A kind of bubble glaze for glass mosaic and preparation process of glass mosaic

A technology of glass mosaic and bubble glaze, which is applied in the field of glass mosaic, can solve the problem of single surface effect, etc., and achieve the effect of strong three-dimensional effect, good bubble effect and clear texture

Active Publication Date: 2022-04-29
佛山市唯格建材有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the splicing pattern of glass mosaic is very rich, the surface effect of a single glass mosaic product on the market is very single, which is not enough to meet the needs of users

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of bubble glaze for glass mosaic and preparation process of glass mosaic
  • A kind of bubble glaze for glass mosaic and preparation process of glass mosaic
  • A kind of bubble glaze for glass mosaic and preparation process of glass mosaic

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0051] Embodiment group A-B-a kind of preparation technology of the glass mosaic with bubble effect, comprises the following steps:

[0052] (1) Weigh the glass powder, blowing agent and low-temperature lead-free frit according to the proportions in Table 1 below, and sieve them to the limits of the glaze fineness in Table 2 below, and set aside;

[0053] (2) Take the sieved glass powder, foaming agent and low-temperature lead-free frit, add stabilizer and suspending agent, add water and carry out ball milling, the ball milling process parameters are limited by the ball milling ratio and ball milling time in Table 2, and obtain the basic glaze pulp;

[0054] (3) Take 90-95 parts of the basic glaze slurry obtained in step (2), and 0-5 parts of the coloring material, stir evenly, add water to mix according to the mass-volume concentration limit in Table 2, and obtain the glazing glaze slurry-bubble Glaze A1, A2, A3;

[0055] (4) Apply the glazing slurry obtained in step (3) to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a bubble glaze for glass mosaics. The bubble glaze comprises the following raw materials according to mass percentage: 80-90 parts of glass powder, 5-10 parts of foaming agent, and 5-10 parts of low-temperature lead-free frit 10 parts, 0-5 parts of pigment and water; and the fineness of the bubble glaze is 200-250 mesh. Correspondingly, the invention also discloses a glass mosaic with the bubble glaze and a preparation method thereof. The glass mosaic with bubble effect prepared by using the technical scheme of the invention has uniform and fine glaze, good bubble effect, clear texture and strong three-dimensional effect.

Description

technical field [0001] The invention relates to the technical field of glass mosaics, in particular to a bubble glaze for glass mosaics and a preparation process for glass mosaics. Background technique [0002] Made of natural minerals and glass powder, glass mosaic is the safest building material and an outstanding environmental protection material. With the continuous improvement of people's living standards, people's pursuit of home interior decoration is also changing, and the requirements for decorative mosaics are also increasing. At present, for home decoration, especially the decoration of bathrooms and kitchens, glass mosaics can be used to create richer pattern effects, so more people choose glass mosaics with rich pattern effects. Although the splicing pattern of glass mosaic is very rich, the surface effect of a single glass mosaic product on the market is very single, which is not enough to meet the needs of users. Therefore, in order to further improve the ri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/02C03C8/14C03C17/02
CPCC03C8/02C03C8/14C03C17/02
Inventor 姚文江任东王飞韦明皇
Owner 佛山市唯格建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap