Silane modified polyether sealant and preparation method thereof

A silane-modified polyether and sealant technology, which is applied in the direction of polyether adhesives, adhesives, carboxyl rubber adhesives, etc., can solve the problems of large proportion of resin, high cost, and difficulty in ensuring long-term performance

Inactive Publication Date: 2020-05-05
HUNAN KOSEN NEW MATERIAL
View PDF2 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It is difficult for the existing MS sealant to ensure good fluidity, elastic recovery rate and other indicators under high filler content. The filler content is usually controlled in the range of 40-45%, the proportion of resin is large, the cost is high, and it is difficult to guarantee long-term performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Silane modified polyether sealant and preparation method thereof
  • Silane modified polyether sealant and preparation method thereof
  • Silane modified polyether sealant and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0026] The preparation steps of described hyperbranched fluorine-containing polyester are as follows:

[0027] Add hyperbranched carboxyl polyester and 2-perfluorooctyl ethanol to the reaction kettle so that the number of moles of carboxyl groups is twice the number of moles of hydroxyl groups, add p-toluenesulfonic acid dropwise under a nitrogen atmosphere, and reflux at 105°C until the acid value of the system is basically Stable, obtain hyperbranched fluorine-containing polyester, viscosity at 25°C <4000mPa.s.

[0028] The sealant formula of embodiments 1 to 4 is shown in Table 1, and the sealant is prepared in the following way:

[0029] (1) Take each component by weight, add hyperbranched fluorine-containing polyester, MS resin, ultrafine fully vulcanized carboxylated styrene-butadiene rubber, plasticizer, and antioxidant into a stainless steel mixing device with a planetary mixer. It has the functions of stirring, temperature adjustment, vacuuming, feeding and dischargi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses a silane modified polyether sealant and a preparation method thereof. The silane modified polyether sealant comprises the following components (by weight): 12-20% of MS resin,1-4% of hyperbranched fluorine-containing polyester, 1-3% of superfine full-vulcanized carboxylic butadiene styrene rubber, 60-70% of a filler, 2-5% of a thixotropic agent, 1-3% of a dehydrating agent, 0.03-0.08% of a catalyst, 9-20% of a plasticizer, 0.10-0.40% of an ultraviolet light absorber, 0-3% of a coloring agent, 0.5-1.0% of a coupling agent, 0.04-0.1% of an antioxidant and 0.4-1.0% of a flame retardant. By matching the above components, the content of the filler is increased, and good comprehensive properties such as flowability, aging resistance and stain resistance are guaranteed.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a silane-modified polyether sealant and a preparation method thereof. Background technique [0002] Silane-modified polyether resin, also known as MS resin, is an alkoxysilane-terminated polyether resin. Under the action of a catalyst and water, it will undergo hydrolysis, cross-linking and curing to form a macromolecular elastomer. Molecular elastomer has low modulus, high elastic recovery rate, good adhesion, good water resistance and aging resistance, and can be used as a mixture with plasticizers, fillers, colorants, catalysts, anti-aging agents, and flame retardants. It can be used to seal the gaps between the inner and outer walls of traditional buildings, or the sealing of vehicles, mechanical equipment, doors and windows, glass curtain walls, etc., which is called MS sealant in the industry. It is difficult for the existing MS sealant to ensure good fluidity, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J171/00C09J167/00C09J113/00C09J11/04C09J11/06C09J11/08
CPCC08K2003/026C08K2201/014C08L2201/08C08L2205/025C08L2205/03C08L2205/035C09J11/04C09J11/06C09J11/08C09J171/00C08L67/00C08L13/00C08K13/06C08K5/12C08K3/36C08K3/34C08K7/26C08K9/10C08K3/02
Inventor 郑保昌王理尧钟雪琴欧阳光华石亮
Owner HUNAN KOSEN NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com