Raw material formula of PU wheel, raw material production process and processing method thereof

A technology of raw materials and formulations, applied in other household appliances, household components, applications, etc., can solve the problems of high heat production of rubber carcass, black marks on the road surface, environmental pollution, etc., and achieve good grip, not easy to slip, and wear resistance. Good results

Inactive Publication Date: 2018-11-06
江苏唯源橡塑制品有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the prior art, wheelchairs generally use rubber tires, which are generally pneumatic tires. In the case of uneven road surfaces, the inside of the rubber carcass tends to generate high heat, thus causing the tires to burst.
Now there are some rubber solid tires on the market, and these rubber solid tires often add carbon black and other materials to their raw materials in order to increase their strength, so that black marks will appear on the road surface when the tires are running, which in turn will cause environmental pollution, etc.
[0003] To sum up, traditional rubber tires have short service life, low safety, and poor wear resistance, and there are a large number of quality defects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Raw material formula of PU wheel, raw material production process and processing method thereof
  • Raw material formula of PU wheel, raw material production process and processing method thereof
  • Raw material formula of PU wheel, raw material production process and processing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] A raw material formulation of a PU wheel, comprising A component and B component, wherein, A component consists of the following raw materials in parts by weight:

[0049]

[0050] The B component consists of the following raw materials in parts by weight:

[0051] 20-parts of polyester polyol;

[0052] 5 parts of polyether polyol;

[0053] 80 parts of isocyanate.

[0054] Specifically, the function of the foam stabilizer is to make the pores of the foam more uniform and dense. The foam stabilizer Y~10366 can be selected, and the aramid pulp is selected from aramid 1414 pulp, with an average length of 2mm and a surface area of ​​8㎡ / g , has a better reinforcing effect.

[0055] Described tensio-active agent is foam stabilizer and silicone surfactant, and wherein the weight parts of both are respectively:

[0056] Foam stabilizer 0.1 part;

[0057] Among them, the foam stabilizer can emulsify the foam material, stabilize the foam and adjust the cells.

[0058] Sp...

Embodiment 2

[0105] A raw material formulation of a PU wheel, comprising A component and B component, wherein, A component consists of the following raw materials in parts by weight:

[0106]

[0107] The B component consists of the following raw materials in parts by weight:

[0108] Polyester polyol ~50 parts;

[0109] 30 parts of polyether polyols;

[0110] 90 parts of isocyanate.

[0111] Specifically, the function of the foam stabilizer is to make the pores of the foam more uniform and dense. The foam stabilizer Y~10366 can be selected, and the aramid pulp is selected from aramid 1414 pulp, with an average length of 2mm and a surface area of ​​8㎡ / g , has a better reinforcing effect.

[0112] Described tensio-active agent is foam stabilizer and silicone surfactant, and wherein the weight parts of both are respectively:

[0113] 3 parts of foam stabilizer;

[0114] The foam stabilizer can emulsify the foam material, stabilize the foam and regulate the cells.

[0115] Specifical...

Embodiment 3

[0162] A raw material formulation of a PU wheel, comprising A component and B component, wherein, A component consists of the following raw materials in parts by weight:

[0163]

[0164]

[0165] The B component consists of the following raw materials in parts by weight:

[0166] 40 parts of polyester polyols;

[0167] 17.5 parts of polyether polyols;

[0168] 85 parts of isocyanate.

[0169] Specifically, the function of the foam stabilizer is to make the pores of the foam more uniform and dense. The foam stabilizer Y~10366 can be selected, and the aramid pulp is selected from aramid 1414 pulp, with an average length of 2mm and a surface area of ​​8㎡ / g , has a better reinforcing effect.

[0170] Described tensio-active agent is foam stabilizer and silicone surfactant, and wherein the weight parts of both are respectively:

[0171] 1.55 parts of foam stabilizer;

[0172] The foam stabilizer can emulsify the foam material, stabilize the foam and regulate the cells. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a raw material formula of a PU wheel, a raw material production process and a processing method thereof. The raw material formula of the PU wheel comprises a component A and acomponent B, wherein the component A is prepared from the following raw materials in parts by weight: 60-80 parts of polyester polyol, 0.1-0.2 part of foam stabilizer, 5-10 parts of foaming agent, 1.3-5 parts of surfactant, 15-20 parts of chain extender, 0.15-0.3 part of composite catalyst, 5-10 parts of aramid pulp, 3-5 parts of curing agent and 6-12 parts of antistatic agent. The component B isprepared from the following raw materials in parts by weight: 20-50 parts of polyester polyol, 5-30 parts of polyether polyol and 80-90 parts of isocyanate. The PU wheel produced by the formula has elasticity, is excellent in damping effect, strong in road holding force, low in possibility of slippage, high in abrasion resistance, high in tearing strength, high in safety and long in service life.

Description

technical field [0001] The invention relates to the production field of PU wheels, in particular to a raw material formula, a raw material manufacturing process and a processing method of a PU wheel. Background technique [0002] In the prior art, what wheelchairs generally adopt are rubber tires, and rubber tires are generally pneumatic tires. In the case of some uneven road surfaces, the inside of the rubber carcass tends to generate high heat, thus causing the tires to burst. Now there are some rubber solid tires on the market, and these rubber solid tires often add carbon black and other materials to their raw materials in order to increase their strength, so that black marks will appear on the road surface during tire driving, which in turn will cause environmental pollution. [0003] To sum up, traditional rubber tires have short service life, low safety, poor wear resistance, and a large number of quality defects. Contents of the invention [0004] The invention pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L75/04C08L75/06C08L75/08C08L77/10C08G18/66C08G18/48C08G18/42C08G18/32C08J9/14B29C44/12B29C44/04C08G101/00B29L31/32
CPCB29C44/04B29C44/12B29L2031/32C08G18/4018C08G18/42C08G18/48C08G18/6607C08G18/6618C08G18/6622C08G2101/00C08J9/141C08J2203/14C08L75/04C08L75/06C08L75/08C08L2205/16C08L77/10
Inventor 丁宁
Owner 江苏唯源橡塑制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap