Organic fiber toughened inorganic composite artificial stone panel and preparation method thereof

An organic fiber and inorganic composite technology, applied in chemical instruments and methods, manufacturing tools, ceramic molding machines, etc., can solve the problems of high water absorption, insufficient compressive performance, poor bending strength and toughness, etc., and achieve low water absorption. , good bonding performance, good ductility effect

Inactive Publication Date: 2020-02-04
黄贺明 +1
View PDF9 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of this, the present invention provides a product with high strength, pollution resistance, high toughness, long service life, Organic Fiber Toughened Inorganic Composite Artificial Stone Panels with Aging, Economical and Rational Multilayer Composite Structures

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Organic fiber toughened inorganic composite artificial stone panel and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Such as figure 1 As shown, an organic fiber toughened inorganic composite artificial stone panel has an overall thickness (t1+t2+t3) of 15-50 mm, including a surface layer with a thickness t1 of 3-5 mm, a middle organic fiber toughened layer and a thickness t3 of 3 mm. ~5mm base toughening layer, the surface layer includes the following raw material components in parts by weight: quartz sand 40, quartz powder 10, inorganic active powder 20, pigment 0.5, water reducing agent 0.3, water 3; middle organic fiber toughening layer Including the following raw material components in parts by weight: inorganic active powder 40, sand 45, water reducer 0.8, water 6, organic fiber 0.5; the base toughening layer includes the following raw material components in parts by weight: inorganic active powder 30 , Quartz sand 30, Quartz powder 15, Water reducing agent 0.5, Water 4, Toughening agent 0.8.

[0033] Among them, the fineness modulus of the quartz sand is 2.3 (the fineness modul...

Embodiment 2

[0048] Except that the formulation of the organic fiber toughened inorganic composite artificial stone panel is different, other conditions are the same as in Example 1.

[0049] An organic fiber toughened inorganic composite artificial stone panel, comprising the following raw materials in parts by weight: the surface layer includes the following raw material components in parts by weight: quartz sand 70, quartz powder 30, inorganic active powder 45, pigment 4, water reducing Agent 1, water 10; the middle organic fiber toughening layer includes the following raw material components in parts by weight: inorganic active powder 60, sand 65, water reducing agent 1.5, water 14, organic fiber 1.2; the base toughening layer includes the following weight Each raw material component of the part: inorganic active powder 50, quartz sand 55, quartz powder 20, water reducer 1.2, water 8, toughening agent 2.5.

Embodiment 3

[0051] Except that the formulation of the organic fiber toughened inorganic composite artificial stone panel is different, other conditions are the same as in Example 1.

[0052] An organic fiber toughened inorganic composite artificial stone panel, comprising the following raw materials in parts by weight: the surface layer includes the following raw material components in parts by weight: quartz sand 50, quartz powder 15, inorganic active powder 27, pigment 1.5, water reducing agent 0.5, water 4.5; the middle organic fiber toughening layer includes the following raw material components in parts by weight: inorganic active powder 45, sand 50, water reducing agent 0.9, water 8, organic fiber 0.7; the base toughening layer includes the following weight Each raw material component of the part: inorganic active powder 35, quartz sand 36, quartz powder 16, water reducer 0.65, water 5, toughening agent 1.2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an organic fiber toughened inorganic composite artificial stone panel and a preparation method thereof. The panel comprises a surface layer, an intermediate organic fiber toughened layer, and a base toughened layer, wherein the surface layer comprises the following raw material components in parts by weight: 40-70 parts of quartz sand, 10-30 parts of a quartz powder, 20-45parts of an inorganic active powder, 0.5-4 parts of a pigment, 0.3-1 part of a water reducing agent, and 3-10 parts of water; the intermediate organic fiber toughened layer comprises the following rawmaterial components in parts by weight: 40-60 parts of the inorganic active powder, 45-65 parts of sand, 0.8-1.5 parts of the water reducing agent, 6-14 parts of water, and 4-8 parts of organic fibers; and the base toughened layer comprises the following raw material components in parts by weight: 30-50 parts of the inorganic active powder, 30-55 parts of the quartz sand, 15-20 parts of the quartz powder, 0.5-1.2 parts of the water reducing agent, 4-8 parts of water, 0.8-2.5 parts of a toughening agent. The panel has good volume stability, low shrinkage, no warping and deformation during use,extremely low water absorption, good durability, no problems such as aging, good adhesion between layers, and good ductility and no instant brittle fracture, can be used as a bearing structure, has good surface dirt resistance, and is suitable for popularization and use.

Description

technical field [0001] The invention relates to the technical field of processed artificial stone, and more specifically relates to an organic fiber toughened inorganic composite artificial stone panel and a preparation method thereof. Background technique [0002] As the country strengthens the protection of the ecological environment, natural stone mining is strictly controlled. On the other hand, China's infrastructure construction, such as airports, subway stations, high-speed rail stations, commercial plazas, and club centers, is still going on. There is also a large demand for artificial stone panel materials in a large number of infrastructure constructions. Artificial stones that replace natural stones have broad market prospects. [0003] Traditional artificial stone is mainly composed of resinous organic artificial stone and a small amount of inorganic artificial stone. Resin artificial stone mainly has the disadvantages of large heat deformation, easy deformation...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04E04F13/14B28B1/52B28B3/02
CPCC04B28/04B28B3/022B28B1/525B28B1/522E04F13/14C04B2201/50C04B14/068C04B2103/54C04B2103/302C04B16/0641C04B24/2623C04B24/2652B32B18/00C04B2111/00008C04B2111/00612C04B2111/542C04B14/06C04B14/30C04B16/0625C04B16/0633C04B16/0683C04B16/0691C04B20/0004C04B20/006C04B20/008C04B40/0028C04B40/0067C04B40/0089C04B40/0263C04B40/04B28B11/0845B28B13/022E04F13/0866E04F13/0873E04F13/142E04F13/147
Inventor 刘福财肖敏李斌
Owner 黄贺明
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com