Modified floating bead/graphene oxide flame-retardant runway particle material

A granular material, graphene technology, applied in roads, roads, buildings, etc., can solve problems such as escape and rescue personnel difficulties, environmental threats, fatal accidents, etc., achieve good processing performance and mechanical properties, good flame retardant effect, market great effect

Inactive Publication Date: 2019-12-17
福建宸琦新材料科技有限公司
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Once a fire breaks out, it will bring great difficulties to escape and rescue personnel. In severe cases, it will lead to fatal accidents, and it also poses a greater threat to the environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified floating bead/graphene oxide flame-retardant runway particle material
  • Modified floating bead/graphene oxide flame-retardant runway particle material
  • Modified floating bead/graphene oxide flame-retardant runway particle material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A method for preparing modified floating beads / graphene oxide flame-retardant runway granular material, the specific steps are:

[0030] 1) Disperse 10g of floating beads in 100mL of 20% HNO 3 , acidified by ultrasonication for 1 h, washed several times with absolute ethanol, and dried at 70°C.

[0031] 2) Measure absolute ethanol and deionized water in a volume ratio of 9:1 and mix them in a beaker, add 2mL KH550, and stir at room temperature for 1h.

[0032] 3) Disperse 2g of floating beads in the solution described in 2), stir at 80°C for 6h, wash with absolute ethanol and dry at 110°C to obtain modified floating beads.

[0033] 4) Dissolve 1 part of GO prepared by the Hummers method in deionized water, add 0.5 part of sodium hexadecylbenzene sulfonate and ultrasonically shake for 30 minutes, then add 1 part of modified floating beads, stir for 1 hour, wash and then bake at 60 °C Dry. A compound flame retardant is prepared.

[0034] 5) Weigh 20 parts of polystyre...

Embodiment 2

[0039] A method for preparing modified floating beads / graphene oxide flame-retardant runway granular material, the specific steps are:

[0040] 1) Disperse 10g of floating beads in 100mL of 20% HNO 3 , acidified by ultrasonication for 1 h, washed several times with absolute ethanol, and dried at 70°C.

[0041] 2) Measure absolute ethanol and deionized water in a volume ratio of 9:1 and mix them in a beaker, add 2mL KH550, and stir at room temperature for 1h.

[0042] 3) Disperse 2g of floating beads in the solution described in 2), stir at 80°C for 6h, wash with absolute ethanol and dry at 110°C to obtain modified floating beads.

[0043] 4) Dissolve 1 part of GO prepared by the Hummers method in deionized water, add 0.5 part of sodium hexadecylbenzenesulfonate and ultrasonically shake for 30 minutes, then add 2 parts of modified floating beads, stir for 1 hour, wash and then bake at 60 °C Dry. A compound flame retardant is prepared.

[0044] 5) Weigh 20 parts of polystyre...

Embodiment 3

[0049] A method for preparing modified floating beads / graphene oxide flame-retardant runway granular material, the specific steps are:

[0050] 1) Disperse 10g of floating beads in 100mL of 20% HNO 3 , acidified by ultrasonication for 1 h, washed several times with absolute ethanol, and dried at 70°C.

[0051] 2) Measure absolute ethanol and deionized water in a volume ratio of 9:1 and mix them in a beaker, add 2mL KH550, and stir at room temperature for 1h.

[0052] 3) Disperse 2g of floating beads in the solution described in 2), stir at 80°C for 6h, wash with absolute ethanol and dry at 110°C to obtain modified floating beads.

[0053] 4) Dissolve 1 part of GO prepared by the Hummers method in deionized water, add 0.5 part of sodium hexadecylbenzenesulfonate and ultrasonically shake for 30 minutes, then add 3 parts of modified floating beads, stir for 1 hour, wash and then bake at 60 °C Dry. A compound flame retardant is prepared.

[0054] 5) Weigh 20 parts of polystyre...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
degree of graftingaaaaaaaaaa
oxygen indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses a modified floating bead / graphene oxide flame-retardant runway particle material and a preparation method thereof. The material comprises the following raw materials in parts by weight: 100 parts of a rubber-plastic elastomer, 10-50 parts of a compound flame retardant, 5-12 parts of naphthenic oil, 5-10 parts of superfine white carbon black, 3-5 parts of slaked lime, 1-2 parts of zinc stearate, 100-130 parts of calcium carbonate and 0.5 part of plastic toner; and the mass ratio of modified floating beads to graphene oxide in the compound flame retardant is (1-5): 1. Theprepared modified floating bead / graphene oxide flame-retardant runway particle material has the characteristics of good flame-retardant effect, aging resistance, high tensile strength and the like, and is wide in application prospect and huge in market demand.

Description

technical field [0001] The invention belongs to the technical field of plastic runways, and in particular relates to a modified floating bead / graphene oxide flame-retardant runway granular material and a preparation method thereof. Background technique [0002] The plastic runway is an indispensable and important facility in modern track and field venues, and has been designated by the International Olympic Committee as one of the necessary conditions for international competition venues. Compared with the traditional soil runway, it has good elasticity, skid resistance, wear resistance, shock absorption, easy site maintenance, bright colors, beautiful and tidy. In view of the above advantages, the plastic track was quickly adopted by various track and field venues soon after it came out. However, runway granules are flammable materials, which are easy to cause fire during use and pose a great threat to people's property and personal safety. Therefore, it is imperative to f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/16C08L53/02C08L75/04C08L51/06C08L23/12C08K13/06C08K9/06C08K9/02C08K7/26C08K3/04E01C13/00
CPCC08L23/16C08L2201/02C08L2205/035E01C13/00C08L53/025C08L75/04C08L51/06C08L23/12C08K13/06C08K9/06C08K9/02C08K7/26C08K3/042
Inventor 郑玉婴于文泰
Owner 福建宸琦新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com