Recycled aggregate water-permeable brick and production method thereof

A technology of recycled aggregates and permeable bricks, which is applied in the field of building materials, can solve the problems of complex preparation of raw materials, high strength, and long maintenance period, and achieve fast and simple mixing ratio and preparation method, high compressive strength and water permeability coefficient, and improved The effect of resource utilization

Active Publication Date: 2019-11-05
QINGDAO AGRI UNIV
View PDF4 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] 1. Recycled aggregate permeable bricks with high strength mostly use recycled and natural aggregates in a ratio of half, while permeable bricks using fully recycled aggregates have lower strength;
[0007] 2. The cement consumption of recycled aggregate permeable bricks is relatively large, and the cement consumption mostly accounts for more than 70%;
[0008] 3. The preparation of raw materials is complicated, the preparation method is complicated, and the material preparation is complicated;
[0009] 4. Most of the maintenance methods adopt standard maintenance. The maintenance conditions are difficult to achieve, and the cost is relatively high, the maintenance cycle is long, the storage space is occupied, and it is difficult to realize large-scale industrial production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A recycled aggregate permeable brick. The base layer comprises the following raw materials in parts by weight: 100 parts of Class II recycled aggregate, 14 parts of cement, 14 parts of fly ash, and 0.28 parts of a water reducer.

[0037] Wherein, in parts by weight, the parts of the recycled aggregate with a particle size of 1.18-2.36 mm, 2.36-4.75 mm, and 4.75-9.5 mm respectively account for 40 parts, 40 parts, and 20 parts.

[0038] The main process parameters of the preparation method of recycled aggregate permeable bricks: put the mixture into the mold, vibrate and extrude, the pressure is 2.0MPa, and the time is 25s; , autoclaved curing temperature 173 ℃, pressure 0.8 MPa, time 8h.

[0039] Contrast style 1:

[0040] A recycled aggregate permeable brick. The base layer comprises the following raw materials in parts by weight: 100 parts of natural aggregate, 166 parts of cement, 16 parts of fly ash, and 0.28 parts of water reducing agent.

[0041] Wherein, in part...

Embodiment 2

[0045] A recycled aggregate permeable brick. The base layer comprises the following raw materials in parts by weight: 100 parts of Class II recycled aggregate, 16 parts of cement, 16 parts of fly ash, and 0.32 parts of a water reducer.

[0046] Wherein, the parts of the recycled aggregate with particle diameters of 1.18-2.36 mm, 2.36-4.75 mm, and 4.75-9.5 mm account for 40, 40, and 20 parts, respectively.

[0047] The main process parameters of the preparation method of recycled aggregate permeable bricks: the mixture is put into the mold, vibrating and extruded, the pressure is 1.5MPa, and the time is 30s; , autoclaved curing temperature 173 ℃, pressure 0.8 MPa, time 8h.

[0048] Contrast style 2:

[0049] A recycled aggregate permeable brick. The base layer comprises the following raw materials in parts by weight: 100 parts of Class II recycled aggregate, 22.4 parts of cement, 9.6 parts of fly ash, and 0.32 parts of water reducing agent.

[0050] Wherein, the regenerated a...

Embodiment 3

[0054] A recycled aggregate permeable brick. The base layer comprises the following raw materials in parts by weight: 100 parts of Class II recycled aggregate, 14 parts of cement, 14 parts of fly ash, and 0.28 parts of a water reducer.

[0055] Wherein, the parts of the recycled aggregate with particle diameters of 1.18-2.36 mm, 2.36-4.75 mm, and 4.75-9.5 mm account for 60, 30, and 10 parts, respectively.

[0056] The main process parameters of the preparation method of recycled aggregate permeable bricks: put the mixture into the mold, vibrate and extrude, the pressure is 3MPa, and the time is 15s; The autoclave curing temperature is 183°C, the pressure is 1 MPa, and the time is 6h.

[0057] Contrast style 3:

[0058] A recycled aggregate permeable brick. The base layer comprises the following raw materials in parts by weight: 100 parts of Class II recycled aggregate, 14 parts of cement, 14 parts of fly ash, and 0.28 parts of a water reducer.

[0059] Wherein, the particle si...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a recycled aggregate water-permeable brick and a production method thereof. The recycled aggregate water-permeable brick comprises a base layer, and the base layer comprises, byweight, 95-105 parts of recycled aggregates, 14-16 parts of cement, 14-16 parts of fly ash and 0.22-0.32 part of a water reducer. The production method comprises the following steps: uniformly mixingthe cement, the fly ash and the water reducer, adding water, performing stirring, and adding wetted aggregates; adding the obtained mixture into a mold, and carrying out vibration extrusion molding under 1.5-3 MPa for 15-30 s; and demolding the obtained water-permeable brick, standing the water-permeable brick for 2 h, transferring the water-permeable brick into an autoclave, and curing the water-permeable brick under 0.8-1 MPa at 173-185 DEG C for 6-10 h. The aggregates are recycled aggregates, the use amount of the cement is small, the water-permeable brick has a high compressive strength and a high water permeability, the molding process is quick and simple, and has a low cost, and the environmental pollution can be effectively reduced, so the recycled aggregate water-permeable brick is suitable for large-scale industrial production.

Description

technical field [0001] The invention belongs to the technical field of building materials, in particular to a recycled aggregate permeable brick and a preparation method thereof. Background technique [0002] At present, natural resources are scarce, and the price of construction raw materials continues to rise. Making construction waste into recycled aggregate after crushing, screening and particle shaping can effectively realize the resource utilization of construction waste, alleviate the current situation of resource shortage, and achieve resource conservation. The purpose of reducing environmental pollution. Due to the large fluctuations in the quality of recycled aggregate, its instability limits its application in housing construction. Most of the recycled concrete is used in infrastructure construction with low safety requirements. These products have low market value, and the recycled aggregate is prepared As a new type of pavement material, permeable brick has the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B38/00C04B40/02C04B18/08C04B18/16
CPCC04B28/04C04B40/024C04B2111/00284C04B18/16C04B18/08C04B2103/302C04B38/0041Y02W30/91
Inventor 岳公冰李秋义王卓
Owner QINGDAO AGRI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products