Bamboo mildew-proof treatment method

A mildew-proof treatment, bamboo technology, applied in wood treatment, pressurized wood treatment, wood treatment details, etc., can solve the problems of easy mildew and decay, endangering human health, poor effect, etc., to achieve good synergy, The effect of increasing the permeability and improving the penetration effect

Inactive Publication Date: 2019-01-04
广德竹之韵工艺品厂
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, bamboo is rich in nutrients such as sugar, protein and fat, and it is prone to mildew and decay during storage, transportation and use, which not only causes waste of resources but also endangers human health, severely limiting its application
A variety of anti-mildew treatment methods have been disclosed at present, but there are generally defects of poor effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A kind of mildew-proof treatment method of bamboo that the present invention proposes, comprises the following steps:

[0024] S1, drying the bamboo to a moisture content of 14wt%, then adding it to water, and obtaining bamboo A after ultrasonic treatment;

[0025] S2, treating the bamboo material A for 100 min under the condition of a vacuum degree of 0.1 MPa to obtain the bamboo material B;

[0026] S3, adding the bamboo material B into the protective agent, and holding the pressure for 45 minutes under a pressure of 2 MPa to obtain the bamboo material C;

[0027] S4. Mix zinc acetate, copper acetate and methanol evenly, raise the temperature to 45° C., dropwise add methanol solution of sodium hydroxide, stir for 25 minutes, cool and age, immerse in bamboo material C for 10 minutes, and obtain bamboo material D after drying;

[0028] S5. Mix zinc nitrate hexahydrate, copper nitrate, hexamethylenetetramine, polyethylene glycol with water, add bamboo material D, carry ...

Embodiment 2

[0030] A kind of mildew-proof treatment method of bamboo that the present invention proposes, comprises the following steps:

[0031] S1, drying the bamboo to a moisture content of 12.5wt%, then adding it into water, and obtaining bamboo A after ultrasonic treatment;

[0032] S2, treating the bamboo material A for 60 minutes under the condition of a vacuum degree of 0.06MPa to obtain the bamboo material B;

[0033] S3, adding bamboo material B into the protective agent, and holding the pressure for 30 minutes under a pressure of 2.5 MPa to obtain bamboo material C;

[0034] S4. Mix zinc acetate, copper acetate and methanol evenly, raise the temperature to 55° C., dropwise add methanol solution of sodium hydroxide, stir for 10 minutes, cool and age, then immerse in bamboo material C for 20 minutes, and obtain bamboo material D after drying;

[0035] S5. Mix zinc nitrate hexahydrate, copper nitrate, hexamethylenetetramine, polyethylene glycol with water, add bamboo material D, ...

Embodiment 3

[0037] A kind of mildew-proof treatment method of bamboo that the present invention proposes, comprises the following steps:

[0038] S1, drying the bamboo to a moisture content of 13.6wt%, then adding it to water, and obtaining bamboo A after ultrasonic treatment;

[0039] S2, treating the bamboo material A for 90 minutes under the condition of a vacuum degree of 0.07MPa to obtain the bamboo material B;

[0040] S3, adding bamboo material B into the protective agent, and holding the pressure for 42 minutes under a pressure of 2.2 MPa to obtain bamboo material C;

[0041] S4. Mix zinc acetate, copper acetate and methanol evenly, raise the temperature to 47° C., dropwise add methanol solution of sodium hydroxide, stir for 23 minutes, cool and age, then immerse in bamboo material C for 14 minutes, and obtain bamboo material D after drying;

[0042] S5. Mix zinc nitrate hexahydrate, copper nitrate, hexamethylenetetramine, polyethylene glycol with water, add bamboo material D, ca...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Moisture contentaaaaaaaaaa
Login to view more

Abstract

The invention discloses a bamboo mildew-proof treatment method. The method includes: drying bamboos until the moisture content is 12.5-14wt%, and ultrasonically treating in water to obtain a bamboo material A; treating the bamboo material A for 60-100min under vacuum of 0.06-0.1MPa to obtain a bamboo material B; adding the bamboo material B into a protecting agent, and treating for 30-45min underthe pressure of 2-2.5MPa to obtain a bamboo material C; well mixing zinc acetate, copper acetate and methyl alcohol, heating to 45-55 DEG C, dropwise adding methanol solution of sodium hydroxide, stirring for 10-25min, cooling, aging, soaking the bamboo material C to treat for 10-20min, and drying to obtain a bamboo material D; mixing zinc nitrate hexahydrate, copper nitrate, hexamethylenetetramine, polyethylene glycol and water, adding the bamboo material D, and performing hydrothermal reaction, washing and drying. The bamboo mildew-proof treatment method is simple in process, and treated bamboos are high in mildew-proof effectiveness and long in mildew-proof time.

Description

technical field [0001] The invention relates to the technical field of bamboo, in particular to a method for treating mildew of bamboo. Background technique [0002] Bamboo is hard, flexible, tensile, and compressive, and has a short growth cycle and strong renewability. It is an ideal alternative resource to alleviate the contradiction between wood supply and demand. It has been widely used in indoor and outdoor furniture, construction, decoration, and musical instruments. and automobile manufacturing. However, bamboo is rich in nutrients such as sugar, protein and fat, and it is prone to mildew and decay during storage, transportation and use, which not only causes waste of resources but also endangers human health, severely limiting its application. Multiple anti-mildew treatment methods have been disclosed at present, but generally have the defect that the effect is not good enough. Contents of the invention [0003] Based on the technical problems in the background ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B27K9/00B27K5/00B27K3/52B27K3/08
CPCB27K3/08B27K3/52B27K5/001B27K5/0065B27K5/0075B27K9/002B27K2240/20
Inventor 赵耀祥
Owner 广德竹之韵工艺品厂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap