Flame-retardant wear-resistant coating for surface of bamboo product

A technology for wear-resistant coatings and bamboo products, which is applied in the direction of fire-resistant coatings, anti-fouling/underwater coatings, coatings, etc., and can solve the problem of poor abrasion resistance of coatings, easy mildew and decay, and poor flame-retardant properties, etc. problem, to achieve the effect of inhibiting the escape of combustible gas, preventing the escape of combustible gas from oxygen, and enhancing the wear resistance

Inactive Publication Date: 2019-01-29
广德竹之韵工艺品厂
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, bamboo is prone to mildew and decay during processing, storage, transportation and use.
In the existing methods, coatings are often applied on the surface...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A flame retardant and wear-resistant coating for the surface of bamboo products proposed by the present invention, its raw materials include by weight: 75 parts of silicon acrylic emulsion, 10 parts of water-based polyurethane emulsion, 10 parts of alkyd resin, 5 parts of furfuryl alcohol resin, nitrogen methylol 8 parts of resin, 3 parts of boron-containing flame retardant, 4.8 parts of ammonium dihydrogen phosphate, 0.5 parts of halloysite nanotubes, 1.5 parts of graphene, 2 parts of nano-bamboo charcoal, 3.8 parts of vermiculite, 3 parts of nano-zinc oxide, 3.2 parts of silicon oxide, 3 parts of polyether ether ketone, 1 part of 3-iodo-2-propynyl butyl carbamate, 0.2 parts of chitosan, 0.8 parts of plant essential oil, 1 part of amino silicone oil, film-forming aid 5 parts, 0.2 parts of additives, 85 parts of water.

Embodiment 2

[0019] A flame retardant and wear-resistant coating for the surface of bamboo products proposed by the present invention, its raw materials include by weight: 60 parts of silicon acrylic emulsion, 20 parts of water-based polyurethane emulsion, 5 parts of alkyd resin, 10 parts of furfuryl alcohol resin, nitrogen methylol 3 parts of resin, 5.5 parts of boron-containing flame retardant, 2 parts of ammonium dihydrogen phosphate, 2.3 parts of halloysite nanotubes, 0.3 parts of graphene, 3.2 parts of nano-bamboo charcoal, 1 part of vermiculite, 8 parts of nano-zinc oxide, 0.5 parts of silicon oxide, 5 parts of polyether ether ketone, 0.1 part of 3-iodo-2-propynyl butyl carbamate, 0.55 parts of chitosan, 0.1 part of plant essential oil, 2 parts of amino silicone oil, film-forming aid 1 part, 0.7 parts of additives, 50 parts of water.

Embodiment 3

[0021] A flame retardant and wear-resistant coating for the surface of bamboo products proposed by the present invention, its raw materials include by weight: 72 parts of silicon acrylic emulsion, 13 parts of water-based polyurethane emulsion, 9 parts of alkyd resin, 7 parts of furfuryl alcohol resin, nitrogen methylol 7 parts of resin, 3.8 parts of boron-containing flame retardant, 4.5 parts of ammonium dihydrogen phosphate, 1 part of halloysite nanotube, 1.3 parts of graphene, 2.5 parts of nano-bamboo charcoal, 3.5 parts of vermiculite, 4 parts of nano-zinc oxide, 3 parts of silicon oxide, 3.6 parts of polyether ether ketone, 0.8 parts of 3-iodo-2-propynyl butyl carbamate, 0.26 parts of chitosan, 0.7 parts of plant essential oil, 1.3 parts of amino silicone oil, film-forming aids 4.2 parts, 0.3 parts of additives, 82 parts of water;

[0022] Wherein, the solid content of the silicone acrylic emulsion is 50wt%; the solid content of the aqueous polyurethane emulsion is 37wt%; ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
The average particle sizeaaaaaaaaaa
The average particle sizeaaaaaaaaaa
The average particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a flame-retardant wear-resistant coating for the surface of a bamboo product. The coating comprises the following raw materials: a silicon-acrylic emulsion, a water-based polyurethane emulsion, alkyd resin, furfuryl alcohol resin, nitrogen hydroxymethyl resin, a boron-containing flame retardant, ammonium dihydrogen phosphate, halloysite nanotubes, graphene, nanometer bamboocharcoal, vermiculite, nanometer zinc oxide, nanometer silica, polyetheretherketone, 3-iodo-2-propynylbutylcarbamate, chitosan, plant essential oil, amino silicone oil, a film forming aid, an accessory agent and water. The flame-retardant wear-resistant coating for the surface of the bamboo product in the invention has strong adhesion to bamboo wood and excellent flame retardancy, wear resistanceand mildew resistance.

Description

technical field [0001] The invention relates to the field of bamboo technology, in particular to a flame-retardant and wear-resistant coating for the surface of bamboo products. Background technique [0002] Bamboo, as one of the important forest resources, has the characteristics of toughness, compression resistance and tensile resistance, and also has the advantages of fast growth, large output, wide sources and low price. It has been widely used to make furniture, floors, handicrafts, etc. . However, bamboo is prone to mildew and decay during processing, storage, transportation and use. In the existing methods, coatings are often applied on the surface of bamboo products to provide protective measures. However, the existing coatings have poor wear resistance and poor flame retardancy, which limits their application. Contents of the invention [0003] Based on the technical problems existing in the background technology, the present invention proposes a flame-retardant...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D133/04C09D5/18C09D5/14C09D7/61C09D7/62C09D7/63C09D7/65
CPCC08K2003/2296C08K2201/011C08K2201/014C08L2201/02C08L2201/08C08L2205/035C09D5/14C09D5/18C09D7/61C09D7/62C09D7/63C09D7/65C09D7/67C09D7/70C09D143/04C08L75/04C08L67/08C08L71/14C08L91/00C08L5/08C08L83/08C08K13/06C08K9/06C08K7/26C08K3/042C08K3/04C08K3/36C08K5/55
Inventor 赵耀祥
Owner 广德竹之韵工艺品厂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap