Antistatic glass fiber reinforced PBT/ASA composite material and preparation method thereof

A composite material and antistatic technology, applied in the field of composite materials, can solve problems such as unsatisfactory antistatic effect, achieve good comprehensive physical properties, broad market space, and reduce damage to physical properties

Inactive Publication Date: 2019-06-04
太仓市华鼎塑料有限公司
View PDF10 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the composite material provided by this patent has unsatisfactory antistatic effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0041] Simultaneously, the present invention also provides a kind of preparation method of antistatic glass fiber reinforced PBT / ASA composite material, and described preparation method comprises the following steps:

[0042]1) According to the proportion, add the polybutylene terephthalate, ASA resin, compatibilizer, antioxidant and dispersant into the stirring tank, add liquid additives, and Stir at a rotating speed for 10-15 minutes, add an antistatic agent, stir at a rotating speed of 1000-1200 rpm for 15-20 minutes, and mix evenly to obtain a mixed material;

[0043] 2) Put the mixed material into the twin-screw extruder, manually add glass fiber from the first vacuum port of the twin-screw extruder, control the barrel temperature of the twin-screw extruder at 220-240°C, and extrude, Adjust the ratio between the main engine speed and the feeding speed of the twin-screw extruder to adjust the glass fiber content and control the glass fiber content;

[0044] 3) Stranding, ...

Embodiment 1

[0050] The antistatic glass fiber reinforced PBT / ASA composite material includes the following components by weight: polybutylene terephthalate: 25 parts, ASA resin: 20 parts, glass fiber: 15 parts, compatibilizer: 7 parts parts, antioxidant: 3 parts, dispersant: 4 parts, antistatic agent: 2 parts, liquid additive: 3 parts.

[0051] The performance parameters of the antistatic glass fiber reinforced PBT / ASA composite material are shown in Table 2.

[0052] Table 2

[0053] Test items

Embodiment 2

[0055] The antistatic glass fiber reinforced PBT / ASA composite material includes the following components by weight: polybutylene terephthalate: 30 parts, ASA resin: 25 parts, glass fiber: 10 parts, compatibilizer: 5 parts parts, antioxidant: 5 parts, dispersant: 1 part, antistatic agent: 1 part, liquid additive: 5 parts.

[0056] The performance parameters of the antistatic glass fiber reinforced PBT / ASA composite material are shown in Table 3.

[0057] table 3

[0058] Test items

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
bending strengthaaaaaaaaaa
flexural modulusaaaaaaaaaa
electrical resistivityaaaaaaaaaa
Login to View More

Abstract

The invention provides an antistatic glass fiber reinforced PBT / ASA composite material and a preparation method thereof. The composite material comprises the following ingredients (by weight): 20-30 parts of polybutylene terephthalate, 15-25 parts of ASA resin, 10-20 parts of glass fiber, 5-10 parts of a compatilizer, 1-5 parts of an anti-oxidant, 1-5 parts of a dispersant, 1-5 parts of an antistatic agent and 1-5 parts of a liquid additive. Under the precondition of guaranteeing excellent properties such as high strength, good electrical property, dimensional stability, good heat resistance,low water absorption and easy forming, the antistatic property of the composite material is enhanced. The invention brings greater profit margins for the application of PBT / ASA plastic alloy.

Description

technical field [0001] The invention belongs to the technical field of composite materials, and in particular relates to an antistatic glass fiber reinforced PBT / ASA composite material and a preparation method thereof. Background technique [0002] Polybutylene terephthalate (PBT) is an engineering material with high strength, good electrical properties, stable dimensions, good heat resistance, low water absorption and easy molding and processing. It is widely used in automobiles, electronics Electrical appliances and machinery manufacturing industries have become the fifth largest engineering plastics. [0003] However, the notched impact strength of PBT resin is low and the molding shrinkage is large. These problems limit the development and application of PBT resin in some fields to a certain extent. [0004] The introduction of ASA makes the alloy have excellent mechanical properties, dimensional stability, chemical resistance, weather resistance, etc., which expands th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/02C08L51/04C08L23/08C08K7/14C08J5/04
Inventor 时亚马凤贺徐军徐卢碧赵小康万吴军
Owner 太仓市华鼎塑料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com