A Laser Arc Fused Wire Welding Process Avoiding Slag Inclusion

A laser arc and welding process technology, applied in laser welding equipment, welding equipment, welding media, etc., can solve the problems of complex equipment structure, low efficiency of slag removal, and numerous operations, so as to achieve sufficient metallurgical reaction, less electrode spatter, Avoid the effect of slag inclusion

Active Publication Date: 2020-09-15
HUBEI TRI RING FORGING
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing patent number is CN201810046047.X, and the Chinese invention patent titled "Casting Magnesium Alloy Products Surface Treatment Equipment and Process" discloses a kind of equipment and process for treating slag inclusions on the surface of magnesium alloy products, and the equipment structure is complex , many operations, and the efficiency of slag removal is low and the cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A laser arc fuse welding process for avoiding slag inclusion in the present invention comprises the following steps: S1: fixing the workpiece, grinding the welding part of the workpiece; S2: spraying cleaning agent on the welding part; S3: preheating before welding: the workpiece needs to be cleaned before welding Preheating; S4: Activation of the welding surface: after the heating is stopped, the active agent is sprayed quickly; S5: After the welding part is dry, the welding operation is performed with an electrode; S6: Cooling is used to set the shape.

[0024] As a further improvement of the present invention, the welding rod in step S6 includes the following components and proportions: a, coating components: 100 parts of marble, 50 parts of fluorite, 10 parts of silicate, 15 parts of deoxidizer, and 25 parts of alloying agent b. Solder core composition: C≦0.020%, Si≦0.050%, Mn0.40-0.60%, S≦0.006%, P≦0.006%, Cr≦0.05%, Mo≦0.05%, Ni≦0.05% , Ti≦0.05%, Cu≦0.05%, As≦0.001...

Embodiment 2

[0033] A laser arc fuse welding process for avoiding slag inclusion in the present invention comprises the following steps: S1: fixing the workpiece, grinding the welding part of the workpiece; S2: spraying cleaning agent on the welding part; S3: preheating before welding: the workpiece needs to be cleaned before welding Preheating; S4: Activation of the welding surface: after the heating is stopped, the active agent is sprayed quickly; S5: After the welding part is dry, the welding operation is performed with an electrode; S6: Cooling is used to set the shape.

[0034] As a further improvement of the present invention, the electrode in step S6 includes the following components and proportions: a, coating components: 100 parts of marble, 50 parts of fluorite, 15 parts of silicate, 20 parts of deoxidizer, 35 parts of alloying agent b. Solder core composition: C≦0.020%, Si≦0.050%, Mn0.40-0.60%, S≦0.006%, P≦0.006%, Cr≦0.05%, Mo≦0.05%, Ni≦0.05% , Ti≦0.05%, Cu≦0.05%, As≦0.001%.

...

Embodiment 3

[0043]A laser arc fuse welding process for avoiding slag inclusion in the present invention comprises the following steps: S1: fixing the workpiece, grinding the welding part of the workpiece; S2: spraying cleaning agent on the welding part; S3: preheating before welding: the workpiece needs to be cleaned before welding Preheating; S4: Activation of the welding surface: after the heating is stopped, the active agent is sprayed quickly; S5: After the welding part is dry, the welding operation is performed with an electrode; S6: Cooling is used to set the shape.

[0044] As a further improvement of the present invention, the welding rod in step S6 includes the following components and proportions: a, coating components: 100 parts of marble, 50 parts of fluorite, 12 parts of silicate, 18 parts of deoxidizer, and 30 parts of alloying agent b. Solder core composition: C≦0.020%, Si≦0.050%, Mn0.40-0.60%, S≦0.006%, P≦0.006%, Cr≦0.05%, Mo≦0.05%, Ni≦0.05% , Ti≦0.05%, Cu≦0.05%, As≦0.001%...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a laser-arc fuse wire welding process for avoiding slag inclusion. The laser-arc fuse wire welding process for avoiding slag inclusion comprises the following steps of S1, fixing a workpiece, and polishing a workpiece welding part; S2, spraying a cleaning agent for the welding part; S3, preheating before welding: preheating the workpiece before welding; S4, activating the welding surface: after stopping heating, quickly spraying an active agent; S5, after drying the welding part, adopting a welding rod for welding; and S6, cooling for shaping. The invention aims to research and develop the laser-arc fuse wire welding process for avoiding slag inclusion from the welding source in order to reduce slag inclusion of the die workpiece and reduce the difficulty and the necessity of a follow-up slag inclusion removal process.

Description

technical field [0001] The invention relates to the technical field of automatic mold processing, in particular to a laser arc fuse welding process for avoiding slag inclusion. Background technique [0002] Laser welding is a new type of welding technology developed in recent decades. It has the advantages of less heat input, concentrated energy density, small deformation of the heat-affected zone, and greater penetration depth. Especially when combined with robots, it can give full play to With the advantages of high welding efficiency, laser welding has more and more applications in industrial production. [0003] The existing patent number is CN201810046047.X, and the Chinese invention patent titled "Casting Magnesium Alloy Products Surface Treatment Equipment and Process" discloses a kind of equipment and process for treating slag inclusions on the surface of magnesium alloy products, and the equipment structure is complex , the operation is numerous, and the efficiency...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K26/348B23K26/60B23K35/36
Inventor 张运军陈天赋左长兵杨诗山杨杰晏洋钟平洋李飞朱旭峰
Owner HUBEI TRI RING FORGING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com