A kind of glass fiber reinforced npg-pet transparent composite material and preparation method thereof

A technology of glass fiber and composite materials, applied in the field of glass fiber reinforced NPG-PET transparent composite materials and its preparation, can solve the problems of low toughness, etc., and achieve increased external area, high rigidity and surface gloss, surface roughness and appearance The effect of increasing the area

Active Publication Date: 2021-09-07
腾龙特种树脂(厦门)有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] NPG-PET is formed by esterification and polycondensation of neopentyl glycol, ethylene glycol and terephthalic acid. It is a new transparent resin with scratch resistance, aging resistance, chemical resistance and high gloss. High fluidity, but compared with CHDM-PETG, its toughness is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of glass fiber reinforced npg-pet transparent composite material and preparation method thereof
  • A kind of glass fiber reinforced npg-pet transparent composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A glass fiber reinforced NPG-PET transparent composite material. The components in the raw materials include 50 parts of NPG-PET, 50 parts of modified glass fiber, 0.9 part of antioxidant and 0.3 part of lubricant.

[0035] The above-mentioned NPG-PET is formed by esterification and polycondensation of neopentyl glycol, ethylene glycol and terephthalic acid.

[0036] Above-mentioned lubricant selects stearate for use.

[0037] The above antioxidant is selected from phenolic antioxidant 1010.

[0038] The preparation method of above-mentioned modified glass fiber comprises the following steps:

[0039] S1: Add an appropriate amount of glass fiber with a length of 3-4.5mm and a single filament diameter of 8-17μm into a 9.5mol / L phosphoric acid solution, where the mass ratio of glass fiber to phosphoric acid solution is 1:25, and stir at room temperature for 3 minutes;

[0040] S2: Filter the treated glass fiber from the phosphoric acid solution, wash it with deionized w...

Embodiment 2

[0049] A glass fiber reinforced NPG-PET transparent composite material. The components in the raw material include 60 parts of NPG-PET, 40 parts of modified glass fiber, 0.1 part of antioxidant and 0.6 part of lubricant.

[0050] The above-mentioned NPG-PET is formed by esterification and polycondensation of neopentyl glycol, ethylene glycol and terephthalic acid.

[0051] Above-mentioned lubricant selects fatty alcohol diacid ester for use.

[0052]The above-mentioned antioxidant is selected from phosphite lipid antioxidant 168.

[0053] The preparation method of above-mentioned modified glass fiber comprises the following steps:

[0054] S1: Add an appropriate amount of glass fiber with a length of 3-4.5mm and a single filament diameter of 8-17μm into a 9.5mol / L phosphoric acid solution, where the mass ratio of glass fiber to phosphoric acid solution is 1:26, and stir at room temperature for 6 minutes;

[0055] S2: Filter the treated glass fiber from the phosphoric acid so...

Embodiment 3

[0064] A glass fiber reinforced NPG-PET transparent composite material. The components in the raw material include 75 parts of NPG-PET, 30 parts of modified glass fiber, 1.8 parts of antioxidant and 0.5 part of lubricant.

[0065] The above-mentioned NPG-PET is formed by esterification and polycondensation of neopentyl glycol, ethylene glycol and terephthalic acid.

[0066] The above-mentioned lubricants are selected from stearic acid ester and fatty alcohol diacid ester, and the ratio of the two is 1:1.

[0067] The above antioxidants are selected from phenolic antioxidant 1010 and phosphite antioxidant 168, in which 1010 and 168 are 1:2.

[0068] The preparation method of above-mentioned modified glass fiber comprises the following steps:

[0069] S1: Take an appropriate amount of glass fiber with a length of 3-4.5mm and a single filament diameter of 8-17μm, add it to a 9.5mol / L phosphoric acid solution, where the mass ratio of glass fiber to phosphoric acid solution is 1:2...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of polymer materials, in particular to a glass fiber-reinforced NPG-PET transparent composite material and a preparation method thereof. The components in the raw materials are calculated in parts by weight, including 50-95 parts of NPG-PET, modified glass fiber 5-50 parts, 0.1-3 parts of antioxidant, 0.3-2 parts of lubricant; NPG-PET used in the present invention is composed of three monomer esters of neopentyl glycol (NPG), ethylene glycol and terephthalic acid Formed by chemicalization and polycondensation, it has good fluidity and high gloss. The modified glass fiber is mixed into NPG-PET, so that the obtained glass fiber reinforced NPG-PET composite material has high impact strength, heat resistance, high modulus, high rigidity and high surface gloss while remaining transparent.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a glass fiber reinforced NPG-PET transparent composite material and a preparation method thereof. Background technique [0002] Glass fiber is often used in composite materials to strengthen and toughen, improve the strength, heat insulation and other properties of composite materials. When glass fiber is applied to PETG composite material, due to the smooth surface of glass fiber, the adhesion with the base material is weak, the compatibility is poor, and it is easy to appear floating fibers and other undesirable phenomena, which is not conducive to the strengthening and toughening of PETG composite material , which greatly limits its application. [0003] PETG is a transparent resin, which is an amorphous copolyester. The comonomer commonly used in PETG is 1,4-cyclohexanedimethanol (CHDM), which is called polyethylene terephthalate-1,4- Cyclohexane dimethanol ester,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L67/02C08K13/06C08K9/06C08K9/02C08K7/14C08K5/103C08J5/08
CPCC08J5/08C08J2367/02C08J2467/02C08K5/103C08K7/14C08K9/02C08K9/06C08K13/06C08K2201/003C08K2201/004
Inventor 王惠武曾晓强梁腾辉刘虎杨立清赵铁侠黄耀智吴荣汉
Owner 腾龙特种树脂(厦门)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com