming mold, and immediately place it at -12°C for 8 hours to freeze to obtain a freeze-formed hydrocolloid film;

[0045] (3) Vacuum-seal the hydrocolloid film freeze-formed in...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of medical dressings, and specifically relates to a hydrocolloid antibacterial dressing and a preparation method thereof. The dressing contains small-molecule silk peptide, fish scale collagen, chitosan, moisturizing materials, skeleton materials, purified water and other components. The hydrocolloid antibacterial dressing of the present invention has the functions of sweat absorption, antibacterial and moisturizing properties, and the like, and conforms to various humanized designs, can prevent related damage caused by frontal facial instrumental pressure, and effectively protect the skin safety of medical personnel. Combined with the use of moisturizing and antibacterial active ingredients, the dressing can further enrich the use properties of hydrocolloid dressings and protect and repair damaged skin in all directions.

Description

technical field [0001] The invention belongs to the field of medical dressings, in particular to a hydrocolloid antibacterial dressing and a preparation method thereof. Background technique [0002] During the epidemic, for effective protection, the general population needs to wear masks when going out. In some special positions, such as medical staff, epidemic prevention staff, workshop workers, etc., who need to wear masks and goggles and other preventive medical devices for a long time, the skin is in a state of oppression and airtightness for a long time, and some symptoms may occur. A series of problems, such as: (1) indentation: due to wearing a mask for a long time, the pressure is too high, the blood circulation is not smooth, and deep marks will appear on the pressured part, which will not disappear for a long time; (2) skin infection: due to Wearing a mask and goggles for a long time will cause displacement due to incomplete coordination with the face, resulting i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61L26/00
CPCA61L26/0023A61L26/0033A61L26/0047A61L26/0061A61L26/0066A61L26/008A61L2300/232A61L2300/404C08L89/00C08L5/08
Inventor 肖健张宏宇许可王梦莹曹慧鑫李校堃
Owner WENZHOU MEDICAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com