Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Lubricating oil for engine and preparation method thereof

A technology for lubricating oil and engine, applied in the field of lubricating oil, can solve the problems of lubricating oil cannot form effective rolling friction, insufficient wear resistance, etc., and achieve the effects of enhancing hydrolytic stability, reducing wear, and improving biodegradability

Inactive Publication Date: 2018-11-30
HEFEI OUSHIJIA ELECTRICAL & MECHANICAL EQUIP CO LTD
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this lubricating oil cannot form effective rolling friction, and there is still the problem of insufficient wear resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The engine lubricating oil of the present embodiment is made up of the following raw materials in parts by weight: 57.2 parts of polyalkylene glycol base oils, 25 parts of PAO base oils, 0.5 parts of tackifiers, 1.5 parts of friction modifiers, 2.5 parts of organic molybdenum, 1 part of borate additive, 0.4 part of composite antioxidant, 0.7 part of extreme pressure antiwear agent, 0.6 part of preservative, and 0.6 part of antifoaming agent.

[0029] The kinematic viscosity of the polyalkylene glycol base oil at 40°C is 220-1100 centistokes, the open flash point is not lower than 230°C, the viscosity index is not less than 155, and the mechanical impurities are not more than 0.03%;

[0030] The PAO base oil is preferably PA010.

[0031] Wherein, the said tackifier is selected as the main ingredient of the tackifier which is a composite polymer with a flash point greater than 250° C. after dissolving in synthetic oil.

[0032] Wherein, the friction modifier is composed ...

Embodiment 2

[0041] The engine lubricating oil of the present embodiment is made up of the following raw materials in parts by weight: 54.3 parts of polyalkylene glycol base oils, 30 parts of PAO base oils, 1.5 parts of tackifiers, 3.5 parts of friction modifiers, 4.5 parts of organic molybdenum, 3 parts of borate additive, 0.6 part of composite antioxidant, 0.9 part of extreme pressure antiwear agent, 0.8 part of preservative, and 0.9 part of antifoaming agent.

[0042] The kinematic viscosity of the polyalkylene glycol base oil at 40°C is 220-1100 centistokes, the open flash point is not lower than 230°C, the viscosity index is not less than 155, and the mechanical impurities are not more than 0.03%;

[0043] The PAO base oil is preferably PA010.

[0044] Wherein, the said tackifier is selected as the main ingredient of the tackifier which is a composite polymer with a flash point greater than 250° C. after dissolving in synthetic oil.

[0045] Wherein, the friction modifier is composed...

Embodiment 3

[0054] The engine lubricating oil of the present embodiment is made up of following raw materials in parts by weight: 53.2 parts of polyalkylene glycol base oils, 35 parts of PAO base oils, 1.0 parts of tackifiers, 2.5 parts of friction modifiers, 3.5 parts of organic molybdenum, 2 parts of borate additive, 0.5 part of composite antioxidant, 0.8 part of extreme pressure antiwear agent, 0.7 part of preservative, and 0.8 part of antifoaming agent.

[0055] The kinematic viscosity of the polyalkylene glycol base oil at 40°C is 220-1100 centistokes, the open flash point is not lower than 230°C, the viscosity index is not less than 155, and the mechanical impurities are not more than 0.03%;

[0056] The PAO base oil is preferably PA010.

[0057] Wherein, the said tackifier is selected as the main ingredient of the tackifier which is a composite polymer with a flash point greater than 250° C. after dissolving in synthetic oil.

[0058] Wherein, the friction modifier is composed of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
flash pointaaaaaaaaaa
flash pointaaaaaaaaaa
viscosity indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses lubricating oil for an engine and a preparation process thereof. The lubricating oil is prepared from the following raw materials in parts by weight: 49 to 69 parts of polyalkylene glycol base oil, 15 to 35 parts of PAO base oil, 0.5 to 1.5 parts of a tackifier, 1.5 to 3.5 parts of a friction modifier, 2.5 to 4.5 parts of organic molybdenum, 1 to 3 parts of borate additive,0.4 to 0.6 part of a complex antioxidant, 0.7 to 0.9 part of an anti-wear reagent at extreme pressure, 0.6 to 0.8 part of a preservative and 0.6 to 0.9 part of an anti-foaming agent. The lubricatingoil for the engine provided by the invention has better wear resistance, and can repair abrasion and reduce abrasion.

Description

technical field [0001] The invention relates to the technical field of lubricating oil, in particular to an engine lubricating oil and a preparation method thereof. Background technique [0002] The engine is the heart of automobiles and many industrial equipment, and its lubricating oil consumption accounts for about 50% of the total lubricating oil. As the blood of the engine, engine oil plays the roles of lubrication, cooling, sealing, cleaning, anti-rust and anti-corrosion, etc. It is a functional liquid to keep the engine running long and efficiently. [0003] As the manufacture of the engine becomes more and more sophisticated, the requirements for lubricating oil become more and more stringent. It is difficult for the existing engine oil to guarantee the normal operation of the engine, which leads to aggravated wear of the engine, serious corrosion of the piston ring and cylinder liner, and serious corrosion of the filter oil. The grid is clogged and the oil change i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10M169/04C10N30/06C10N30/08C10N30/10C10N40/25
CPCC10M169/048C10M2201/085C10M2201/087C10M2205/0285C10M2207/04C10M2207/08C10M2207/125C10M2207/283C10M2209/1033C10M2215/04C10M2219/066C10M2223/04C10M2223/045C10M2223/049C10M2229/041C10N2030/06C10N2030/08C10N2030/10C10N2030/64C10N2030/66C10N2040/25
Inventor 孔令翠
Owner HEFEI OUSHIJIA ELECTRICAL & MECHANICAL EQUIP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com