A kind of preparation method of antibacterial glass and antibacterial vacuum glass

A technology of antibacterial glass and vacuum glass, which is applied in glass manufacturing equipment, glass tempering, manufacturing tools, etc., can solve the problems of easy oxidation of antibacterial ions, decrease of glass transmittance, complex process, etc., to achieve favorable performance and transmittance Light performance, avoiding the decrease of light transmittance, simple and effective method

Active Publication Date: 2021-09-28
CHINA BUILDING MATERIALS ACAD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Therefore, the technical problem to be solved by the present invention is to overcome the defects that the antibacterial glass preparation process in the prior art mostly adopts step-by-step exchange, the process is complex, the cost is high, and the bacteriostatic ions are easily oxidized, and the light transmittance of the glass decreases more. , thereby providing a preparation method of antibacterial glass and antibacterial vacuum glass

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of antibacterial glass and antibacterial vacuum glass
  • A kind of preparation method of antibacterial glass and antibacterial vacuum glass

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Embodiment 1 (embodiment 1-6 is chemical method)

[0043] The present embodiment provides a kind of preparation method of antibacterial glass, concrete steps are:

[0044] Cut the original glass sheet with a thickness of 4mm, put it into the mixed molten salt of potassium nitrate, silver nitrate and ferrous sulfate, in which the mass fraction of silver ions is 0.1%, and the mass concentration of ferrous ions is 0.2%. Conditions, ion exchange for 2 minutes, then the glass is taken out, cooled and cleaned to obtain the antibacterial glass.

Embodiment 2

[0046] The present embodiment provides a kind of preparation method of antibacterial glass, concrete steps are:

[0047] Cut the original glass sheet with a thickness of 4mm and put it into the mixed molten salt of potassium nitrate, silver nitrate and ferrous sulfate, in which the mass fraction of silver ions is 3%, and the mass concentration of ferrous ions is 1.5%. Under the condition of ℃, ion exchange for 1 minute, then the glass is taken out, cooled and washed to obtain the antibacterial glass.

Embodiment 3

[0049] The present embodiment provides a kind of preparation method of antibacterial glass, concrete steps are:

[0050] Cut the original glass sheet with a thickness of 4mm, put it into the mixed molten salt of potassium nitrate, silver nitrate and ferrous sulfate, in which the mass fraction of silver ions is 0.01%, and the mass concentration of ferrous ions is 0.01%. Conditions, ion exchange for 10 minutes, then take out the glass, cool and wash to obtain the antibacterial glass.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
heightaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of glass preparation, and in particular relates to a preparation method of antibacterial glass and antibacterial vacuum glass. The preparation method of the antibacterial glass comprises the following steps of performing one-step ion exchange on the glass with a salt solution or melt containing silver and ferrous ions, and introducing antibacterial ions into the glass body to obtain the antibacterial glass. The invention realizes the exchange of antibacterial ions and sodium and potassium ions inside the glass through a one-step ion exchange method, and introduces antibacterial ions into the glass body, the method is simple and effective, and the cost is saved. By introducing ferrous ions in the ion exchange process, the oxidation of antibacterial ions can be effectively inhibited, the concentration of antibacterial ions can be effectively increased, and the decrease of light transmittance of glass can be avoided, which is beneficial to the improvement of antibacterial glass performance and light transmission performance.

Description

technical field [0001] The invention belongs to the technical field of glass preparation, and in particular relates to a preparation method of antibacterial glass and antibacterial vacuum glass. Background technique [0002] With the advancement of science and technology and the improvement of people's living standards, people pay more and more attention to environmental sanitation. Refrigerators and freezers are becoming more and more popular as heat preservation and refrigeration equipment in people's daily life. Now the glass used for ordinary freezer doors is hollow glass. Compared with vacuum glass, its thickness is large and its heat insulation performance is poor. There is a small amount of application in luxury goods such as wine cabinets; as for antibacterial vacuum glass, there is little research, and there are no related mature products yet. [0003] Antibacterial glass, also known as green glass, is a new type of ecological functional material, which is of great...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C21/00C03B27/00C03C27/10C03C27/08
CPCC03B27/00C03C21/001C03C21/005C03C27/08C03C27/10
Inventor 张凡陈玮李要辉王晋珍
Owner CHINA BUILDING MATERIALS ACAD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com