A kind of heat-resistant antique iron stoneware and preparation method

An iron-based, heat-resistant technology, used in the production of clay products, ceramic materials, and other household appliances, can solve problems such as increasing production costs and losing ceramic properties, improving thermal shock resistance, reducing expansion coefficient, increasing The effect of mechanical strength

Active Publication Date: 2022-04-26
HUNAN HUALIAN CHINA IND
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above-mentioned ceramics basically belong to the category of porcelain, and the glaze will be applied to the green body. Although the thermal stability is improved, it will lose the characteristics of the pottery itself and increase the production cost.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of heat-resistant antique iron stoneware and preparation method
  • A kind of heat-resistant antique iron stoneware and preparation method
  • A kind of heat-resistant antique iron stoneware and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Components and content in the formula of the present invention are:

[0032]

[0033] Accurately formulate the weight of each raw material in the above formula, make mud sticks, form green bodies, or carve patterns on the green bodies according to the mud making method above. Or add color patterns, put them in a kiln and burn them with reduced flames. During the firing cycle in a reducing atmosphere, the carbon monoxide gas content (volume fraction) is kept at 3% to 4%; the flame transfer temperature is 950°C to ensure that the porcelain body becomes iron-like black brown; the high fire holding temperature is 1270°C to 1290°C °C, the holding time is 10 minutes; the annealing holding temperature is 1020 °C, and the holding time is 45 minutes. The volume expansion coefficient is 100.5×10 -7 / °C. The water absorption test and thermal stability test of the obtained antique irony black brown cooking stoneware products are as follows:

[0034] Water absorption test:

...

Embodiment 2

[0039]Components and content in the formula of the present invention are:

[0040]

[0041]

[0042] Accurately formulate the weight of each raw material in the above formula, make mud sticks, form green bodies, or carve patterns on the green bodies according to the mud making method above. Or add color patterns, put them in a kiln and burn them with reduced flames. During the firing cycle in a reducing atmosphere, the carbon monoxide gas content (volume fraction) is kept at 3% to 4%; the flame transfer temperature is 950°C to ensure that the porcelain body becomes iron-like black brown; the high fire holding temperature is 1270°C to 1290°C °C, the holding time is 10 minutes; the annealing holding temperature is 1020 °C, and the holding time is 45 minutes. The volume expansion coefficient is 94.6×10 -7 / °C. The water absorption test and thermal stability test of the obtained antique irony black brown cooking stoneware products are as follows:

[0043] Water absorptio...

Embodiment 3

[0048] Components and content in the formula of the present invention are:

[0049]

[0050] Accurately formulate the weight of each raw material in the above formula, make mud sticks, form green bodies, or carve patterns on the green bodies according to the mud making method above. Or add color patterns, put them in a kiln and burn them with reduced flames. During the firing cycle in a reducing atmosphere, the carbon monoxide gas content (volume fraction) is kept at 3% to 4%; the flame transfer temperature is 950°C to ensure that the porcelain body becomes iron-like black brown; the high fire holding temperature is 1270°C to 1290°C °C, the holding time is 10 minutes; the annealing holding temperature is 1020 °C, and the holding time is 45 minutes. The volume expansion coefficient is 91.8×10 -7 / °C. The water absorption test and thermal stability test of the obtained antique irony black brown cooking stoneware products are as follows:

[0051] Water absorption test:

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to View More

Abstract

The invention relates to a heat-resistant antique iron stone pottery and a preparation method thereof. The raw materials include the following components in parts by weight: calcined kaolin, washed kaolin, porcelain clay, iron slag, feldspar and mullite; the heat-resistant In the antique iron stoneware, the weight content of silicon dioxide is 54-56%, the weight content of aluminum oxide is 34-36%, the weight content of ferric oxide is 5.0-6.0%; the density is 1.8-2.1g / cm 3 , the water absorption rate is below 3%, and the volume expansion coefficient is 90~105×10 ‑7 / °C, and the heat stability is 200°C repeated three times; the present invention has low production cost, low expansion coefficient, good heat stability, and better retains the simple and rough aesthetic feeling of the rough pottery itself.

Description

technical field [0001] The invention belongs to the technical field of antique iron coarse pottery for cooking, and in particular relates to a heat-resistant antique iron coarse pottery and a preparation method. Background technique [0002] At present, the daily cooking ceramics produced in our country are mainly heat-resistant porcelain that can be cooked on fire in Chaozhou, Fujian, Jiangxi and other places, as well as Yixing purple sand ceramics in Jiangsu and new types of feldspar porcelain developed in Shahu Lake in recent years. It is mainly used for daily-use ceramics for cooking in electric hot pots. The volume expansion coefficient of heat-resistant porcelain in Chaozhou, Fujian, Jiangxi and other places is generally 0 to 30×10 -7 / ℃, so it has good thermal shock resistance and can be cooked directly on the fire. However, because of the large amount of imported spodumene and petalite feldspar as the main formula materials, its cost is quite high, and its product...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/13C04B33/132C04B33/138
CPCC04B33/131C04B33/1321C04B33/138C04B33/1324C04B2235/3463C04B2235/3418C04B2235/3217C04B2235/3272C04B2235/3232C04B2235/3201C04B2235/3208C04B2235/3206C04B2235/77C04B2235/96Y02P40/60
Inventor 麦潮棠汪大谷叶守明陈芳
Owner HUNAN HUALIAN CHINA IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com