Polyurethane composition for wood-like spraying all-water foaming system as well as preparation method and equipment

A technology of all-water foaming and polyurethane, which is applied in polyurea/polyurethane coatings, coatings, chemical/physical/physicochemical fixed reactors, etc., and can solve problems that cannot meet market demand, coating texture is not clear, and spraying performance Poor and other problems, to achieve the effect of large-scale popularization and application, little change in production process, and solution to foam brittleness

Inactive Publication Date: 2020-04-03
清远市蓝林新材料有限公司
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Aiming at the deficiencies of the prior art, the present invention provides a polyurethane composition, preparation method and equipment for imitation wood spraying all-water foaming system, focusing on synchronous improvement of the polyurethane composition, preparation method and equipment to solve the current Some polyurethane spraying materials have problems such as high component cost, poor comprehensive performance, poor spraying performance, unclear texture formed by the coating, high production cost, and cannot meet market demand.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyurethane composition for wood-like spraying all-water foaming system as well as preparation method and equipment
  • Polyurethane composition for wood-like spraying all-water foaming system as well as preparation method and equipment
  • Polyurethane composition for wood-like spraying all-water foaming system as well as preparation method and equipment

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] see Figure 1-3 , the polyurethane composition that the present invention is used for imitation wood spraying all-water foaming system, polyurethane composition is prepared by the component of following parts by weight:

[0038] Polyether: 85 parts; Polyester: 15 parts; Crosslinking agent: 3-5 parts; Catalyst: 1-5 parts; Foam stabilizer: 2-5 parts; Water: 1-1.5 parts.

[0039] The present invention also provides the above-mentioned preparation method for the polyurethane composition of imitation wood spraying all-water foaming system, comprises the following steps:

[0040] S1. Raw material configuration: according to the set weight ratio, polyether and polyester are placed in the equipment for configuration;

[0041] S2. Heat exchange and grinding: Pump the prepared slurry to the grinding equipment for grinding. During the slurry pumping process, heat exchange is performed through the heat exchange equipment, and the viscosity is reduced by increasing the temperature ...

Embodiment 2

[0060] The polyurethane composition, preparation method and equipment for wood-like spraying all-water foaming system provided in this embodiment are basically the same as in Example 1, except that:

[0061] In this embodiment, the polyurethane composition used for imitation wood spraying all-water foaming system is specifically prepared from the following components by weight:

[0062] Polyether: 60 parts; polyester: 15 parts; crosslinking agent: 3-5 parts; catalyst: 3-5 parts; foam regulator: 5-7 parts; water: 5-10 parts.

Embodiment 3

[0064] The polyurethane composition, preparation method and equipment for imitation wood spraying all-water foaming system provided by this embodiment are basically the same as embodiment 1 and embodiment 2, and its difference is:

[0065] Polyether: 60 parts; Polyester: 15 parts; Crosslinking agent: 1-3 parts; Catalyst: 2-4 parts; Foam stabilizer: 3-6 parts; Water: 4-8 parts.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a polyurethane composition for a wood-like spraying all-water foaming system. The polyurethane composition is prepared from the following components in parts by weight: 85 parts of polyether; 15 parts of polyester; 3-5 parts of a cross-linking agent; 1 to 5 parts of a catalyst; 2-5 parts of a foam stabilizer; and 1-1.5 parts of water. The preparation method of the polyurethane composition comprises the following steps: S1, raw material preparation; S2, heat exchange and grinding; and S3, dehydration, stirring and reaction; and S4, metering, filling and detecting. The invention also provides preparation equipment of the polyurethane composition for the wood-like spraying all-water foaming system. According to the invention, the polyurethane composition, the preparation method and the equipment are synchronously improved, so that the component cost of the polyurethane composition spraying material is reduced, the comprehensive performance is improved, the sprayingperformance is good, the texture formed by a coating layer is clear, the production cost is reduced, the market demand can be met, and the large-scale popularization and application are facilitated.

Description

technical field [0001] The invention relates to the technical field of polymer polyurethane coating manufacturing, in particular to a polyurethane composition, preparation method and equipment for wood-like spraying all-water foaming system. Background technique [0002] With the development of material technology, less and less solid wood materials are used, and other materials are used instead of wood. These materials require surface spraying operations. For example, imitation wood railings, doors and windows, furniture and other products made of concrete materials, metal materials, wood-plastic composite materials, etc., have specific requirements for spraying materials and processes. During the painting process, attention should be paid to the uniformity and smoothness of the imitation wood strips on the surface, so that the paint surface is uniform and the brightness is uniform. The surface of the parts should not be wrong, the coating should not be leaked, the coatin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G18/48C08G18/42C09D175/06C09D175/08B01J19/18C08G101/00
CPCB01J19/18C08G18/4018C08G18/42C08G18/48C09D175/06C09D175/08C08G2110/0083
Inventor 曾庆刚
Owner 清远市蓝林新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products