A kind of dyeing method of polyester nylon composite silk fabric

A polyester-nylon composite yarn and dyeing method technology, applied in the direction of dyeing method, textile and papermaking, etc., can solve the problems of imperfect dyeing process, poor dyeability and poor color fastness of polyester-nylon composite yarn fabrics, and improve the color fastness. The effect of high color fastness, high color fastness and full color

Active Publication Date: 2022-03-22
HANGZHOU ZHUODA PRINTING & DYEING CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the imperfect dyeing process of polyester-nylon composite silk fabrics, the dyeability and color fastness of polyester-nylon composite silk fabrics are poor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of dyeing method of polyester nylon composite silk fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] A method for dyeing polyester-nylon composite silk fabrics, comprising cold-stacking pretreatment, open-width drum vibration washing, overflow tank pre-shrinking, presetting treatment, disperse dyeing, acid overdyeing, and setting treatment.

[0055] Specifically include the following steps:

[0056] (1) Cold stack pretreatment

[0057] Pretreatment working solution: caustic soda 75g / L, hydrogen peroxide 9g / L with a weight fraction of 40%, refining agent TF125L 3.5g / L, chelating agent TF-510T 1g / L;

[0058] Pre-treatment process: Under the condition of temperature of 40°C and vehicle speed of 35m / min, padding is carried out on the fabric, the excess rate is 70%, and then coiled, and then wrapped and sealed with plastic paper, at a temperature of 40°C Under the conditions of stacking, stacking treatment 30h, in the whole process of stacking, keep the rotating speed of stacking at 8r / min;

[0059] (2) Open-width rotary drum vibration washing

[0060] Shock washing work...

Embodiment 2

[0083] A method for dyeing polyester-nylon composite silk fabrics, comprising cold-stacking pretreatment, open-width drum vibration washing, overflow tank pre-shrinking, presetting treatment, disperse dyeing, acid overdyeing, and setting treatment.

[0084] Specifically include the following steps:

[0085] (1) Cold stack pretreatment

[0086] Pretreatment working solution: caustic soda 85g / L, hydrogen peroxide with a weight fraction of 30% 7.5g / L, refining agent TF125L 3g / L, chelating agent TF-510T 1.5g / L;

[0087] Pre-treatment process: Under the condition of temperature of 35°C and vehicle speed of 30m / min, padding is carried out on the fabric, the excess rate is 75%, and then rolled, and then wrapped and sealed with plastic paper, at a temperature of 40°C Under the condition of 28 hours, keep the rotation speed of stacking at 8r / min during the whole process of stacking;

[0088] (2) Open-width rotary drum vibration washing

[0089] Shock washing working fluid: caustic s...

Embodiment 3

[0112] A method for dyeing polyester-nylon composite silk fabrics, comprising cold-stacking pretreatment, open-width drum vibration washing, overflow tank pre-shrinking, presetting treatment, disperse dyeing, acid overdyeing, and setting treatment.

[0113] Specifically include the following steps:

[0114] (1) Cold stack pretreatment

[0115] Pretreatment working solution: caustic soda 80g / L, hydrogen peroxide with a weight fraction of 35% 8g / L, refining agent TF125L 4g / L, chelating agent TF-510T 2g / L;

[0116] Pre-treatment process: Under the condition of temperature of 40°C and vehicle speed of 35m / min, padding is carried out on the fabric, the excess rate is 80%, and then coiled, and then wrapped and sealed with plastic paper, at a temperature of 40°C Under certain conditions, the stacking process was carried out for 24 hours, and during the whole stacking process, the rotating speed of the stacking was kept at 8r / min;

[0117] (2) Open-width rotary drum vibration washin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for dyeing polyester-nylon composite silk fabrics, which belongs to the technical field of fabric dyeing, and includes cold pile pretreatment, open-width drum oscillation washing, overflow tank pre-shrinking, pre-setting treatment, disperse dyeing, and acid overdyeing. , setting treatment, and use the synergy between the working fluids of each step and the synergy between the processes of each step to make the fabric show high color fastness to perspiration, color fastness to water stains, and color fastness to soaping High degree, so that the fabric has the advantages of high color fastness, and also has the advantages of full and rich colors.

Description

technical field [0001] The invention relates to the technical field of fabric dyeing, in particular to a method for dyeing polyester-nylon composite silk fabrics. Background technique [0002] Polyester-nylon composite yarn fabric is a fabric made of polyester-nylon composite yarn. Polyester-nylon composite yarn is two polymer melts that are divided by a special distribution plate, and then extruded through the same spinneret hole, that is, it has nylon It has the advantages of wear resistance and high strength, and polyester has the advantages of good elasticity and shape retention. However, due to the imperfect dyeing process of the polyester-nylon composite yarn fabric, the dyeing property and color fastness of the polyester-nylon composite yarn fabric are relatively poor. Contents of the invention [0003] The object of the present invention is to provide a method for dyeing polyester-nylon composite silk fabrics, which has the advantages of high color fastness, full ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06P1/16D06P1/44D06P1/673D06P1/653D06P5/10D06P5/02D06P1/41D06P3/87
CPCD06P1/0032D06P1/16D06P1/445D06P1/67341D06P1/6533D06P5/10D06P5/02D06P1/41D06P1/6735D06P1/673D06P3/8219D06P3/54D06P3/06
Inventor 圣光应浩叶民
Owner HANGZHOU ZHUODA PRINTING & DYEING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com