Aluminum foil mylar adhesive tape and preparation method thereof

A technology of aluminum foil Mylar and tape, applied in the direction of adhesives, adhesive types, film/sheet adhesives, etc., can solve the problems of separation of aluminum foil and polyester tape, denaturation of aluminum foil Mylar tape, loss of use effect, etc. , to achieve the effect of improving bonding stability, improving performance and prolonging service life

Inactive Publication Date: 2020-02-21
昆山恒永昌电子科技有限公司
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the existing aluminum foil Mylar tape is prone to denaturation of the aluminum foil Mylar tape itself due to changes in temperature, humidity, etc. during use due to its production process and irregular materials, or due to excessive stretching. The fracture phenomenon caused by it, thus losing its use effect, and in the process of use, the aluminum foil and the polyester tape are prone to separation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A kind of aluminum foil Mylar tape, described aluminum foil Mylar tape comprises: polyester film layer, adhesive layer, aluminum foil layer, adhesive layer and isolation layer arranged from top to bottom, wherein, adhesive layer counts by weight parts Including: 5 parts of water-based acrylic acid and 20 parts of cross-linked polyacrylic acid. When in use, mix water-based acrylic acid and cross-linked polyacrylic acid and add them to a hot melt machine, melt them and stir them evenly. The mixing temperature is 120 °C to obtain the adhesive.

[0030] Wherein, the polyester film layer is a black PET film with a thickness of 0.08 mm and a light transmittance of ≤40%, and the isolation layer is a single-sided or double-sided silicone release paper or film.

[0031] A preparation method of aluminum foil Mylar tape, comprising the following steps:

[0032] S1. Substrate preparation: use high-purity aluminum foil as the substrate, the thickness of the aluminum foil is 0.04mm,...

Embodiment 2

[0044] A kind of aluminum foil Mylar tape, described aluminum foil Mylar tape comprises: polyester film layer, adhesive layer, aluminum foil layer, adhesive layer and isolation layer arranged from top to bottom, wherein, adhesive layer counts by weight parts Including: 10 parts of water-based acrylic acid and 15 parts of cross-linked polyacrylic acid. When in use, mix water-based acrylic acid and cross-linked polyacrylic acid and add them to a hot melt machine, melt them and stir them evenly. The mixing temperature is 135 °C to obtain the adhesive.

[0045] Wherein, the polyester film layer is a black PET film with a thickness of 0.10mm and a light transmittance of ≤40%, and the isolation layer is a single-sided or double-sided silicone release paper or film.

[0046] A preparation method of aluminum foil Mylar tape, comprising the following steps:

[0047] S1. Substrate preparation: use high-purity aluminum foil as the substrate, the thickness of the aluminum foil is 0.07mm,...

Embodiment 3

[0059] A kind of aluminum foil Mylar tape, described aluminum foil Mylar tape comprises: polyester film layer, adhesive layer, aluminum foil layer, adhesive layer and isolation layer arranged from top to bottom, wherein, adhesive layer counts by weight parts Including: 15 parts of water-based acrylic acid and 15 parts of cross-linked polyacrylic acid. When in use, mix water-based acrylic acid and cross-linked polyacrylic acid and add them to a hot melt machine, melt them and stir them evenly. The mixing temperature is 135 °C to obtain the adhesive.

[0060] Wherein, the polyester film layer is a black PET film with a thickness of 0.03 mm and a light transmittance ≤ 40%, and the isolation layer is a single-sided or double-sided silicone release paper or film.

[0061] A preparation method of aluminum foil Mylar tape, comprising the following steps:

[0062] S1. Substrate preparation: use high-purity aluminum foil as the substrate, the thickness of the aluminum foil is 0.02mm, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of aluminum foil mylar adhesive tapes, particularly to an aluminum foil mylar adhesive tape and a preparation method thereof, wherein the prepared aluminumfoil mylar adhesive tape is good in weather resistance, cannot be denatured and broken under the condition of temperature change and humidity change, can avoid the separation of an aluminum foil froma polyester tape in a use process, and comprises a polyester film layer, an adhesion layer, an aluminum foil layer, an adhesion layer and an isolation layer, wherein the polyester film layer, the adhesion layer, the aluminum foil layer, the adhesion layer and the isolation layer are arranged from top to bottom, the adhesion layer comprises 5-15 parts of aqueous acrylic acid and 15-20 parts of cross-linked polyacrylic acid, and during the use, the aqueous acrylic acid and the cross-linked polyacrylic acid are mixed and added into a hot melting machine and are melted and stirred and mixed uniformly. The preparation method comprises: S1, base material preparing; S2, adhesive preparing; S3, polyester film layer treatment; S4, coating with an adhesive solution; Ss5, drying treatment; S6, laminating treatment; S7, curing treatment; S8, irradiation cross-linking modification treatment; S9, winding; and S10, slitting.

Description

technical field [0001] The invention relates to the technical field of aluminum foil Mylar tape, in particular to an aluminum foil Mylar tape and a preparation method thereof. Background technique [0002] Aluminum foil Mylar is a new type of material that is gradually replacing traditional light-shielding materials. Aluminum foil Mylar is made of metal aluminum foil, glued on the back and polyester tape (generally PET, PP, etc.) , Mobile phones, computers, PDAs, PDPs, LED displays, notebook computers, copiers and other electronic products where electromagnetic shielding is required, which can eliminate electromagnetic interference, isolate electromagnetic waves from harming the human body, and prevent interference voltage and current from affecting product functions. [0003] Aluminum foil Mylar tape is made of aluminum foil and coated with acrylic or rubber pressure-sensitive adhesive. It adopts high-quality pressure-sensitive adhesive, which has good viscosity, strong ad...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/29C09J7/38C09J133/04
CPCC08L2205/025C09J133/04C09J2203/326C09J2400/163C09J2433/00C09J2467/006C09J7/29C09J7/385C09J2301/122C09J2301/16C09J2301/302C09J2301/416C08L33/04
Inventor 曹向阳刘庆伟刘飞曹诗阳余龙
Owner 昆山恒永昌电子科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com