Polyacrylate resin 3D printing material and preparation method thereof

A polyacrylate, 3D printing technology, applied in the field of printing materials, can solve the problems of poor stain resistance and water resistance, insufficient cohesion, weak adhesion, etc., to achieve stain resistance and water resistance, improve electrical conductivity, and strong adhesion Effect

Inactive Publication Date: 2019-08-23
广东华斓汽车材料研究院
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to overcome the problems that the existing existing 3D printing materials also have insufficient strength, poor colorability, weak temperature resistance, insufficient cohesion, weak adhesion, poor stain resistance and water resistance. Problem, the quality of the printed product cannot be guaranteed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyacrylate resin 3D printing material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The invention provides a polyacrylate resin 3D printing material and a preparation method thereof. The components of the coating are calculated according to the weight percentage content: 15-20% of photosensitive resin polymer monomer, and 10-20% of photosensitive resin prepolymer , Photoinitiator 0.5 to 5%, terminator 1 to 2.5%, functionalized nanoparticles 5 to 10%, color additives 5 to 10%, high scores from polymers 10 to 25%, polymer additives 3.5 to 5%, Metal powder 5-10%, carbon fiber 0.5-2%, binder 0.5-1%, inorganic filler 1.5-3%, compatibilizer 2-5%, polyacrylate resin 20-30%, ABS plastic masterbatch 11 ~20% and PLA10~15%.

[0028] Specific steps are as follows:

[0029] Step 1: Take the ethylenically unsaturated phosphate monomer, acrylic acid and its lipid monomer chain transfer agent and initiator, place them in a mechanical mixer and stir evenly until a monomer mixture is formed;

[0030] Step 2: Melt and mix the ABS plastic masterbatch and PLA at high temperatur...

Embodiment 2

[0036] The invention provides a polyacrylate resin 3D printing material and a preparation method thereof. The components of the coating are calculated according to the weight percentage content: 15-20% of photosensitive resin polymer monomer, and 10-20% of photosensitive resin prepolymer , Photoinitiator 0.5 to 5%, terminator 1 to 2.5%, functionalized nanoparticles 5 to 10%, color additives 10 to 15%, high scores from polymers 10 to 25%, polymer additives 3.5 to 5%, Carbon fiber 0.5-2%, adhesive 0.5-1%, inorganic filler 1.5-3%, compatibilizer 2-5%, ABS plastic masterbatch 21-20% and PLA 20-15%.

[0037] Specific steps are as follows:

[0038] Step 1: Melt and mix ABS plastic masterbatch and PLA evenly at high temperature. After the mixture is cooled to 40-55°C, put it into extrusion, then pulverize to obtain powder;

[0039] Step 2: Dissolve the photosensitive resin polymer monomer, photoinitiator and terminator in a solvent, and perform a prepolymerization reaction at a certain tem...

Embodiment 3

[0044] The invention provides a polyacrylate resin type 3D printing material and a preparation method thereof. The components of the coating are calculated according to the weight percentage content: 25-20% of photosensitive resin polymer monomer and 20-25% of photosensitive resin prepolymer , Photoinitiator 0.5 to 5%, terminator 1 to 2.5%, color additives 5 to 10%, high scores from polymer 10 to 25%, polymer additives 3.5 to 5%, metal powder 5 to 10%, carbon fiber 0.5 ~2%, 0.5~1% of adhesive, 1.5~3% of inorganic filler, 2~5% of compatibilizer, 25~30% of polyacrylate resin.

[0045] Specific steps are as follows:

[0046] Step 1: Take the ethylenically unsaturated phosphate monomer, acrylic acid and its lipid monomer chain transfer agent and initiator, place them in a mechanical mixer and stir evenly until a monomer mixture is formed;

[0047] Step 2: Dissolve the photosensitive resin polymer monomer, photoinitiator and terminator in a solvent, and perform a prepolymerization reacti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a polyacrylate resin 3D printing material, and a preparation method thereof. The polyacrylate resin 3D printing material comprises, by weight, 15 to 20% of a photosensitive resin polymer monomer, 10 to 20% of a photosensitive resin prepolymer, 0.5 to 5% of a photoinitiator, 1 to 2.5% of a terminator, 5 to 10% of functionalized nanoparticles, 5 to 10% of a color additive, 10to 25% of a high molecular polymer, 3.5 to 5% of a high molecular additive, 5 to 10% of metal powder, 0.5 to 2% of carbon fiber, 0.5 to 1% of an adhesive, 1.5 to 3% of an inorganic filler, 2 to 5% ofa compatibilizer, 20 to 30% of polyacrylate resin, 11 to 20% of ABS plastic masterbatch, and 10 to 15% of PLA. The adopted polyacrylate resin is a high elasticity polyacrylate resin, a formed film after film forming is compact, the surface of the 3D printing material is provided with the compact protective film, so that water and oxygen insulation effect and 3D printing material oxidation effectare achieved, the temperature resistance is excellent, the cohesive force is large, the clunging force is high, and stain resistance and water resistance are excellent.

Description

Technical field [0001] The invention relates to a printing material, in particular to a polyacrylate resin 3D printing material and a preparation method thereof. Background technique [0002] 3D printing is known as another industrial revolution that subverts traditional manufacturing. Its forming process is: first design the required computer three-dimensional surface or solid model by the software, and then layer it according to a certain thickness according to the process requirements, and turn the original three-dimensional electronic model into two-dimensional plane information. The layered data is processed to a certain extent, the processing parameters are input, and the numerical control code is generated: under the control of the microcomputer, the numerical control system sequentially processes each thin layer in an orderly manner in a plane processing mode and makes them automatically bonded and formed. 3D printing technology It is still in its infancy in China, with ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/12C09D133/14C09D155/02C09D167/04C09D179/08C09D5/16
CPCB33Y70/00C08K2003/0806C08K2003/0812C08K2003/265C08K2201/001C08K2201/011C08L2201/08C08L2205/035C09D5/1687C09D7/61C09D7/65C09D7/70C09D133/12C08L33/14C08L55/02C08L67/04C08L79/08C08L69/00C08L63/00C08K13/04C08K7/06C08K3/08C08K3/26
Inventor 李桂琴林志丹汤汉良王小健杜续生张鹏巫克帆
Owner 广东华斓汽车材料研究院
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com