A quick-setting epoxy perfusion mortar suitable for emergency repair construction in summer

Abstract

The invention discloses a quick-setting epoxy grouting mortar suitable for emergency repair construction in summer, which consists of resin component A, curing agent component B and bone powder component C in a mass ratio of 1:(0.2-0.26): (5-7) mixed; A component by weight parts: 100 parts of modified epoxy resin, 1-15 parts of alcohol ether compound diluent, 1-3 parts of coupling agent, 0.5-0.5 parts of rheological agent 3; B component by weight: 16-23 parts of modified polyamine curing agent, 1-3 parts of accelerator; C component by weight: 1-23 parts of dolomite powder, 15-23 parts of barium sulfate powder 46 parts, 10-121 parts of cement, 385-588 parts of sea sand, and 0.1-1.5 parts of defoamer. The invention has the technical characteristics of short curing time, high hourly strength, and no violent aggregation during high-temperature construction. It is also non-toxic, harmless, and simple to prepare. Suitable for summer repair construction.

Description

technical field [0001] The invention belongs to the technical field of emergency repair construction of construction engineering, and in particular relates to a quick-setting epoxy perfusion mortar suitable for emergency repair construction in summer. Background technique [0002] Epoxy perfusion mortar is a kind of perfusion gravity mortar material mixed with epoxy resin, curing agent and bone powder in a certain proportion. Epoxy perfusion mortar has excellent mechanical properties and bonding properties, high early strength, and is widely used in defect repair and reinforcement of concrete engineering structures; epoxy mortar also has excellent flexural and fatigue resistance, and is often used in bridge supports, Anchoring of equipment foundations, grouting of supporting substrates of large equipment under dynamic load conditions such as rails and door cranes. [0003] The current repair materials mostly use finished cement-based grouting materials, which have good cons...

AI Technical Summary

Problems solved by technology

[0004] Chinese patent CN201210312422.3 discloses a "high-strength and fast-curing epoxy resin grouting material and its preparation method". It has the characteristics of high adhesion to the substrate, but the hourly strength of this method is not high, and the curing time of 60MPa is more than 10h. There is still a big gap in the early strength development and the requirements for emergency repairs.

At the same time, due to the relatively small size of the mortar (<2.5), for deeper pouring depths, the amount of glue used will cause heat accumulation, especially when the ambient temperature is high in summer.

[0005] Chinese patent CN201610227275.0 discloses a "high-strength quick-setting epoxy resin mortar and its preparation method". However, the curing time is still above 6 hours, and the dosage range of triethylenetetramine and tetraethylenepentamine aliphatic amine curing agents is relatively small, which requires high accuracy of mixing and weighing, and is easy to explode at high temperature, and is harmful to the human body. More poisonous

[0006] Chinese patent CN201711423774.5 discloses a "high-strength and high-fluidity epoxy resin grouting material and its preparation method". In this method, a curing agent system of aliphatic amine, alicyclic amine and polyether amine and a thixotropic agent are used. Excellent construction fluidity and mechanical strength, but long curing time, unable to meet emergency repair requirements