High-strength anti-falling ceramic product and manufacturing method thereof

A ceramic product and high-strength technology, applied in the field of ceramics, can solve problems such as poor practicability and loss of practical significance, and achieve the effects of high viscosity, shortened drying time, and improved drying performance

Inactive Publication Date: 2019-01-04
德化县高圣工艺品有限公司
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Ceramic pillows have been handed down until now, but have gradually lost their practical significance. They are more used as decorations. There are various patterns and inscriptions painted on the pillow surface, and there are also character pillows, animal pillows, and table pillows. Meaning, town house to ward off evil spirits, not very practical

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength anti-falling ceramic product and manufacturing method thereof
  • High-strength anti-falling ceramic product and manufacturing method thereof
  • High-strength anti-falling ceramic product and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] This embodiment provides a high-strength anti-fall ceramic product, including tire material and glaze, characterized in that the tire material includes the following raw materials in parts by weight: 36 parts of kaolin, 15 parts of quartz, 21 parts of potassium feldspar, 8 parts of clay The glaze includes the following raw materials in parts by weight: 18 parts of orthoclase, 12 parts of zinc oxide, 12 parts of calcium oxide, 4 parts of potassium oxide, 6 parts of barium carbonate, 2 parts of plant ash, and 3 parts of copper oxide.

[0031] The high-strength and drop-resistant ceramic product provided by the present invention is characterized in that the ceramic pillow is hollow, 30 cm long, 1-1.5 cm thick, and has a square side with a side length of 13 cm. One of the sides can be opened, and the other four sides are Curved, the height of the lowest point of the curved surface is 9cm, there are ventilation holes on all six sides, and multiple ventilation holes form plum ...

Embodiment 2

[0040] This embodiment provides a high-strength anti-fall ceramic product, including tire material and glaze, characterized in that the tire material includes the following raw materials in parts by weight: 38 parts of kaolin, 17 parts of quartz, 23 parts of potassium feldspar, 9 parts of clay The glaze includes the following raw materials in parts by weight: 19 parts of orthoclase, 14 parts of zinc oxide, 14 parts of calcium oxide, 4 parts of potassium oxide, 7 parts of barium carbonate, 3 parts of plant ash, and 3 parts of copper oxide.

[0041]The high-strength and drop-resistant ceramic product provided by the present invention is characterized in that the ceramic pillow is hollow, 36 cm long, 1-1.5 cm thick, and has a square side with a side length of 15 cm. One of the sides can be opened, and the other four sides are Curved, the height of the lowest point of the curved surface is 10cm, and there are ventilation holes on all six sides, and multiple ventilation holes form p...

Embodiment 3

[0050] This embodiment provides a high-strength anti-fall ceramic product, including a tire material and a glaze, and is characterized in that the tire material includes the following raw materials in parts by weight: 40 parts of kaolin, 18 parts of quartz, 24 parts of potassium feldspar, and 10 parts of clay. The glaze includes the following raw materials in parts by weight: 20 parts of orthoclase, 15 parts of zinc oxide, 15 parts of calcium oxide, 5 parts of potassium oxide, 5 parts of barium carbonate, 4 parts of plant ash, and 4 parts of copper oxide.

[0051] The high-strength and drop-resistant ceramic product provided by the present invention is characterized in that the ceramic pillow is hollow, 40 cm long, 1-1.5 cm thick, and has a square side with a side length of 16 cm. One of the sides can be opened, and the other four sides are Curved, the height of the lowest point of the curved surface is 11cm, with ventilation holes on all six sides, and multiple ventilation hol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Wall thicknessaaaaaaaaaa
Wall thicknessaaaaaaaaaa
Wall thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides a high-strength anti-falling ceramic product. The high-strength anti-falling ceramic product comprises a body material and a glaze material. The body material comprises the following raw materials in parts by weight: 36-42 parts of kaolin, 15-20 parts of quartz, 21-26 parts of potassium feldspar and 8-12 parts of clay; and the glaze material comprises the following raw materials in parts by weight: 18-22 parts of orthoclase, 12-18 parts of ZnO, 12-18 parts of CaO, 4-6 parts of K2O, 6-10 parts of barium carbonate, 2-5 parts of plant ash and 3-5 parts of CuO. The manufacturing method comprises the following steps: (1) separately mixing the body material and the glaze material, adding water in the mixture and wet-milling the mixture by using a ball-miller, and sieving the slurry by using a sieve with meshes of 250 to obtain body material slurry and glaze slurry; (2) manufacturing blank body from the body material slurry and carrying out biscuiting; (3) applying glaze; and (4) firing at the temperature of 1350-1480 DEG C. The ceramic product fired in the invention is in a jade-like opacifying semitransparent sky blue state, is quietly elegant in color, and has quite high anti-falling property.

Description

technical field [0001] The invention belongs to the technical field of ceramics, and in particular relates to a high-strength and drop-resistant ceramic product and a manufacturing method thereof. Background technique [0002] Ceramics are various products made from natural clay and various natural minerals through crushing, kneading, molding and calcination. In the past, people called ceramics made of clay and fired at high temperature in special kilns. Ceramics is the general term for pottery and porcelain. The traditional concept of ceramics refers to all artificial industrial products that use inorganic non-metallic minerals such as clay as raw materials. It includes various products made of clay or a mixture containing clay through kneading, molding, and calcination. It ranges from the roughest earthenware to the finest fine pottery and porcelain. [0003] Porcelain pillow is a good product for sleeping and sleeping during the summer summer in ancient my country, and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B33/13C04B41/86C03C8/00A47G9/10
CPCA47G9/10C03C8/00C03C2204/04C03C2205/02C04B33/13C04B41/5022C04B41/86C04B2235/3201C04B2235/3418C04B2235/3472C04B2235/656C04B41/4539C04B41/0072
Inventor 郑贵高
Owner 德化县高圣工艺品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap