Gel leakage stoppage slurry for well drilling as well as preparation method of leakage stoppage slurry and plug leakage stoppage method

A technology of plugging slurry and gel, which is applied in drilling compositions, chemical instruments and methods, and earth-moving drilling and mining, etc. Low pressure capacity, etc.

Active Publication Date: 2018-12-21
SOUTHWEST PETROLEUM UNIV
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to overcome the problems in the prior art that the success rate of conventional bridge plugging is very low due to the existence of formation fluid in the leakage layer of the reservoir, and the low success rate of single bridge plugging and single condensation In order to solve the problem of low pressure bearing capacity of the rubber, a kind of gel plugging slurry for drilling, a preparation method of the plugging slurry and a slug plugging method are provided. The gel slug plugging method for drilling of the present invention has the advantages of simple construction, The advantage of low environmental requirements; moreover, the bridging material, connecting material and filling material in the gel plugging slurry of the present invention form a stable structure inside the gel, thereby effectively improving the plugging effect of the gel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Gel leakage stoppage slurry for well drilling as well as preparation method of leakage stoppage slurry and plug leakage stoppage method

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0041] A kind of preparation method of gel plugging slurry for drilling according to a preferred embodiment of the present invention, wherein, the method comprises the following steps:

[0042] (1) Pour water into the mixer and stir evenly at 2000-4000 rpm, add special gel and stir evenly for 10-20 minutes;

[0043] (2) Slowly add the bridging material along the stirring rod and stir evenly for 25-35 minutes;

[0044] (3) Slowly add the connecting material along the stirring rod and stir evenly for 25-30 minutes;

[0045] (4) Finally, slowly add the filling material along the stirring bar and stir evenly for 10-15 minutes.

[0046] Among them, in the present invention, the advantage of adding slowly along the stirring rod is that it can make the solid phase components more uniformly dispersed in the lost circulation slurry.

[0047] Wherein, in the present invention, the slow adding speed may be 0.5-2 g / s, preferably 1-1.5 g / s.

[0048] The third aspect of the present inven...

Embodiment 1

[0061] This example is to illustrate the gel plugging slurry prepared by the preparation method of the present invention

[0062] Add 6g of special gel ZND-2 to 100 ml of tap water (this special gel is a light yellow transparent particle, the particle size is between 8mm, at a shear rate of 1200s -1 Under conditions, the viscosity is 30mPa.s), and after stirring for 15 minutes under the environment of 3000 rev / min at the stirring rate, slowly add 5g glass fiber and 10g asbestos fiber along the stirring rod, and under the environment of 3000 rev / min at the stirring rate After stirring for 30 minutes, slowly add 30g of walnut shells (the particle size of the walnut shells is 5mm) along the stirring rod, and then slowly add 35g of nanobarite powder along the stirring rod after stirring for 27 minutes at a stirring rate of 3000 rpm (The particle size of the nanobarite powder is 5 μm). After stirring for 12 minutes, the plugging slurry A1 was obtained.

[0063] A plugging instrume...

Embodiment 2

[0065] This example is to illustrate the gel plugging slurry prepared by the preparation method of the present invention

[0066] According to the same method as in Example 1 to prepare the plugging slurry, the difference is: 3g of special gel ZND-2 is added to 100 milliliters of tap water (this special gel is light yellow transparent particles, and the particle size is between 5mm between, at a shear rate of 1000s -1 Under conditions, the viscosity is 20mPa s), and after stirring for 10 minutes under the environment of 2000 rev / min at the stirring rate, slowly add 2g glass fiber and 12g asbestos fiber along the stirring rod, and under the environment of 2000 rev / min at the stirring rate Stir for 25 minutes, then slowly add 25g of walnut shells along the stirring rod, stir for 25 minutes at a stirring rate of 2000 rpm, then slowly add 30g of nanobarite powder along the stirring rod, and stir for 10 minutes to obtain plugging Pulp A2.

[0067] A plugging instrument was used t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of well drilling leakage stoppage of petroleum industry, and discloses gel leakage stoppage slurry for well drilling as well as a preparation method of leakage stoppage slurry and a plug leakage stoppage method. The gel leakage stoppage slurry comprises water, special gel, a bridging material, a connecting material and a filling material; and by adopting 100 weight parts of water as a reference, the content of the special gel is 1 to 15 weight parts, the content of the bridging material is 8 to 20 weight parts, the content of the connecting material is 20 to40 weight parts, and the content of the filling material is 25 to 45 weight parts. The gel leakage stoppage slurry is short in time for waiting the solidification, fast in effectiveness, and capable of rapidly forming a structure at a crack of a leaking stratum; meanwhile, the bridging material, the connecting material and the filling material can effectively block various cracks of a great width;and in the gel plug leakage stoppage method for the well drilling, a packer is arranged to pack a shaft, so that the leakage stoppage slurry can be ensured to accurately reach the leaking stratum, and the plugging efficiency can be improved.

Description

technical field [0001] The invention relates to the field of oil industry drilling plugging, in particular to a gel plugging slurry for drilling, a preparation method of the plugging slurry and a slug plugging method. Background technique [0002] Bridge plugging technology is widely used at home and abroad, and it has the advantages of high speed, low cost, and simple operation. The plugging particles used in bridge plugging can be as large as a few millimeters or even a few centimeters, and as small as tens of microns. , can play a role in slowing down the leakage, or completely blocking the leakage layer and improving the pressure bearing capacity. However, due to the presence of formation fluid in the leakage layer of the reservoir, the success rate of conventional bridge plugging is very low; formation fluid refers to oil, natural gas, water and their mixtures in the formation, such as oilfield water that dissolves inorganic and organic components and natural gas. It ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09K8/44E21B33/13
CPCC09K8/426C09K8/44C09K2208/04C09K2208/08C09K2208/18E21B33/13
Inventor 白杨罗平亚邓嘉丁
Owner SOUTHWEST PETROLEUM UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com