Fiber cement external wall board and preparation method thereof

A technology of fiber cement and exterior wall panels, applied in the field of building materials and its production, to achieve the effects of increasing compactness, enhancing bonding, and improving flexural strength

Active Publication Date: 2019-03-01
BEIJING NEW BUILDING MATERIALS PLC +1
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention aims to solve the problems described above

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fiber cement external wall board and preparation method thereof
  • Fiber cement external wall board and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] In order to make the purpose, technical solutions and advantages of the embodiments of the present invention clearer, the technical solutions in the embodiments of the present invention will be clearly and completely described below. Obviously, the described embodiments are part of the embodiments of the present invention, not all of them. the embodiment. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention. It should be noted that, in the case of no conflict, the embodiments in the present application and the features in the embodiments can be combined arbitrarily with each other.

[0020] The inventor added a certain proportion of microsilica fume (also called silica fume) to the production formula, and used the existing process equipment for production and maintenance. The final produced fiber cement exterior wal...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a fiber cement external wall board and a preparation method thereof. The fiber cement external wall board comprises the following components in parts by weight: 80-120 parts ofcement, 22-27 parts of silicon micropowder, 43-58 parts of closed-pore vitrified microbeads, 20-29 parts of talcum powder, 12-18 parts of mica, 20-28 parts of wood fiber and 27-34.5 parts of fly ash,wherein the silicon micropowder has the particle size of 10-20 microns and has the silicon dioxide content of 99% or above. Through addition of a certain proportion of silicon micropowder into a production formula, pores of a cement substrate can be effectively filled, the compactness of the board is improved, and the water absorbing rate is reduced; meanwhile, through production of a gel by virtue of a hydration reaction of the silicon micropowder and the cement, adhesion between the fiber and the cement is strengthened and the flexural strength of the board is effectively improved.

Description

technical field [0001] The invention relates to the technical field of building materials and production thereof, in particular to a fiber cement exterior wall board and a preparation method thereof. Background technique [0002] As a new type of energy-saving and green building material, fiber cement exterior wall cladding has been widely used, but there is still a problem that cracks are prone to appear in the production of cement exterior cladding. In order to prevent cracks, a certain amount of polypropylene fiber or glass fiber is often added in production. The addition of polypropylene fiber or glass fiber does improve the crack resistance of the board to a certain extent, but at the same time it also leads to an increase in the porosity of the fiber-cement contact surface, resulting in enhanced water absorption and reduced flexural strength of the board. Guarantee the strength of the product. Contents of the invention [0003] The present invention aims to solve t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B111/82
CPCC04B28/04C04B2111/82C04B2201/20C04B2201/50C04B18/146C04B18/027C04B14/042C04B14/20C04B18/26C04B18/08C04B20/008
Inventor 梁宝伟
Owner BEIJING NEW BUILDING MATERIALS PLC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com