A kind of preparation method of dispersion strengthened aluminum bronze spherical powder

A technology for strengthening aluminum and aluminum bronze. It is applied in the field of copper alloy powder preparation and surface spraying. It can solve the problems of affecting the powder rate, affecting the spraying effect, and the inability to obtain dispersion-strengthened aluminum bronze powder. It achieves high hardness and improved wear resistance. Effect

Active Publication Date: 2021-10-01
DONGGUAN HYPER TECH COMPANY
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are great difficulties in the preparation of dispersion-strengthened aluminum bronze powder by the internal oxidation method: since the aluminum content in aluminum bronze is as high as about 10%, during the internal oxidation process, a dense aluminum oxide passivation film will be preferentially formed on the surface of the powder particles. Prevent the internal oxidation process from continuing, so that the aluminum oxide disperse phase cannot be generated inside the powder; and the presence of an aluminum oxide passivation layer on the surface of the powder particles will also affect the spraying effect and the powder coating rate
Therefore, the conventional internal oxidation method cannot obtain dispersion strengthened aluminum bronze powder

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] This embodiment provides a preparation method of dispersion strengthened aluminum bronze spherical powder, comprising the following steps:

[0025] Step 1: Put the aluminum bronze raw material with the brand name QAL9-4 in the graphite crucible of the intermediate frequency melting furnace, melt it in vacuum, and use the nitrogen atomization method to make the aluminum bronze spherical powder. Take the fine powder (-300 mesh) whose particle size distribution is within the range of 15-53 microns;

[0026] Step 2: Put nano-alumina powder (average particle size 30-50 nm) with a weight percentage of 2.5% of aluminum bronze into pure water with a weight percentage of 30% of aluminum bronze, and add surfactant AD18#, the proportion of which is aluminum 0.3%wt of bronze powder forms a colloid after ultrasonic dispersion;

[0027] Step 3: Put the above aluminum bronze powder into the colloidal solution, stir it well, place it together with the liquid in an oven, and dry it at ...

Embodiment 2

[0031] This embodiment provides a preparation method of dispersion strengthened aluminum bronze spherical powder, comprising the following steps:

[0032] Step 1: Put the raw material of aluminum bronze with the brand name QAL9-4 in the graphite crucible of the intermediate frequency melting furnace, vacuum melt, the superheat of the melt is 250-300°C, and use the nitrogen atomization method to make aluminum bronze spherical powder. Take the fine powder (-100+250 mesh) whose particle size distribution is in the range of 50-120 microns;

[0033] Step 2: Put nano-alumina powder (average particle size 30-50 nm) with a weight percentage of 3% of aluminum bronze into pure water with a weight percentage of 25% of aluminum bronze, and add surfactant AD18#, the ratio of which is aluminum 0.2%wt of bronze powder forms a colloid after ultrasonic dispersion;

[0034] Step 3: Put the above aluminum bronze powder into the colloidal solution, stir it well, place it together with the liquid...

Embodiment 3

[0038] This embodiment provides a preparation method of dispersion strengthened aluminum bronze spherical powder, comprising the following steps:

[0039] Step 1: Put the aluminum bronze raw material with the brand name QAL10-4-4 in the graphite crucible of the intermediate frequency melting furnace, melt it in vacuum, and use the nitrogen atomization method to make the aluminum bronze spherical powder. Take the fine powder (-150+300 mesh) whose particle size distribution is in the range of 40-100 microns;

[0040] Step 2: Put nano-zirconia powder (average particle size 20 nm) with a weight percentage of 3% of aluminum bronze into pure water with a weight percentage of 25% of aluminum bronze, and add surfactant AD18#, the ratio of which is aluminum bronze powder 0.2%wt of 0.2%wt, form a colloid after ultrasonic dispersion;

[0041] Step 3: Put the above aluminum bronze powder into the colloidal solution, stir it thoroughly, put it together with the liquid in an oven, and dry ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of copper alloy powder, and in particular relates to a method for preparing a dispersion-strengthened aluminum bronze spherical powder, which comprises the following steps: placing the aluminum bronze pre-alloyed raw material in a graphite crucible of an intermediate frequency induction furnace, melting in a vacuum, and then using gas mist The aluminum bronze spherical powder is made by the chemical process; the nano-dispersed phase powder is put into pure water, and an organic silicon surfactant is added at the same time. After ultrasonic dispersion, the nano-phase forms a colloidal solution in the water; the aluminum bronze spherical powder is put into the colloid solution, fully stirred, placed in an oven, heated and dried; the obtained powder was put into a mixing tank for mixing, and the powders were rubbed against each other to obtain dispersion-strengthened aluminum bronze spherical powder. Compared with the prior art, the coating structure prepared by using the aluminum bronze powder of the present invention is compact, and the dispersed phase particles of nanometer to submicron size are distributed in the coating, and the size of the dispersed phase particles is stable, and they are evenly distributed in the layer obtained by cold spraying In the film layer of the like structure, it has the effect of particle dispersion strengthening.

Description

technical field [0001] The invention belongs to the technical field of copper alloy powder preparation and surface spraying, and in particular relates to a preparation method of dispersion-strengthened aluminum bronze spherical powder. Background technique [0002] Aluminum bronze has high strength, good elasticity, good fatigue resistance, corrosion resistance, wear resistance, low temperature impact resistance and other advantages, and is widely used in machinery, electronics, metallurgy, shipbuilding, marine industry and other fields. As a coating material, aluminum bronze is not only a common surface repair material, but also an excellent soft wear-resistant coating material, which has the advantages of anti-contact wear, anti-cavitation, and excellent dry friction performance. It is used in large ships. It is widely used in propellers, aero-engine components, mechanical transmission shaft components and other fields. However, there are not many ways to further improve ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22F9/08B22F1/00
CPCB22F1/0003B22F9/082
Inventor 李晖云崔宁
Owner DONGGUAN HYPER TECH COMPANY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com