Acrylamide copolymer and its preparation method and application

A technology of acrylamide copolymer and polymerization reaction, which is applied in the direction of chemical instruments and methods, drilling compositions, etc., can solve the problems of complex oil-water relationship and poor effect, and achieve high surface/interface activity, excellent viscosification, and dissolution The effect of speed, high temperature and high salt resistance

Active Publication Date: 2021-07-02
CHINA PETROLEUM & CHEM CORP +1
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to severe water flooding of oil wells and complex oil-water relationship in the ultra-high water cut stage, traditional water plugging and profile control agents such as pre-crosslinked gel particles and clay gel polymer flocculation systems are difficult to achieve deep control and displacement under the reservoir. lead to poor on-site implementation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Acrylamide copolymer and its preparation method and application
  • Acrylamide copolymer and its preparation method and application
  • Acrylamide copolymer and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0015] According to the first aspect of the present invention, the present invention provides a method for preparing an acrylamide copolymer, the preparation method comprising: under solution polymerization conditions, in the presence of an initiator and a surfactant, acrylamide, A monomer mixture consisting of comonomers and reactive monomers is polymerized in water.

[0016] In the present invention, the structure of the comonomer is as shown in formula (1), and the structure of the active monomer is as shown in formula (2); the initiator includes initiator A and initiator B, and the The structure of initiator A is shown in formula (3), and the initiator B is biuret and / or 1,5-diaminobiuret;

[0017]

[0018] Among them, R 1 -R 3 and R 5 each independently hydrogen or C1-C4 alkyl, R 4 For C1-C4 alkylene, M is hydrogen, sodium or potassium; R 6 -R 9 Each is independently a C1-C4 alkyl group, n is an integer of 1-10, and m is an integer of 2-6.

[0019] In the presen...

Embodiment approach

[0043] According to a more specific preferred embodiment, the preparation method of the acrylamide copolymer comprises the following steps:

[0044] 1) Add acrylamide, comonomer and water into a three-necked flask (hereinafter also referred to as a polymerization bottle) to form an aqueous solution, adjust the pH of the aqueous solution to 6-10 with alkali, and blow nitrogen gas for 20-60 minutes to remove oxygen;

[0045] 2) Under the protection of nitrogen, add the surfactant, the complexing agent aqueous solution, the other auxiliary agents and the active monomer into the aqueous solution, place in a water bath at 25-40°C, stir and disperse evenly, Form stable micelles;

[0046] 3) Under the protection of nitrogen, add initiator A and initiator B to the reaction system of step 2) at a temperature of 25-40°C until the solution becomes thick, that is, the polymerization reaction starts, and the reaction is maintained for 6-8 hour; then the reaction was heated up to 60-70°C, ...

Embodiment 1

[0063] This example is used to illustrate the acrylamide copolymer of the present invention and its preparation method.

[0064] 1) Add 11.8g of acrylamide, 8.0g of 2-acrylamido-2-methylpropanesulfonic acid and 60.0g of deionized water into the polymerization bottle to dissolve the monomer to obtain an aqueous solution of the monomer mixture, which is then oxidized with hydrogen Adjust the pH to 6.0 with sodium, and blow nitrogen gas for 30 minutes;

[0065] 2) under nitrogen protection, add 0.2g sodium lauryl sulfate, 0.2g active monomer (R 5 is methyl, n=1), 0.2g urea and 1.0g EDTA-2Na aqueous solution, put the polymerization bottle in a 25°C water bath, stir and disperse to form stable micelles;

[0066] 3) Under the protection of nitrogen, add 0.01g of N,N,N',N'-tetramethylethylenediamine and 0.002g of biuret into the polymerization bottle at 25°C to initiate polymerization of the monomer mixture and react 6 hour, then warming up to 60°C to continue the polymerization re...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of oil field water injection, and discloses an acrylamide copolymer and its preparation method and application. Amide, the monomer mixture that the comonomer of structure as shown in formula (1) and the active monomer composition of structure as shown in formula (2) carry out polymerization reaction in water; Initiator includes structure as shown in formula (3) Initiator A and initiator B, initiator B is biuret and / or 1,5-diaminobiuret; Wherein, R 1 -R 3 and R 5 each selected from hydrogen or C1-C4 alkyl, R 4 Is C1-C4 alkylene, M is hydrogen, sodium or potassium; R 6 -R 9 Each is a C1-C4 alkyl group, n is an integer of 1-10, and m is an integer of 2-6. The prepared acrylamide copolymer has ultra-high molecular weight viscosity-increasing properties, excellent solubility, temperature and salt resistance, and good surface / interface activity.

Description

technical field [0001] The invention relates to the technical field of oilfield water injection, in particular to an acrylamide copolymer and its preparation method and application. Background technique [0002] In the process of oilfield water injection development, due to the existence of formation heterogeneity, the injected water will rush along the high permeability layer, resulting in an increase in the water production rate of the oil well year by year. Profile control of water injection wells and water plugging of oil wells have become important measures to stabilize and increase production in oil fields. However, with the increase of rounds of conventional plugging control systems and measures, the remaining oil saturation in the near-wellbore area has dropped significantly, and the oil increase effect has become worse. Only through deep plugging control can more effectively adjust and improve reservoir heterogeneity , so as to increase the swept volume and sweep c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F220/56C08F220/58C08F220/54C09K8/508C09K8/88
CPCC08F220/56C08F220/58C09K8/5083C09K8/882C08F220/54
Inventor 赵方园王晓春杨捷
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com