Stereoscopic silk imitation fur plus material

A technology of imitating fur and silk, applied in the field of textiles, can solve the problems of reducing the impact of silk appearance, consumer purchases, not having a three-dimensional effect, and increasing the cost of silk, etc., to achieve a wide range of product use, good three-dimensional structure and pattern effect , The effect of strong adaptability of raw materials

Active Publication Date: 2019-03-22
GUANGZHOU PANYU POLYTECHNIC
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing silk is generally presented with a smooth surface cloth, which does not have a three-dimensional effect, which reduces the impact of the silk appearance on human vision and the purchase volume of consumers, and the existing silk generally loses The use of single mechanical equipment for construction reduces the efficiency of its production and increases the cost of silk production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Stereoscopic silk imitation fur plus material
  • Stereoscopic silk imitation fur plus material
  • Stereoscopic silk imitation fur plus material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Such as figure 1 Shown, a kind of three-dimensional silk imitation fur fabric, comprises real silk fluff layer 1, rayon base layer 2, adhesive layer 3 and imitation leather fleece layer 4, and described real silk fluff layer 1 is combined with described rayon base layer by knitting 1, the rayon base layer 2 and the leather-like suede layer 4 are bonded through the adhesive layer 3. Wherein, the adhesive layer is a thermosetting adhesive layer.

[0039] The silk fluff layer 1 uses mulberry silk as fluff raw material; the rayon base layer 2 uses rayon as a raw material, and the real silk fluff layer 1 and the rayon base layer 2 are formed by circular knitting, specifically comprising the following steps:

[0040] (1a) Using mulberry silk as the fluff raw material, using rayon as the base layer raw material, putting mulberry silk and rayon on the large circular knitting machine;

[0041](2a) The large circular knitting machine reuses the yarn to form a coil, which is for...

Embodiment 2

[0053] A kind of three-dimensional silk fur-like fabric, comprising a real silk fluff layer 1, an artificial silk base layer 2, an adhesive layer 3 and an imitation leather fleece layer 4, and the real silk fluff layer 1 is knit with the top of the artificial silk base layer 1 Fixedly connected, the rayon base layer 2 and the leather-like suede layer 4 are bonded through the adhesive layer 3 . Wherein, the adhesive layer is a thermosetting adhesive layer.

[0054] The preparation method of the mulberry silk is the same as in Example 1. The fineness of the mulberry silk is 50D; the length of the mulberry silk is 10mm.

[0055] Before the mulberry silk and rayon are spun, the mulberry silk and rayon are also subjected to antibacterial modification treatment, which specifically includes the following steps:

[0056] (1d) adding rhubarb into ethanol solution according to the mass ratio of 1:20 after crushing rhubarb, extracting at 65-70° C. for 2-3 hours, centrifuging, and conce...

Embodiment 3

[0064] A kind of three-dimensional silk fur-like fabric, comprising a real silk fluff layer 1, an artificial silk base layer 2, an adhesive layer 3 and an imitation leather fleece layer 4, and the real silk fluff layer 1 is knit with the top of the artificial silk base layer 1 Fixedly connected, the rayon base layer 2 and the leather-like suede layer 4 are bonded through the adhesive layer 3 . Wherein, the adhesive layer is a thermosetting adhesive layer.

[0065] The preparation method of the mulberry silk is the same as in Example 1. The fineness of the mulberry silk is 100D; the length of the mulberry silk is 20mm

[0066] Before the mulberry silk and rayon are weaved, the mulberry silk and rayon are subjected to antibacterial modification treatment, which specifically includes the following steps:

[0067] (1d) adding rhubarb into ethanol solution according to the mass ratio of 1:15 after crushing rhubarb, extracting at 65-70° C. for 2-3 hours, centrifuging, and concentr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a stereoscopic silk imitation fur plus material. The plus material comprises a real silk nap layer, a rayon basal layer, a bonding layer and an imitation leather nap layer, wherein the real silk nap layer is fixedly connected with the upper part of the rayon basal layer through a knitting way; and the rayon basal layer and the imitation leather nap layer are bonded throughthe bonding layer. According to the stereoscopic silk imitation fur plus material, mulberry silk is used as a nap raw material; rayon is used as a raw material for the basal layer; through carrying out weaving by adopting a circular knitting machine, the real silk nap layer is fixed on the rayon basal layer; and through the combination of the imitation leather nap layer, the stereoscopic silk imitation fur plus material is formed. The real silk nap layer of the stereoscopic silk imitation fur plus material is good in gloss, has a favorable stereoscopic structure and design effect; a concave-convex stereoscopic perception is given to the plus material; the line is smooth; and a visual perception is good. The stereoscopic silk imitation fur plus material adopts the rayon as a material for the basal layer, and compared with silk, is light in weight and lower in cost. According to the plus material provided by the invention, animal fur is imitated; a natural silk component is protein; thesense of touch of skin is enabled to be better; the air permeability is good; and further, the stereoscopic silk imitation fur plus material is more environment-friendly.

Description

technical field [0001] The invention relates to the technical field of textiles, in particular to a three-dimensional silk imitation fur fabric. Background technique [0002] Artificial fur is a plush fabric with an appearance similar to animal fur. It is an imitation animal fur made by artificial methods. The commonly used manufacturing methods include knitting and machine weaving. Among them, the knitting weft knitting method has the fastest development and is the most widely used. Acrylic fiber, modified acrylic fiber, chlorine fiber and other materials can be used as raw materials for artificial fur. Although artificial fur is not as warm as real fur, it is soft and beautiful. It can be made into coats, hats, collars and carpets, etc., and is widely used. At present, the popular imitation fur on the market is made of polyester or acrylic fiber which is woven into gray fabric by circular knitting machine, and then de-haired and brushed. The resulting product is hard, air...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B9/02B32B9/04B32B7/12B32B5/06D04B1/04D06M13/00D06M15/00D06M15/03
CPCB32B5/02B32B5/06B32B5/26B32B7/12B32B2250/20B32B2262/08B32B2307/40B32B2307/718B32B2307/724D04B1/04D06M13/00D06M15/00D06M15/03D06M16/00D06M2101/10D10B2211/04
Inventor 刘科江王勇张来源张雪峰侯文峰邓单
Owner GUANGZHOU PANYU POLYTECHNIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap