Decontamination self-cleaning insulator protective agent and preparation method thereof

A self-cleaning, insulator technology, used in biocide-containing paints, antifouling/underwater coatings, coatings, etc. Enhanced adhesion and performance durability, excellent cleaning and detergency, and increased densification effects

Active Publication Date: 2019-12-24
北京诚和龙盛工程技术有限公司
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there is a lack of practical testing and theoretical support for recoating RTV coatings. During the use of RTV coating cleaning agents, many problems should be paid attention to: such as the type, composition and amount of pollutants attached to the surface of RTV coatings, and the aging residue of RTV coatings. Chemical composition, equipment, time and cost of cleaning operations, safety of cleaning operations, cleanliness after cleaning, environmental protection during cleaning, etc.
This limits the popularization and use of RTV paint cleaning agent to a certain extent
[0004] At present, it is also reported that the bionic lotus leaf effect is used to prepare superhydrophobic anti-fouling flashover coatings, such as Chinese Patent No. CN102417773, Chinese Patent No. CN102660182, Chinese Patent No. CN103666173 and Chinese Patent No. CN103642378 disclose four kinds of low Surface energy binder, a hydrophobic coating composed of hydrophobic nanoparticles as fillers, in certain occasions, it can have a good super-hydrophobic effect, but its wear resistance and adhesion are poor, and it will be damaged after a short period of wind erosion or friction Loss of super-hydrophobic properties, poor adhesion to plastic, glass and other substrates, limited use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Decontamination self-cleaning insulator protective agent and preparation method thereof
  • Decontamination self-cleaning insulator protective agent and preparation method thereof
  • Decontamination self-cleaning insulator protective agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0045] According to the decontamination and self-cleaning insulator protective agent provided by the present invention, the surface treatment agent includes 15-35 parts of hydrophobic nanoparticles, preferably 20-30 parts by weight. The hydrophobic nano-particles in the present invention are hydrophobic nano-silica powder, the particle size of the hydrophobic nano-silica powder is 50-200nm, and the preparation method of the hydrophobic nano-silica powder includes the following steps : Mixing nano-silica powder, bis-(γ-triethoxysilylpropyl) tetrasulfide, water, azobisisobutyronitrile and ethanol, the nano-silica powder, bis- The mass ratio of (γ-triethoxysilylpropyl) tetrasulfide, water, azobisisobutyronitrile and ethanol is (4-8): (2-5): (0.5-1): (0.05 -0.5): (3-6), after stirring for 3-6h in a reaction kettle at 50-120℃, mixture one is obtained, and the mixture is naturally cooled to room temperature, and the above mixture one is extracted at 50-80℃ using a Soxhlet extractor. ...

Embodiment 1

[0050] 1) The configuration of the mixed solvent: stir and disperse 5 parts of isopropanol, 20 parts of 120# gasoline, 56 parts of trifluorotrichloroethane and 10 parts of ethanol to obtain a mixed solvent;

[0051] 2) The configuration of the primer: add 3 parts of hydrogen-containing silicone oil to 89 parts of the above-mentioned mixed solvent, and then add 8 parts of micron particles at a speed of 1500 rpm and continue to disperse at a high speed for 15 minutes to obtain the primer ;

[0052] 3) The configuration of the surface treatment agent: stir and mix 15 parts of low surface energy resin with 55 parts of ethyl acetate, and then add 30 parts of hydrophobic nanoparticles at a speed of 5000 rpm to continue high-speed dispersion for 25 minutes to obtain the surface treatment agent ;

[0053] The active hydrogen content of the hydrogen-containing silicone oil in the present invention is 0.35%, and the viscosity is 110 mPa·s,

[0054] The hydrophobic nano-particles are hydrophobi...

Embodiment 2

[0056] 1) The configuration of the mixed solvent: 15 parts of isopropanol, 25 parts of 120# gasoline, 52 parts of trifluorotrichloroethane and 8 parts of ethanol are stirred and dispersed uniformly to obtain a mixed solvent;

[0057] 2) The configuration of the primer: add 6 parts of hydrogen-containing silicone oil to 82 parts of the above mixed solvent, and then add 12 parts of micron particles at 3000 rpm and continue to disperse at high speed for 20 minutes to obtain the primer ;

[0058] 3) The configuration of the surface treatment agent: stir and mix 10 parts of low surface energy resin with 65 parts of ethyl acetate, then add 25 parts of hydrophobic nanoparticles at 3000 rpm and continue to disperse at high speed for 20 minutes to obtain the surface treatment agent ;

[0059] The hydrogen-containing silicone oil in the present invention has an active hydrogen content of 0.6% and a viscosity of 580 mPa·s; the hydrophobic nanoparticles include hydrophobic nano silica with part...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a decontamination self-cleaning type insulator protective agent, which is prepared from a bottom treating agent and a surface treating agent, wherein the bottom treating agentis prepared from, by weight, 3-8 parts of hydrogen-containing silicone oil, 1-15 parts of micron-sized powder and 85-95 parts of a mixed solvent; and the surface treating agent is prepared from 3 to 15 parts of low-surface-energy resin, 15 to 35 parts of hydrophobic nanoparticles and 30 to 85 parts of ethyl acetate; the invention also discloses a preparation method of the decontamination self-cleaning insulator protective agent. The decontamination self-cleaning type insulator protective agent has excellent cleaning and decontamination performance and good adhesion to various base materials, and a protective film formed on the surface of a treated object has the characteristics of good super-hydrophobicity, wear resistance, durability and the like.

Description

Technical field [0001] The invention belongs to the technical field of insulation protection, and specifically relates to a dirt-removing and self-cleaning insulator protection agent and a preparation method thereof. Background technique [0002] In severe weather conditions (such as rain, fog, dew, etc.), flashover will occur along the contaminated and humid insulator surface, causing a pollution flashover accident in the power system. In the power system, due to the wide range of power grid pollution flashover accidents and long power outages, they seriously threaten the safe operation of power transmission and transformation equipment and cause huge economic losses to the national economy. Therefore, the pollution flashover problem of the power grid has always plagued power An important subject of business development, how to effectively solve the problem of power grid pollution flashover has become an important task to ensure the safe production of power systems. [0003] In r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/05C09D127/12C09D5/16C09D7/20C09D7/62C09D7/65
CPCC08K2201/011C08L2203/20C08L2205/025C08L2205/03C09D5/1675C09D5/1687C09D127/12C09D183/04C09D7/20C08L27/18C08K9/06C08K3/36
Inventor 车千里陈浩刘宝安骆川刘泉林
Owner 北京诚和龙盛工程技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com